4 Material und Umwelt
Filtern
Erscheinungsjahr
- 2018 (21) (entfernen)
Dokumenttyp
- Vortrag (10)
- Zeitschriftenartikel (5)
- Buchkapitel (2)
- Beitrag zu einem Tagungsband (2)
- Posterpräsentation (2)
Sprache
- Englisch (21) (entfernen)
Schlagworte
- Leaching (5)
- Ecotoxicity (3)
- HP14 (3)
- Recycling materials (3)
- Bottom ash (2)
- Degradation (2)
- Geosynthetics (2)
- Risk assessment (2)
- Robustness studies (2)
- Waste management (2)
Organisationseinheit der BAM
- 4.3 Schadstofftransfer und Umwelttechnologien (21) (entfernen)
Eingeladener Vortrag
- nein (10)
Geosynthetics are widely used in hydraulic engineering and within coastal protection constructions at the Baltic Sea shore, such as walls, promenades, and gabions walls. Storms influence leads to deformation of some of the protection structures and cause the release of geotextiles onto the beach. Fragments of geotextile migrate along the shore, experiencing additional degradation and destruction down to macro-, meso-, and micro-particles. During October 2017 - March 2018, the Baltic Sea shore along the Sambia Peninsula (Kaliningrad Oblast of the Russian Federation) was monitored to establish the contamination of sandy beaches by geotextiles that had degraded. Several local sources of pollution of beaches by geosynthetic materials were established.
Transformation of carbendazim, diuron, octylisothiazolinone and terbutryn was investigated in two paints containing either white titanium dioxide or a red iron oxide pigment.
Test specimens of these coatings on glass were exposed to water contact and UVA-radiation under laboratory conditions. Panels of birch plywood were coated and exposed to natural weather conditions in a field experiment. Concentrations of biocides and transformation products were analysed in leachates from laboratory tests, runoff samples and remaining coatings. Water contact, UVA radiation as well as pigments in the paints affected the pattern and amount of transformation products.
Waste-to-energy (WtE) is one of the leading technologies for municipal solid waste (MSW) treatment in Europe. According to Eurostat data, in 2015, 27 % of MSW was utilized in WtE plants, which represents more than 80 million tons per year. Therefore, the European annual production of incineration bottom ash (IBA) is about 20 million tons, as it is about 25 wt% of input MSW. In the European List of Waste, IBA is listed as mirror entry (i.e. waste materials which should be classified as either non-hazardous or hazardous, depending on its hazardous properties and/or content of hazardous substances) under codes 19 01 11 and 19 01 12.
Recent trends indicate that WtE allows, apart from utilization of the energy content of waste, also the recovery of various valuable components. Hence, WtE can be included in the key technologies that can put the circular economy concept into practice. Secondary raw materials in the case of WtE are solid residues, especially IBA, as it is a secondary source, particularly of ferrous metals (Fe) and non-ferrous metals (NF) and glass. Moreover, the residual mineral fraction can be used for various applications in the construction industry, i.e. as aggregates substitute for bound or unbound applications, in cement manufacturing or, as indicated by recent research, also in more sophisticated applications, e.g. for ceramics production. Recovery of these metals can also cause huge greenhouse gas savings. Alone in Europe, metal recovery from IBA reduces greenhouse gas emissions by approximately 3.2 million tonnes of CO2 equivalent.
Small grain size fractions of municipal solid waste incineration (MSWI) bottom ash (BA) contain elemental and chemically bonded metals in appreciable amounts, especially copper. Investigations with a centrifugal concentrator were carried out using samples, which had been treated with different impact devices. Partly the impacts of single devices were visible in outlines, but mostly the surfaces of the metals were still covered with mineral residues. To generate copper rich fractions, parameters of the separation process should ensure mass yields <2%, best between 0.5 and 1%. The density of the concentrates is then generally >3.2 g/cm3. Best results were achieved with material from a special treatment train which is adapted to grain sizes <2 mm. Reliable copper contents between 20 and 40% (single runs >50%) could be realised.
However, considering the required mass yields, referred to this subset only 150–170 g copper would be recovered from 1 Mg MSWI BA. Furthermore, this copper is only in parts present in elemental form. A
dependable added value of such treatment step seems to be given only, if that enables a recycling of the mineral aggregates (tailings) in parallel to avoid landfill costs.
Direct and indirect effects (DIERec) of the recovery of secondary resources are in the range of 500 million tons per year in Germany; energy savings are 1.4 million TJ. These savings are between 10 and 20% of the total. The effects of materials recovery exceed those of energy recovery by far except for secondary plastic material, where DIERec from energy recovery is higher by factor of 2.7. Untapped potential for the recovery of secondary resources exists in the fine fraction of bottom ash from municipal solid waste incineration, mainly Cu and precious metals, and in urban mining.
