3.4 Sicherheit von Lagerbehältern
Filtern
Erscheinungsjahr
- 2018 (41) (entfernen)
Dokumenttyp
- Vortrag (20)
- Beitrag zu einem Tagungsband (8)
- Zeitschriftenartikel (5)
- Posterpräsentation (5)
- Buchkapitel (2)
- Monografie (1)
Schlagworte
- Metal seal (9)
- Creep (7)
- Long-term behavior (6)
- Endlagerbehälter (5)
- Seal (4)
- Ageing (3)
- Hochaktive wärmeentwickelnde Abfälle (3)
- IAEA (3)
- Numerical simulation (3)
- Radioactive (3)
Organisationseinheit der BAM
- 3 Gefahrgutumschließungen; Energiespeicher (41)
- 3.4 Sicherheit von Lagerbehältern (41)
- 3.3 Sicherheit von Transportbehältern (7)
- 5 Werkstofftechnik (2)
- 5.2 Metallische Hochtemperaturwerkstoffe (2)
- 3.0 Abteilungsleitung und andere (1)
- 8 Zerstörungsfreie Prüfung (1)
- 8.0 Abteilungsleitung und andere (1)
Eingeladener Vortrag
- nein (20)
During dynamic processes, a certain range of strain rates is often observed along loaded structures and components. For precise numerical simulations, it is necessary to determine rate-dependent properties in dynamic tests and to describe the material behavior correctly within an appropriate domain of strain rates including adiabatic heating effects at higher strain rates, typically higher than 10 1/s. In principle, numerical simulations are compared to experimental results to verify the applied material models. For dynamic tensile tests considering ductile materials and large plastic deformation beyond uniform elongation, it is challenging to obtain comparable results due to plastic instability and necking of the specimen, e.g..
Based on the strain gradient in a general tensile specimen, a theoretical criterion was derived describing the plastic instability in rate-dependent materials under isothermal conditions in. It was applied to different multiplicative and additive constitutive relations and the analytical onset of necking was compared to results from numerical calculations of quasi-static and dynamic tensile tests. The simulations of a sheet-metal specimen with rectangular cross-section were carried out using the Finite Element Method and it was found that the numerical calculated and the theoretical predicted onset of plastic instability agree very good. The analytical criterion for instability holds even for specimens without geometrical or material imperfections and confirms that the onset of plastic instability must be considered a material characteristic.
However, real dynamic problems with higher strain rates are not isothermal, the heat generated by plastic work is not dissipated to the surrounding and the temperature of the material increases significantly. Adiabatic heating and thermal softening must be considered within the constitutive relations of rate-dependent materials and the discussion of plastic instability. In this paper, an enhanced and more generalized approach for the description of the condition for stability is discussed and applied to phenomenological as well as more physical constitutive relations from the literature. This allows an individual assessment of the accuracy and verification of rate-dependent material models with respect to plastic instability.
Component and material investigations on metal seals for high level radioactive waste containers
(2018)
Long-term investigations performed at BAM look to extend the state of knowledge on safety-related components of interim storage containers. Metal seals act as the primary sealing barrier in the bolted double lid closure system of the containers. The behaviour of metal seals has been investigated for ageing times up to 8.5 years and for various temperatures. The main cause for reduction in useable resilience overtime was due to creep deformation of the outer jacket of the seal.
For the long-term storage of spent nuclear fuel and other high-Level radioactive waste, dual purpose casks for the transportation and storage are widely used. Usually, these casks consist of a thick-walled monolithic cask body and a bolted double barrier lid System equipped with metal seals (consisting of an inner helical spring and two outer metal layers with a total cross-section diameter between 5 and 10 mm) to ensure the long-term safe confinement of the radioactive inventory.
Based on analytical and experimental studies, such metallic Systems have been qualified of storage periods of up to four decades so far as long as proper manufacturing and assembling conditions are met. More than 20 years of Operation experience with a permanently increasing number of casks has shown full compliance with the expectations.
In the meantime many countries have to face a significant delay of establishing a high-level radioactive waste repository what leads to Need for extending interim storage periods for probably 60, 80 or 100 years.
For that reason the long-term performance of metal seals for such time periods is of specific internst to demonstrate their sufficient safety function and specific investigations have already been launched, e.g. by BAM, to gain more experimental data and to develop validated models to extrapolate the seal performance to longer periods of time and or requested temperature levels.
