4 Material und Umwelt
Filtern
Dokumenttyp
- Vortrag (91) (entfernen)
Referierte Publikation
- nein (91)
Schlagworte
- Antimicrobial resistance (19)
- Biocides (19)
- MIC (13)
- Biofilms (12)
- Antimicrobial coating (9)
- Bacteria (9)
- Corrosion (8)
- Evolution (7)
- Microbiologically influenced corrosion (7)
- Standardization (7)
Organisationseinheit der BAM
- 4.1 Biologische Materialschädigung und Referenzorganismen (91) (entfernen)
Eingeladener Vortrag
- nein (91)
Microbiologically influenced corrosion (MIC) is a highly unpredictable process involving a complex group of microorganisms, including sulfate-reducing bacteria and methanogens. Standard laboratory MIC testing using static serum bottle enrichments is an easy but limited method, offering poor resolution on the biomineralization process of corrosion products. An example of this is the presumed corrosion product siderite by corrosive methanogens (Mi-MIC). Previous publications reported siderite was the sole corrosion product of M. maripaludis using metal coupons incubated under stationary conditions.
However, the formation of siderite is closely related to the surrounding environmental conditions, i.e. pH, CO2 concentration, flow and temperature. Thus, siderite as the sole corrosion product of Mi-MIC remain inconclusive and questionable. To study Mi-MIC effectively, a novel versatile multiport flow-column corrosion monitoring system (MFC) was developed. MFC allows sectional corrosion rate determination under flow conditions using different types of material, inoculum and packing material. MFC offers great flexibility, ease of operation and accurate corrosion measurements that can be combined with many other techniques. Using MFC, we studied multiple strains of methanogens and compared it with sulfate-reducing bacteria under neutral and low pH conditions. It was revealed by MFC that corrosive methanogens have equally high corrosion potential as sulfate-reducing bacteria. Additionally, siderite is not the dominant nor sole corrosion product of Mi-MIC. Thus, effective corrosion monitoring and establishing standard laboratory practices, i.e. incorporating MFC as part of regular testing process, will provide deeper understanding of MIC. This will allow further microbial electrophysiology understandings, contributing to effective mitigation strategy development.
Biocide mitigation strategies of microbiologically influenced corrosion (MIC) in the oil and gas industry have been primarily used to eliminate the growths of sulfate-reducing microorganisms (SRM). However, methanogenic Archaea (MA) can also be highly corrosive by using iron as an electron source for methanogenesis. Because of the fundamental physiological differences between archaea and bacteria, responses of MA towards SRM-specific biocides cannot be deduced using SRM. Due to the lack of information available on the effect of biocides on corrosive MA, we selected THPS, glutaraldehyde, nitrate and perchlorate to compare against corrosive SRM.
Preliminary results showed that at low concentrations of THPS (0-10 ppm), growth of MA was not affected, methane production and corrosion rates (0.1 mm/yr) were comparable between the different THPS concentrations. On the contrary, the SRM strain showed decreased corrosion rates (0.18 mm/yr to 0.03 mm/yr) with increasing THPS concentrations. Further corrosion tests including electrochemical measurements of different biocides on the growth of MA and SRM will be conducted. Such knowledge not only provide important insights on the physiological response of MA to biocides but also contribute to more effective mitigation strategies that can be both economic and environmentally beneficial.
Microbiologically influenced corrosion (MIC) is an expensive but unpredictable problem for the industries. The most well-known culprit for MIC is the sulfate-reducing microorganisms (SRM), such as members from the genus Desulfovibrio. It has been widely accepted that SRM can contribute significantly to MIC through the production of hydrogen sulfide (HS-) or in some cases a direct electron uptake from the metal surface. However, in a real environmental system, SRM is not exclusive and often involved with other microorganisms that may also contribute to MIC, such as methanogens.
Methanogenic archaea can produce methane (CH4) using H2+CO2, formate, methylated amines or acetate. Methanogens are highly abundant in the environment and many are found in very extreme conditions, such as high temperature and high salinity. Previous researches have demonstrated that methanogens are capable of MIC, though the specific mechanisms are still under investigation. In the oil and gas industry, methanogens are not considered as the main contributor for MIC since the corrosion rates are often too low. However, the tests for methanogen-induced MIC are usually performed at static conditions, which cannot represent the system accurately. Here, we developed a novel anaerobic system to evaluate the corrosion potential of methanogens under flow conditions. We will use the Methanococcus maripaludis KA1 strain, which was isolated from a crude oil tank, as the organism of interest. A separate system for Desulfovibrio alaskensis will be established for corrosion rate comparisons. Furthermore, we will study the synergistic effects of M. maripaludis and D. alaskensis on MIC under flow.
