4 Material und Umwelt
Filtern
Dokumenttyp
- Zeitschriftenartikel (7)
- Beitrag zu einem Tagungsband (7)
- Vortrag (1)
Schlagworte
- Lichtbogenofen (4)
- LD-Schlacke (3)
- Recycling (3)
- Tantal (3)
- Leaching control mechanisms (2)
- Melting experiments (2)
- Pyrometallurgie (2)
- Pyrometallurgy (2)
- Tantalum (2)
- Zement (2)
- Zementklinker (2)
- Zinnschlacke (2)
- Alit (1)
- Alite (1)
- BOFS (1)
- Building and Construction (1)
- Carbide formation (1)
- Carbon feeding (1)
- Chlorine (1)
- Corrosion (1)
- EAF slags (1)
- Electric arc furnace (EAF) slags (1)
- Electric arc furnace slags (1)
- Elektrolichtbogenofen (1)
- FactSage calculations (1)
- FactSageTM calculations (1)
- General Materials Science (1)
- Hydration products (1)
- Laser-induced breakdown spectroscopy (1)
- Nano-Fourier-transform infrared spectroscopy (1)
- Niobium (1)
- On-line analysis (1)
- Perowskit (1)
- Portland Cement (1)
- Reduction process (1)
- Reduktionsprozess (1)
- Scattering-type scanning near-field optical microscopy (s-SNOM) (1)
- Sekundärrohstoff (1)
- Silicon carbide (1)
- Stahlwerksschlacke (1)
- Steelmaking slag (1)
- Synchrotron radiation (1)
- Thermal analysis (1)
- Tricalcium-silicate (1)
- Tricalciumsilikat (1)
- X-ray diffraction (1)
Organisationseinheit der BAM
- 4 Material und Umwelt (15) (entfernen)
Eingeladener Vortrag
- nein (1)
The present study shows the potential of high-resolution imaging and nano-Fourier-transform infrared (nano-FTIR) spectroscopy for corrosion science. The protective oxidation layers of different chlorine-gas treated silicon
carbides (SiCs) were characterized with these techniques. A nitrified SiC showed the highest resistant strength against chlorine corrosion at 1000 °C compared to the other SiCs. Nano-FTIR spectroscopy with a lateral resolution below 40 nm detected differences in the crystallinity of the bulk-SiC and in the transitional region to the protective layer. Furthermore, high-resolution imaging provides deep insight in the interfacial layer between bulk-SiC and the protective oxidation layer on sub-micrometer scale.
Fused cement clinker can be produced from molten basic oxygen furnace slag (BOFS) by way of a reductive thermochemical treatment. During the thermochemical treatment, oxidic iron is reduced to metallic iron and separated. The resulting low-iron slag has a chemical and mineralogical composition similar to ordinary Portland cement (OPC) clinker. In this study, the hydraulic reactivity of the fused clinker from BOFS with and without gypsum was investigated using isothermal calorimetry, differential scanning calorimetry, in situ X-ray diffraction and powder X-ray diffraction. Furthermore, a synthetic fused clinker without foreign ions and fused clinker produced by a mixture of both materials was studied. The hydraulic reaction of the fused clinker from BOFS was considerably slower than that of OPC. However, the reaction can be accelerated by adding gypsum as a sulfate carrier. Furthermore, the results showed an increased reaction rate with decreasing content of foreign ions such as Fe, P or Mn.
