4 Material und Umwelt
Filtern
Dokumenttyp
- Vortrag (440) (entfernen)
Sprache
- Englisch (279)
- Deutsch (155)
- Spanisch (4)
- Französisch (2)
Referierte Publikation
- nein (440)
Schlagworte
- Biocides (20)
- Antimicrobial resistance (19)
- Nano (18)
- Recycling (17)
- Ink (16)
- MIC (14)
- Biofilms (12)
- Phosphor (12)
- XRF (12)
- Klärschlamm (11)
Organisationseinheit der BAM
- 4 Material und Umwelt (440)
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (93)
- 4.1 Biologische Materialschädigung und Referenzorganismen (91)
- 4.3 Schadstofftransfer und Umwelttechnologien (81)
- 4.2 Material-Mikrobiom Wechselwirkungen (77)
- 4.5 Kunst- und Kulturgutanalyse (66)
- 4.0 Abteilungsleitung und andere (46)
- 6 Materialchemie (30)
- 1 Analytische Chemie; Referenzmaterialien (27)
- 6.1 Oberflächen- und Dünnschichtanalyse (16)
OECD Prüfrichtlinie zur Bestimmung der Partikelgröße und Anzahlgrößenverteilung von Nanomaterialien
(2021)
Abschlusspräsentation des Projektes "OECD Prüfrichtlinie zur Bestimmung der Partikelgröße und Anzahlgrößenverteilung von Nanomaterialien" - Projektteil Nanopartikel.
Es hat sich gezeigt, dass alle Methoden zur Bestimmung der Partikelgrößenverteilung Vor- und Nachteile haben. Es wird dringend empfohlen Größenverteilungen immer mit mindestens zwei unterschiedlichen Methoden zu bestimmen: Bildgebend und mit gute Anzahlstatistik.
Verschiedene Durchmesser wurden in der TG-PSD mit einem Indexsystem versehen, welches zukünftig Verwechslungen zwischen unterschiedlichen Durchmessern vermeiden soll.
Wird ein bestimmter Durchmesser benötigt (z.B. hydrodynamisch, aerodynamisch), muss die Methode passend gewählt werden. Eine Umrechnung von einem Durchmesser in einen anderen ist in der Regel fehlerbehaftet.
Es wurde ein einheitliches Reporting-System in der TG-PSD eingeführt.
Vorstellung der Ergebnisse bei der Entwicklung einer neuen OECD Prüfrichtlinie zur Bestimmung der Partikelgröße und Anzahlgrößenverteilung von Nanomaterialien. (Projektteil Fasern.)
Ergebnisse:
Abweichungen zwischen SEM and TEM insbesondere bei langen Fasern
Die Anwendung von TEM auf kurze Fasern < 5 µm beschränkt
Für SEM wurde keine signifikante Abhängigkeit der Bestimmung der Faserdurchmesser von der Pixelgröße der Aufnahmen festgestellt
Für TEM wurde eine Abhängigkeit der Bestimmung der Faserdurchmesser von der Pixelgröße festgestellt
Der Einfluss der Bildauswertenden auf die Varianz der Ergebnisse ist klein im Vergleich zu der gesamten Varianz.
Nanofasern können mit TEM und SEM bestimmt werden!
Vorstellung der Ergebnisse bei der Entwicklung einer neuen OECD Prüfrichtlinie zur Bestimmung der Partikelgröße und Anzahlgrößenverteilung von Nanomaterialien.
Ergebnisse:
Ideal sphärische Partikel sind gut und verlässlich mit vielen Methoden charakterisierbar.
Reale (Nicht ideale) Materialien sind gut charakterisierbar, wenn eine gewisse Homogenität und Stabilität vorliegt.
Stark inhomogene und stark agglomerierende Partikel liefern deutlich unterschiedliche Ergebnisse für verschiedene Methoden.
Partikel mit geringen Größenunterschieden lassen sich mit allen Methoden gut charakterisieren.
Partikel mit sehr deutlichen Größenunterschieden führen häufig zu einer Unterbewertung der kleineren Partikel.
Vollautomatische Partikeldetektion bei elektronenmikroskopischen Aufnahmen ist z.Zt. noch stark fehleranfällig und kann daher nicht empfohlen werden.