The processing of laser-induced periodic surface structures (LIPSS) represents a simple and robust way for the nanostructuring of solids that allows creating a wide range of surface functionalities featuring applications in optics, tribology, medicine, energy technologies, etc. While the currently available laser and scanner technology already allows surface processing rates at the m2/min level, industrial applications of LIPSS are sometimes hampered by the complex interplay between the nanoscale surface topography and the specific surface chemistry. This typically manifests in difficulties to control the processing of LIPSS and in limitations to ensure the long-term stability of the created surface functions. This presentation aims to identify some unsolved scientific problems related to LIPSS, discusses the pending technological limitations, and sketches the current state of theoretical modelling. Hereby, it is intended to stimulate further research and developments in the field of LIPSS for overcoming these limitations and for supporting the transfer of the LIPSS technology into industry.
Bakterielle Biofilme stellen in medizinischen und industriellen Bereichen ein ernsthaftes Problem dar. Eine der größten gesellschaftlichen Herausforderungen liegt in der zunehmenden Resistenz von Bakterien gegen Biozide, die bei antimikrobiellen Behandlungen eingesetzt werden, z.B. durch übermäßigen Einsatz in Medizin, Industrie und Landwirtschaft oder durch Reinigung und Desinfektion in Privathaushalten. Daher sind neue effiziente bakterienabweisende Strategien, die den Einsatz von Bioziden vermeiden, dringend erforderlich.
Ein vielversprechender Weg zur Erzielung bakterienabweisender Oberflächen liegt in der berührungslosen und aseptischen großflächigen Laserbearbeitung von technischen Oberflächen. Maßgeschneiderte Oberflächentexturen, ermöglicht durch verschiedene Laserbearbeitungsstrategien, die zu topographischen Skalen im Bereich von Nanometern bis Mikrometern führen, können eine Lösung für diese Herausforderung darstellen.
In dem Vortrag wird ein Überblick über den aktuellen Stand der Technik bei der subtraktiven Texturierung von Laseroberflächen zur Kontrolle der Biofilmbildung bei verschiedenen Bakterienstämmen und in unterschiedlichen Umgebungen gegeben. Auf der Grundlage spezifischer Eigenschaften von Bakterien und laserbearbeiteten Oberflächen werden die Herausforderungen antimikrobieller Oberflächendesigns erörtert und zukünftige Richtungen aufgezeigt.
Corrosion is a very expensive and serious problem in the different industry sectors, eg. Petroleum-, On- and off-shore, infrastructure. It is estimated that 20% of all corrosion damage is caused by microorganisms or microbiologically influenced corrosion (MIC). Several microorganisms are known to cause corrosion, including sulfate-reducing bacteria, nitrate-reducing bacteria, methanogens etc. For several years, methanogens were regarded as a mild corroder (~0.065 mm/yr), largely due to a lack of detailed investigation on the corrosion mechanism under real-environment simulated conditions. Resulting in the common belief that siderite, a non-conductive compound, is the sole corrosion product (CP) of methanogen-induced MIC (Mi-MIC).
To simulate natural environmental conditions, we developed and introduced the multiport flow column system (MFC), a multi-sectional corrosion flow-cell. Using the MFC, we obtained ten times higher corrosion rates than previously reported. With a combination of several analytical techniques, such as ToF-SIMS, SEM-EDS and FIB-SEM, we found strong indication that siderite is not the sole corrosion product of Mi-MIC. The corrosion layers contained phosphorus, oxygen, magnesium, calcium and iron. The differences in the CP between static and dynamic environments demonstrated the impact of testing procedures on the corrosive potential of methanogens. To further verify and deepen our understanding of Mi-MIC, we are currently studying the influence of additional environmental parameters (e.g. pH, salinity, flow rate) on Mi-MIC.
Overall, results of this study will expand the current understanding of MIC from both analytical and mechanistic points of view, thus aiding the development of different mitigation strategies for various industry sectors.