Potential use of incineration bottom ash in construction – Evaluation of environmental impact
(2018)
Around 5 million tonnes of MSWI bottom ash (BA) are generated per year in Germany. The incineration itself serves for metals as a concentrating and cleaning process. However, due to the almost exclusive wet extraction out of the furnace chamber the various metals are integrated in a heterogeneous and instable matrix. The metal recovery is therefore still a challenge relating the recovery rate and the purity, respectively. With state of the art treatment trains in Germany around 7.7% of ferrous metals and 1.3% of non-ferrous metals can be recovered out of MSWI BA. Large quantities of the mineral fraction are reused for sub-base material in road construction. A three month ageing period has been established as the common practice of further treatment of bottom ash before reuse applications. In the course of this aging the pH value of bottom ash decreases and contaminants are immobilized by processes like carbonation, hydration and oxidation. In particular leaching of heavy metals may be reduced to environmentally acceptable levels. However, the aging results in fixing of other valuable resources such as metals. Two laboratory scale lysimeters (30 cm in diameter) are being operated for more than three years aiming at the investigation of the long-term leaching behavior of a 0.25/45 mm mineral material obtained by treatment of MSWI bottom ash directly after incineration by a wet processing technology. Artificial rainwater is used as leachant (pH ≈ 6, ingredients NO32-, Cl-, SO42-, Na+, K+, Ca2+, Mg2+). The lysimeters are irrigated related to an average annual precipitation rate of 600 mm/a leading to a liquid to solid ratio (L/S) of about 0.7 per year of operation. Lysimeter tests are more adequate to simulate field scenarios and long-term leaching behavior in contrast to laboratory column tests particularly due to the unsaturated conditions and realistic contact time with the leachant.
In comparison to the leaching of bottom ash (aged for 3 month and non-treated) in column tests the chloride and sulfate leaching in the lysimeters was reduced as a consequence of the previous wet processing. The sulfate release kept almost constant limited by CaSO4 solubility up to an L/S of about 0.7 l/kg. The chloride concentrations dropped quickly, starting from 7300 mg/l, and are now at an almost constant level of 50 mg/l which is significantly above the chloride concentration in the leachant. After an initial decrease of the pH from about 10.4 to 8 at L/S of 0.2 l/kg, the pH increased again and leveled out around 9.8 up to L/S 2.2 l/kg. At an L/S of about 2.5 l/kg now, Cr, Cu are still released. The Cu and Cr concentrations in the leachates were about 760 µg/l and 90 µg/l respectively at the beginning. For both metals the concentration decreased to about 35 µg/l now. The Mo concentrations dropped steadily from 1300 to 250 µg/l, whereas V and Sb concentrations increased in the course of the tests. Fe and Mn are not detectable anymore. More results of this experimental study will be presented and discussed with a special focus on elements forming oxyanions.
Whereas the behavior of geosynthetics in landfill engineering is well studied and documented since decades, little is known on application in applications such as coastal protection or ballast layers for wind energy plants.
However, due to the rapid expansion of offshore wind energy, rising water levels and more extreme weather conditions as a result of climate change more and more hydraulic engineering projects will be realized in the future.
Construction with geosynthetics has various advantages, but it has to be ensured that there is no negative environmental impact from the application of geosynthetics in hydraulic engineering.
It is expected that any effect will be visible only on the long-term. Therefore, accelerated testing is needed to derive requirements for geosynthetics in hydraulic engineering.
Die Präsentation erläutert die Hintergründe der nationalen Anforderungen für die Verwendung von Kunststoffdichtungbahnen in Deponieabdichtungen. Die Beständigkeit wird diskutiert. Anforderungen an das Qualitatsmanagement während der Produktion der Produkte und der Bauphase werden aufgezeigt und die Auswirkungen auf die langzeitige Funktionserfüllung werden beschrieben.
Microplastics are increasingly entering marine, limnic and terrestrial ecosystems worldwide, where they sorb hydrophobic organic contaminants. Here, the sorption behavior of the fuel-related water contaminants benzene, toluene, ethyl benzene and xylene (BTEX) and four tertiary butyl ethers to virgin and via UV radiation aged polypropylene (PP) and polystyrene (PS) pellets was investigated. Changes in material properties due to aging were recorded using appropriate polymer characterization methods, such as differential scanning calorimetry, Fourier transform infrared spectroscopy, gel permeation chromatography, X-ray photoelectron spectroscopy, and microscopy.
Pellets were exposed to water containing BTEX and the ethers at 130-190 mg/L for up to two weeks.
Aqueous sorbate concentrations were determined by headspace gas chromatography. Sorption to the polymers was correlated with the sorbate's Kow and was significant for BTEX and marginal for the ethers.
Due to substantially lower glass transition temperatures, PP showed higher sorption than PS. Aging had no effect on the sorption behavior of PP. PS sorbed less BTEX after aging due to an oxidized surface layer.