Es hat sich gezeigt, dass alle Methoden zur Bestimmung der Partikelgrößenverteilung Vor- und Nachteile haben. Es ist dringend zu empfehlen Größenverteilungen immer mit mindestens zwei unterschiedlichen Methoden zu bestimmen: Bildgebend und mit gute Anzahlstatistik.
Verschiedene Durchmesser wurden in der TG-PSD mit einem Indexsystem versehen, welches zukünftig Verwechslungen zwischen unterschiedlichen Durchmessern vermeiden soll.
Wird ein bestimmter Durchmesser benötigt (z.B. hydrodynamisch, aerodynamisch), muss die Methode passend gewählt werden. Eine Umrechnung von einem Durchmesser in einen anderen ist in der Regel fehlerbehaftet.
Es wurde ein einheitliches Reporting-System in der TG-PSD eingeführt.
In 1981 the OECD published the Test Guideline on Particle size and size distribution. This TG is still a valid document for the measurement of particles all over the world.
When nanomaterials gained importance, ISO set up a technical commitee for Nanotechnologies in 2005 and the OECD followed this step in 2006 with the Working Party on Manufactured Nanomaterials.
In the following years ISO and OECD published several documents about nanomaterials and the systematisation developed.
In 2017 it was finally clear that nanomaterials need to be adressed in another way than chemicals and in 2020 ECHA revised the REACH-Annexes accordingly and included nanomaterials.
Unfortunately there is a little problem with this: Only a few applicable test guidelines exit for the measurement of the nanomaterials. Several test guidelines date from 1981 and do not address nanomaterials.
The logical next step for the OECD would be to publish a series of test guidelines which are indeed currently prepared and will be shown in this talk.
Finally there is an additional need for the future of NM standardisation: Digitalisation.
Phosphorus (P) fertilizers from secondary resources became increasingly important in the last years. However, these novel P-fertilizers can also contain toxic pollutants. Chromium in its hexavalent state (Cr(VI)) is regulated with low limit values for agricultural products due to its high toxicity, but the determination of Cr(VI) in these novel fertilizer matrices can be hampered by redox processes that lead to false results. Thus, we applied the passive sampler technique Diffusive Gradients in Thin-films (DGT) for the determination of Cr(VI) in fertilizers and compared the results with the standard wet chemical extraction method (German norm DIN EN 15192) and Cr K-edge X-ray absorption near-edge structure (XANES) spectroscopy. We determined an overall good correlation between the wet chemical extraction and the DGT method. DGT was very sensitive and in most cases selective for the analysis of Cr(VI) in P-fertilizers. However, hardly soluble Cr(VI) compounds cannot be detected with the DGT method since only mobile Cr(VI) is analyzed. Furthermore, Cr K-edge XANES spectroscopy showed that the DGT binding layer also adsorbs small amounts of mobile Cr(III) compounds which leads to overestimated Cr(VI) values. The results of certain types of P-fertilizers containing mobile Cr(III) or partly immobile Cr(VI), showed that optimization of the DGT method is required to avoid over- or underestimation of Cr(VI).
The aim of this study was to investigate the passive sampler method Diffusive Gradients in Thin-films (DGT) for ammonium and nitrate in amended soils. Therefore, we used soils from a pot experiment with maize where nitrogen (N) was supplied as ammonium sulfate nitrate (ASN), without and with a nitrification inhibitor (NI). The additional use of a NI can delay the nitrification in the soil and making the ammonium available for a longer period in the soil solution after its application. Homogenized soil samples were collected directly from each pot after one week of incubation before sowing and after harvesting the maize. Nitrate and ammonium in these soil samples were extracted using DGT devices equipped with a Putolite A520E (for nitrate) and Microlite PrCH (for ammonium) binding layer. Ammonium DGT which determined the mobile and labile ammonium forms based on diffusion and the resupplies from the solid soil phase, only showed a significantly higher amount of extractable ammonium with NI compared to that without NI for some samples. However, significantly lower values were found for nitrate of treatments with NI compared to without NI after harvest. Thus, the lower nitrate amounts for treatments with NI compared to the treatments without NI after harvest indicated the delay of the nitrification process by the NI. Furthermore, we compared also the ammonium and nitrate
DGT results to chemical extraction with KCl solutions. The results demonstrated that the trends of DGT results and chemical extraction were complimentary through all the treatments.
