In Europe, nearly 19 Mt/y of bottom ash (BA) are produced. Of this quota, only 46 %wt. was treated, often in poorly performing plants, leaving behind 10 Mt of untreated and unrecovered BA, destined to landfill. The resulting 2.14 Mt loss of valuable materials included 1 Mt mineral fraction and 0.97 Mt ferrous metals, mostly from untreated BA, and 0.18 Mt non-ferrous metals, mostly from unrecovered BA. For the coarser fractions, the main obstacle to BA being used as recycling aggregate is the content of salts and potential toxic elements (PTEs), concentrated in a layer that coats BA particles. For the fine BA fractions, usually underexploited and landfilled, it is estimated that up to 0.95 Mt/y of ferrous and non-ferrous metals are not recovered in Europe.
During the workshop, the key results of BASH Treat project will be presented: the results of 2 industrial tests performed in BA treatment plants in Germany and Sweden; a novel dry treatment for the removal of salts and PTEs from BA coarse particles; a wet process for the recovery of heavy metal compounds from the fine fraction; a technical-economic assessment of the EU potential for the optimization of BA management.
Waste-to-energy (WtE) is one of the leading technologies for municipal solid waste (MSW) treatment in Europe. According to Eurostat data, in 2015, 27 % of MSW was utilized in WtE plants, which represents more than 80 million tons per year. Therefore, the European annual production of incineration bottom ash (IBA) is about 20 million tons, as it is about 25 wt% of input MSW. In the European List of Waste, IBA is listed as mirror entry (i.e. waste materials which should be classified as either non-hazardous or hazardous, depending on its hazardous properties and/or content of hazardous substances) under codes 19 01 11 and 19 01 12.
Recent trends indicate that WtE allows, apart from utilization of the energy content of waste, also the recovery of various valuable components. Hence, WtE can be included in the key technologies that can put the circular economy concept into practice. Secondary raw materials in the case of WtE are solid residues, especially IBA, as it is a secondary source, particularly of ferrous metals (Fe) and non-ferrous metals (NF) and glass. Moreover, the residual mineral fraction can be used for various applications in the construction industry, i.e. as aggregates substitute for bound or unbound applications, in cement manufacturing or, as indicated by recent research, also in more sophisticated applications, e.g. for ceramics production. Recovery of these metals can also cause huge greenhouse gas savings. Alone in Europe, metal recovery from IBA reduces greenhouse gas emissions by approximately 3.2 million tonnes of CO2 equivalent.
There is an ongoing debate on European scale concerning the criticality of phosphorus. In Switzerland and Germany, phosphorus recovery from phosphorus-rich waste streams will become obligatory. Sewage sludge ash is rich in phosphorus and may become an important secondary feedstock. Thermochemical treatment of sewage sludge ash with sodium sulphate under reducing conditions was shown to remove heavy metals from the solid product and produce the fully plant available crystalline phase CaNaPO4. Pilot-scale experiments in a rotary kiln were carried out at temperatures between 750 and 1000 °C and were compared to laboratory-scale experiments with crucibles. Process upscaling was successfully demonstrated but a series of differences were noticed: In comparison to laboratory-scale, solubility of phosphorus in samples from pilot-scale experiments was lower at all chosen treatment temperatures because of shorter retention time and incomplete decomposition of sodium sulphate. X-ray diffraction analysis revealed remaining phase fractions of whitlockite (Ca3-x(Mg,Fe)x(PO4)2) and sodium sulphate from the starting materials in products and thus indicated incomplete reaction. In contrast to the results of laboratory-scale experiments, the crystalline phase CaNaPO4 was clearly absent in the products from the rotary kiln but instead a Mg-bearing phase (Ca,Mg)NaPO4 was formed. Laboratory-scale experiments confirmed (Ca,Mg)NaPO4 is an intermediate phase between whitlockite and CaNaPO4. However, both crystalline phases are characterized by high plant availability. It was shown that heavy metal removal increased at higher temperatures whereas solubility and thus plant availability of phosphorus already reached its maxima at temperatures of 950 °C in pilot-scale and 875 °C in laboratory-scale experiments.
Popioły pochodzące z instalacji do spalania komunalnych osadów ściekowych, znajdującej się na terytorium Polski, poddano procesom termochemicznego przekształcania, dzięki czemu otrzymano produkty nawozowe spełniające kryteria dopuszczające je do obrotu jako nawozy mineralne. Ponadto dokonano analizy możliwości wykorzystania popiołów na cele nawozowe zgodnie z obecnie przyjętymi dokumentami strategicznymi i planistycznymi dotyczącymi gospodarki odpadami na poziomie krajowym i europejskim.