Die Zementindustrie erzeugt etwa 6-7% der globalen CO2-Emissionen und steht damit als Industriezweig vor dem Hintergrund einer anvisierten Klimaneutralität vor gewaltigen Herausforderungen. Der Prozess der Klinkerherstellung wurde über die vergangenen Jahrzehnte bereits kontinuierlich optimiert. Seit 1990 ist es der deutschen Zementindustrie gelungen, die spezifischen CO2-Emissionen der Zementproduktion u. a. durch den Einsatz alternativer, nicht fossiler Brennstoffe und durch Absenkung des Klinkergehalts im Zement um 20 % zu senken. Weitere konventionelle Minderungsstrategien versprechen jedoch nur noch wenig zusätzliche Reduktion. Im Falle des Portlandklinkers besteht die Schwierigkeit darin, dass zwei Drittel der CO2-Emissionen rohstoffbedingt durch die Entsäuerung des Kalksteins (CaCO3) anfallen, die durch die beschriebenen Maßnahmen nicht weiter abgesenkt werden können. Vielmehr wird es erforderlich sein, noch zu entwickelnde oder zu optimierende Technologien anzuwenden und ggf. alle relevanten Ebenen wie Produktion, Weiterverarbeitung und Anwendung von Zement und Beton neu zu denken. Neben technologischen Ansätzen zur CO2-Abscheidung mit nachfolgender langfristiger Speicherung (Carbon Capture and Storage – CCS) oder Verwertung (Carbon Capture and Utilisation – CCU) werden auch alternative Rohstoffe für die Zementproduktion und alternative Bindemittel in Betracht zu ziehen sein.
Tricalcium-silicate (C3S) or Alite is the most important mineral in Portland cement. Since pure tricalcium-silicate is only stable above temperatures of 1250 °C, its decomposition has to be prevented technically by fast cooling after the sintering process. At room temperature, the decomposition velocity is very slow so that metastable tricalcium-silicate is obtained.
Although the mechanisms of clinker phase formation during burning process of Portland cement in a rotary kiln were solved and improved over the years, in view of possible economic and ecological benefits current projects aim to produce clinker phases from metallurgical slags. Recent studies discovered that the mineral phase which remained after a reducing treatment and separation of formed metallic iron from molten Linz-Donawitz (LD-) slags contained about 60 wt.% Alite despite it was cooled slowly. Because the results could be verified using slags from different origins and varying cooling velocities a chemical stabilisation of the Alite can be assumed. First tests in mortars indicate that workability, hardening and solid state properties are comparable with an ordinary Portland cement. An application of the observed phenomenon in cement production requires enhanced knowledge about formation and stabilisation conditions of Alite during crystallisation from melts in contrast to the sintering reactions in conventional Portland cement production. Therefore, this study focuses on the stabilisation mechanisms of Alite in consolidating melts. Samples from different melting experiments are analysed to determine stabilising factors.
An existing pyrometallurgical process for tantalum and niobium recovery, mainly from low grade pyrometallurgical residues, was investigated. Series of melting experiments were carried out in a pilot-scale electric arc furnace to study how the amount, the grain size and the way of feeding affect the activity of carbon as a reducing agent. During the pyrometallurgical treatment refractory metals such as tantalum and niobium are reduced to their carbide form and enriched in the molten iron-based metal phase. The cooled down slag and metal phase were analysed to investigate thermodynamic and kinetic conditions of the carbide formation. FACT Sage simulations were also used to investigate the material system in state of thermodynamic equilibrium. Results show that mass transfer and kinetics may play an important role if compared to equilibrium analyses using FACT Sage.
LD-Schlacken weisen eine große chemische Ähnlichkeit zu Protlandzementklinker auf. Sie enthalten jedoch noch bis zu 30% Eisen, das mineralisch in oxidischer Form gebunden vorliegt. Dadurch kann sich bei der Erstarrung die wichtigste Klinkerphase "Alit" nicht ausbilden.
Durch eine reduzierende Schmelzbehandlung der Schlacke kann des mineralisch gebundene Eisen als Metall separiert werden. Dadurch wird auch die Mineralogie der Schlacke so verändert, dass auch sie nun praktisch einem Portlandzementklinker entspricht.
Entsprechende Versuche wurden am kleintechnischen Lichtbogenofen der BAM durchgeführt. Es werden Ergebnisse vorgestellt und auf Grenzen und Möglichkeiten eines derartigen Prozesses im Hinblick auf eine industrielle Umsetzung eingegangen.
LD-Schlacken weisen eine große chemische Ähnlichkeit zu Protlandzementklinker auf. Sie enthalten jedoch noch bis zu 30% Eisen, das mineralisch in oxidischer Form gebunden vorliegt. Dadurch kann sich bei der Erstarrung die wichtigste Klinkerphase "Alit" nicht ausbilden.