Gypsum is widely used in the construction sector, and its worldwide consumption has been increasing now for several decades. Currently, the gypsum demand is met up to 60% by FGD gypsum (a by-product from coal-fired power plants) in Germany. The natural gypsum deposits cover the remaining gypsum demand. Due to national climate protection goals and the related shutdown of coal-fired power plants, the FGD gypsum supply will decrease significantly in the coming years and, therefore, other gypsum sources must be found.
Depending on the lifetime of the used gypsum products in the construction sector, an increase of gypsum in construction and demolition waste is to be expected. With regard to an upcoming shortage of gypsum, several approaches are being tested to recover gypsum from construction and demolition waste. Gypsum plasterboard recycling is already implemented on an industrial scale. Furthermore, new processes to recycle different types of gypsum products from construction and demolition waste are being examined. Of particular interest are different types of gypsum boards because they are well suited for selective dismantling. Therefore, they can be recovered comparatively free of impurities which is most important for the gypsum recycling.
In the research project “GipsRec 2.0”, funded by the Federal Ministry of Education and Research, recycling methods for gypsum fiberboards are being investigated. Additionally, the suitability of different types of synthetic gypsum as substitutes for FGD gypsum is being considered. Currently, the quantities of recycled gypsum are not sufficient with regard to the reduction of FGD gypsum. An increase of gypsum recycling should be achieved to narrow the future gypsum gap that will occur in the near future.
Antimicrobial surfaces have broad use in multiple settings including touch surfaces in hospitals, implanted devices, or consumer products. Their aim is to support existing hygiene procedures, and to help combat the increasing threat of antimicrobial resistance. However, concerns have been raised over the potential selection pressure exerted by such surfaces, which might drive the evolution and spread of antimicrobial resistance. In my presentation, I will highlight the risks and knowledge gaps associated with resistance on antimicrobial surfaces by different processes including evolution by de novo mutations and horizontal gene transfer, and species sorting of inherently resistant bacteria dispersed onto antimicrobial surfaces. The latter process has the potential to select for antibiotic resistance via cross-resistance between traits that confer resistance to both the antimicrobial surface coating and antibiotics. Conditions in which antibiotics and antimicrobial coatings are present simultaneously (e.g. implants) will lead to more complex interactions that can either result in the selection for or against antibiotic resistance. We mapped these interactions between several antimicrobials and antibiotics on growth and selection of Pseudomonas aeruginosa. We find prevalent physiological (i.e. synergy and antagonism) and evolutionary (i.e. cross-resistance and collateral sensitivity) combination effects. Understanding these interactions opens the door to tailor therapeutic interventions to select against resistance. In additions, we need new methods and translational studies that investigate resistance development to antimicrobial surfaces under realistic conditions. Therefore, I will present recent developments in our lab on the development of such a method based on existing efficacy standards.
A wide range of analytical methods are used to estimate the plant-availability of soil phosphorus (P). Previous investigations showed that analytical methods based on the Diffusive Gradients in Thin films (DGT) technique provide a very good correlations to the amount of bioavailable nutrients and pollutants in environmental samples (Davison 2016, Vogel et al. 2017). However, the DGT results do not identify which P compound of the soil has the high bioavailability. But there are various spectroscopic techniques (infrared, Raman, P K-edge and L-edge XANES and P NMR spectroscopy) available to characterize P species in soils. Therefore, spectroscopic investigation of DGT binding layers after deployment allow us to determine the specific compounds. Nutrients such as phosphorus and nitrogen are often, together with other elements, present as molecules in the environment. These ions are detectable and distinguishable by infrared, P K- and L-edge X-ray absorption near-edge structure (XANES) and NMR spectroscopy, respectively. Additionally, microspectroscopic techniques make it also possible to analyze P compounds on the DGT binding layer with a lateral resolution down to 1 μm2. Therefore, species of elements and compounds of e.g. a spatial soil segment (e.g. rhizosphere) can be mapped and analyzed, providing valuable insight to understand the dynamics of nutrients in the environment.