Microbiologically influenced corrosion (MIC) is a now well-known challenge and affects industry, society and infrastructure. For a long time, the impact of methanogen-induced MIC (Mi-MIC) was underestimated. This was mainly due to the rather low published corrosion rates and the presumed corrosion product siderite, which is not electrically conductive. In our laboratory, we were able to show that this trivialization or underestimation of Mi-MIC was due to the nature of the testing. The static systems used so far do not provide environmentally relevant information about the corrosion rate and the corrosion product, especially for methanogens
To further illustrate the importance of the environment on the MIC process, we established a multiport flow column (MFC), to simulate the natural environment. With this method, and in contrast to published results using the static conditions, we obtained ten times higher corrosion rates. We analyzed the corrosion products with a combination of techniques, like ToF-SIMS, SEM-EDS and FIB-SEM, and found strong evidence that siderite is not the sole corrosion product of Mi-MIC. The corrosion layers contain phosphorus, oxygen, magnesium, calcium and iron and lacked on carbon-related species. It is hypothesized that methanogens may have influenced the nucleation process of siderite, converting bicarbonate into carbon dioxide for methanogenesis. This results in increased localized corrosion and reduced siderite formation. To verify and deepen our understanding of Mi-MIC, we are currently studying the influence of additional environmental parameters (e.g. pH, salinity, flow rate etc.) on Mi-MIC and the subsequent impacts on corrosion rates and the corrosion products.
Overall, results of this study will expand the current understanding of MIC from both analytical and mechanistic points of view, thus aiding the development of different mitigation strategies for various industry sectors.
The role of methanogens in microbiologically influenced corrosion (Mi-MIC) is often neglected, due to 1) low reported corrosion rates and 2) the suspected corrosion product siderite, which is electrically non-conductive. Typically, MIC corrosion studies are carried out using batch cultures, which did not represent the dynamic conditions, i.e. pipeline and provide insufficient information on the overall corrosion potential.
We established a unique approach, a multiport flow column (MFC), to simulate pipeline conditions and obtained 10-times higher corrosion rates than previously published. Our result showed that testing procedures have a large impact on the corrosive potential of methanogens. We found strong indications with a combination of ToF-SIMS, SEM-EDS and FIB-SEM analyses that siderite is not the sole corrosion product. The corrosion layers contain phosphorus, oxygen, magnesium, calcium and iron. To verify and deepen our understanding of Mi-MIC, we are currently studying the influence of other environmental parameters (e.g. pH) on Mi-MIC.
With the latest ICP-MS technology - ICP-ToF (time of flight)-MS - it is possible to analyze the multi-element fingerprint of individual cells. The interface between material and environmental analysis thus receives special attention, e.g. when considering corrosion processes. Microbiologically influenced corrosion (MIC) is highly unpredictable due to the diversity of microbial communities involved. The development of the MIC-specific ICP-ToF-MS analytical method presented here at the single cell level, in combination with the investigation of steel-MIC interactions, contributes significantly to progress in instrumental MIC analysis and will enable clarification of the processes taking place.
The supplied document shows the basis of a four minutes lightning talk.
The latest ICP-MS technology - ICP-ToF (time of flight)-MS – enables the analysis of the multi-element fingerprint of individual cells. The interface between material and environmental analysis thus receives special attention, e.g., when considering corrosion processes. Microbiologically influenced corrosion (MIC) is a highly unpredictable phenomenon due to the influence of the environment, microbial communities involved and the respective electron source. However, the interaction pathway between cells and the metal surface remains unclear. The development of the MIC-specific ICP-ToF-MS analytical method presented here at the single cell level, in combination with the investigation of steel-MIC interactions, contributes significantly to progress in instrumental MIC analysis and will enable clarification of the processes taking place. For this, a MIC-specific staining procedure was developed. It allows the analysis of archaea at a single cell level and provides information about the interaction of the cells with the staining agent which is extremely scarce compared to other well characterized organisms. Additionally, the single cell ICP-ToF-MS is used for the analysis of archaea involved in MIC of steel. Hence, the possible uptake of individual elements from different steel samples is investigated - the information obtained will be used in the future to elucidate underlying mechanisms and develop possible material protection concepts, thus combining modern methods of analytical sciences with materials.