4 Material und Umwelt
Filtern
Dokumenttyp
Sprache
- Englisch (2)
Referierte Publikation
- ja (2) (entfernen)
Schlagworte
- BESSY (1)
- Bassanite (1)
- Building and Construction (1)
- Calcium sulfate (1)
- Environmental evaluation (1)
- General Environmental Science (1)
- Gypsum (1)
- Gypsum plasterboards (1)
- Gypsum waste (1)
- In situ (1)
- Industrial and Manufacturing Engineering (1)
- MySpot (1)
- Raman (1)
- Recycled gypsum (1)
- Renewable Energy, Sustainability and the Environment (1)
- Scattering (1)
- Strategy and Management (1)
- Synchrotron (1)
Organisationseinheit der BAM
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (2) (entfernen)
Here, we show that calcium sulfate dihydrate (gypsum) can be directly, rapidly and reversibly converted to calcium sulfate hemihydrate (bassanite) in high salinity solutions (brines). The optimum conditions for the efficient production of bassanite in a short time (<5 min) involve the use of brines with c(NaCl) > 4 M and maintaining a temperature, T > 80 °C. When the solution containing bassanite crystals is cooled down to around room temperature, eventually gypsum is formed. When the temperature is raised again to T > 80 °C, bassanite is rapidly re-precipitated. This contrasts with the better-known behaviour of the bassanite phase in low-salt environments. In low-salinity aqueous solutions, bassanite is considered to be metastable with respect to gypsum and anhydrite, and therefore gypsum-to-bassanite conversion does not occur in pure water. Interestingly, the high-salinity transformation of gypsum-to-bassanite has been reported by many authors and used in practice for several decades, although its very occurrence actually contradicts numerical thermodynamic predictions regarding solubility of calcium sulfate phases. By following the evolution of crystalline phases with in situ and time-resolved X-ray diffraction/scattering and Raman spectroscopy, we demonstrated that the phase stability in brines at elevated temperatures was inaccurately represented in the thermodynamic databases. Most notably for c(NaCl) > 4 M, and T > 80 °C gypsum becomes readily more soluble than bassanite, which induces the direct precipitation of the latter from gypsum. The fact that these transformations are controlled by the solution provides extensive opportunities for precise manipulation of crystal formation. Our experiments confirmed that bassanite remained the sole crystalline phase for many hours before reverting into gypsum. This property is extremely advantageous for practical processing and efficient crystal extraction in industrial scenarios.
Gypsum is widely used in the construction sector and its worldwide consumption has been increasing for several decades. Depending on the life-time of the used gypsum products, an increase of gypsum in construction and demolition waste follows. Especially against the background of a circular economy, the recycling of waste gypsum is of growing importance. However, the use of recycled gypsum makes only sense if it is environmentally friendly. Therefore, an evaluation of the environmental impacts of an industrial-scale processing for the recycling of post-consumer gypsum waste was conducted. The evaluation was performed with an established life cycle assessment software. Original data provided by industry and complementary data from a database for life cycle assessments were used for the calculations. Two scenarios for recycled gypsum with different transportation distances were calculated. These results are compared with results of the environmental evaluation of gypsum derived from coal-fired power plants (FGD gypsum) and natural gypsum. The results show that utilization of recycled gypsum can be environmentally advantageous compared to the use of natural gypsum or FGD gypsum, especially in the impact categories land transformation and resource consumption (abiotic depletion potential). For most environmental impact categories the specific transportation distances have a strong influence.