Tricalcium-silicate (C3S) or Alite is the most important mineral in Portland cement. Since pure tricalcium-silicate is only stable above temperatures of 1250 °C, its decomposition has to be prevented technically by fast cooling after the sintering process. At room temperature, the decomposition velocity is very slow so that metastable tricalcium-silicate is obtained.
Although the mechanisms of clinker phase formation during burning process of Portland cement in a rotary kiln were solved and improved over the years, in view of possible economic and ecological benefits current projects aim to produce clinker phases from metallurgical slags. Recent studies discovered that the mineral phase which remained after a reducing treatment and separation of formed metallic iron from molten Linz-Donawitz (LD-) slags contained about 60 wt.% Alite despite it was cooled slowly. Because the results could be verified using slags from different origins and varying cooling velocities a chemical stabilisation of the Alite can be assumed. First tests in mortars indicate that workability, hardening and solid state properties are comparable with an ordinary Portland cement. An application of the observed phenomenon in cement production requires enhanced knowledge about formation and stabilisation conditions of Alite during crystallisation from melts in contrast to the sintering reactions in conventional Portland cement production. Therefore, this study focuses on the stabilisation mechanisms of Alite in consolidating melts. Samples from different melting experiments are analysed to determine stabilising factors.
An existing pyrometallurgical process for tantalum and niobium recovery, mainly from low grade pyrometallurgical residues, was investigated. Series of melting experiments were carried out in a pilot-scale electric arc furnace to study how the amount, the grain size and the way of feeding affect the activity of carbon as a reducing agent. During the pyrometallurgical treatment refractory metals such as tantalum and niobium are reduced to their carbide form and enriched in the molten iron-based metal phase. The cooled down slag and metal phase were analysed to investigate thermodynamic and kinetic conditions of the carbide formation. FACT Sage simulations were also used to investigate the material system in state of thermodynamic equilibrium. Results show that mass transfer and kinetics may play an important role if compared to equilibrium analyses using FACT Sage.
Tantalum and niobium are essential for the development of electronics towards a more and more compact design, but without reducing their performance today. Especially in smart phones and tablets, tantalum and niobium capacitors with high charge densities have already become almost indispensable. However, tantalum as a critical raw material is still a problem for the sustainable production of electronics. Due to this fact, the existence of efficient recycling processes especially in Europe is becoming even more important nowadays.
The Bundesanstalt für Materialforschung und -prüfung (BAM) is currently working on the optimisation of an existing pyrometallurgical tantalum recycling process. Optimisation of this industrial process is carried out in a small-scale electric arc furnace (480 kVA, capacity approx. 150 kg/h) at BAM using a new and innovative equipment for on-line analysis of high temperature processes.
The aim of this project is to identify the best timing for an optimum slag tapping, when the slag is lower than minimum targeted tantalum concentration. Hence, LIBS (Laser induced breakdown spectroscopy) is used to identify the chemical composition of the slag layer and during slag tapping. The on-line-LIBS prototype of BAM enables an in-situ measurement of the element distribution in the melt after calibration on the slag system.
First results of this joint research project will be presented including LIBS-measurements and thermodynamic and kinetic aspects of the process.