Durch eine reduzierende Schmelzbehandlung der Schlacke kann des mineralisch gebundene Eisen als Metall separiert werden. Dadurch wird auch die Mineralogie der Schlacke so verändert, dass auch sie nun praktisch einem Portlandzementklinker entspricht.
Entsprechende Versuche wurden am kleintechnischen Lichtbogenofen der BAM durchgeführt. Es werden Ergebnisse vorgestellt und auf Grenzen und Möglichkeiten eines derartigen Prozesses im Hinblick auf eine industrielle Umsetzung eingegangen.
Tantalum and niobium are essential for the development of electronics towards a more and more compact design, but without reducing their performance today. Especially in smart phones and tablets, tantalum and niobium capacitors with high charge densities have already become almost indispensable. However, tantalum as a critical raw material is still a problem for the sustainable production of electronics. Due to this fact, the existence of efficient recycling processes especially in Europe is becoming even more important nowadays.
The Bundesanstalt für Materialforschung und -prüfung (BAM) is currently working on the optimisation of an existing pyrometallurgical tantalum recycling process. Optimisation of this industrial process is carried out in a small-scale electric arc furnace (480 kVA, capacity approx. 150 kg/h) at BAM using a new and innovative equipment for on-line analysis of high temperature processes.
The aim of this project is to identify the best timing for an optimum slag tapping, when the slag is lower than minimum targeted tantalum concentration. Hence, LIBS (Laser induced breakdown spectroscopy) is used to identify the chemical composition of the slag layer and during slag tapping. The on-line-LIBS prototype of BAM enables an in-situ measurement of the element distribution in the melt after calibration on the slag system.
First results of this joint research project will be presented including LIBS-measurements and thermodynamic and kinetic aspects of the process.
Da das Recycling von tantalhaltigen Post-Consumer-Abfällen praktisch nicht existiert, stellen metallurgische Reststoffe eine äußerst wichtige Rohstoffquelle für das Tantalrecycling dar. Die meisten Zinnerze enthalten von Natur aus erhebliche Mengen an Refraktärmetallen. Diese Elemente werden in den Schlacken der pyrometallurgischen Primärzinngewinnung angereichert. Aufgrund ihrer vergleichsweise hohen Wertstoffkonzentration und ihrer Funktion als zusätzlicher Schlackenbildner stellen diese Schlacken einen wertvollen Rohstoff für die Verhüttung tantalhaltiger Reststoffe dar. In der vorliegenden Arbeit wird ein existierendes Verfahren zur Tantalrückgewinnung diskutiert, dem hauptsächlich pyrometallurgische Rückstände geringer Wertstoffkonzentration als Einsatzstoff dienen. Mit Hilfe des Verfahrens sollte dasoxidisch vorliegende Tantal vollständig reduziert und in der Metallphase angereichert werden. Weiterhin sollte vermieden werden, dass unerwünschte Elemente wie Titan in die Metallphase überführt werden. Ziel der Untersuchung war es, die ablaufenden Reduktionsprozesse besser zu verstehen, um so Ansätze für die Prozessoptimierung identifizieren zu können.
Basic oxygen furnace slags (BOFS) are by-products of the steelmaking process. Several researchers have studied the production of Portland cement clinker and metallic iron from BOFS via a reductive treatment.
In this study, we applied a carbothermal reduction of BOFS in a technical-scale electric arc furnace and characterised the clinker-like products. Those clinker-like non-metallic products (NMPs) had a chemical and mineralogical composition comparable to clinker for ordinary Portland cement (OPC) and contained large elongated alite crystals as major component. The pure NMPs reacted more slowly and achieved a lower degree of hydration compared with commercial OPC.
If the reactivity of the products can be further increased by employing specific adaptations, it can be used as a full clinker substitute for OPC. Nevertheless, it is also an option to use the material without further modifications as a cement component or concrete addition, which contributes to the strength development in both cases.