Optical and thermal analysis of PVB encapsulant polymer functionalized with luminescent organic dyes
(2018)
This work focused on the technology of luminescent down shift (LDS), with a primary aim to identify and investigate a methodology to introduce the luminescent organic dye into PVB polymer encapsulant as emergent material for photovoltaic application. For this goal, we propose to study the feasibility to implement the LDS functionality and to identify suitability of available luminescent to be incorporated into the host polymer encapsulant material. The first step to this direction was through a comprehensive optical study of Violet 570 (V) organic dye in ethanol solvent. The methodology and experimental conditions such as laboratory polymer preparation and luminescence dye concentration were presented. Also, the emergent polymer encapsulant sheets were characterized by using optical and thermal analysis techniques. The absorption spectrum of the prepared PVB material shifts towards longer wavelengths, with increasing organic dye concentration.
After restarting the site selection process for a final repository for spent nuclear fuel (SNF) and heat-generating radioactive waste, all areas with one of the three potential host rock formations considered in Germany – salt, clay and crystalline rock – are under review. The project “KoBrA“, run by BGE TECHNOLOGY and BAM, collects and reviews requirements, criteria and proposals for final disposal container concepts complying with the current safety standards, taking into consideration international experience in the field of high-level nuclear waste (HLW) management.
Accident safe packages for the transport of spent nuclear fuel and high-level waste shall fulfil international IAEA safety requirements. Compliance is shown by consecutive mechanical and thermal testing. Additional numerical analysis are usually part of the safety evaluation. For damage protection some package designs are equipped with wood filled impact limiters encapsulated by steel sheets. The safety of these packages is established in compliance with IAEA regulations. Cumulative mechanical and fire tests are conducted to achieve safety standards and to prevent loss of containment. Mechanical reliability is proven by drop tests. Drop testing might cause significant damage of the impact limiter steel sheets and might enable sufficient oxygen supply to the impact limiter during the fire test to ignite the wood filling. The boundary conditions of the fire test are precisely described in the IAEA regulatory. During the test the impact limiter will be subjected to a 30 minute enduring fire phase. Subsequent to the fire phase any burning of the specimen has to extinguish naturally and no artificial cooling is allowed. At BAM a large-scale fire test with a real size impact limiter and a wood volume of about 3m3 was conducted to investigate the burning behaviour of wood filled impact limiters in steel sheet encapsulation. The impact limiter was equipped with extensive temperature monitoring equipment. Until today burning of such impact limiters is not sufficiently considered in transport package design and more investigation is necessary to explore the consequences of the impacting fire. The objective of the large scale test was to find out whether a self-sustaining smouldering or even a flaming fire inside the impact limiter was initiated and what impact on the cask is resulting. The amount of energy, transferred from the impact limiter into the cask is of particular importance for the safety of heavy weight packages. With the intention of heat flux quantification a new approach was made and a test bench was designed.
Packages for the transport and storage of radioactive materials are often sealed with elastomer or metal seals. These seals are basic components to meet the leak tightness criteria for these kind of packages. An overview over ongoing research and development concerning metal and elastomer seals is given in the presentation. Introductions in the fundamental functionality of elastomer and metal seals are presented. Ageing processes are shown for both components regarding to different ageing effects.
Accident safe packages for the transport of spent nuclear fuel and high-level waste shall fulfil international IAEA safety requirements. Compliance is shown by consecutive mechanical and thermal testing. Additional numerical analysis are usually part of the safety evaluation. For damage protection some package designs are equipped with wood filled impact limiters encapsulated by steel sheets. The safety of these packages is established in compliance with IAEA regulations. Cumulative mechanical and fire tests are conducted to achieve safety standards and to prevent loss of containment. Mechanical reliability is proven by drop tests. Drop testing might cause significant damage of the impact limiter steel sheets and might enable sufficient oxygen supply to the impact limiter during the fire test to ignite the wood filling. The boundary conditions of the fire test are precisely described in the IAEA regulatory. During the test the impact limiter will be subjected to a 30 minute enduring fire phase. Subsequent to the fire phase any burning of the specimen has to extinguish naturally and no artificial cooling is allowed. At BAM a large-scale fire test with a real size impact limiter and a wood volume of about 3m³ was conducted to investigate the burning behaviour of wood filled impact limiters in steel sheet encapsulation. The impact limiter was equipped with extensive temperature monitoring equipment. Until today burning of such impact limiters is not sufficiently considered in transport package design and more investigation is necessary to explore the consequences of the impacting fire. The objective of the large scale test was to find out whether a self-sustaining smouldering or even a flaming fire inside the impact limiter was initiated and what impact on the cask is resulting. The amount of energy, transferred from the impact limiter into the cask is of particular importance for the safety of heavy weight packages. With the intention of heat flux quantification a new approach was made and a test bench was designed. A first computational simulation of transport package temperatures taking into account the results of the conducted fire test was performed.
THz and mid IR spectroscopy of high-molecular PE (HMW) and ultra high-molecular PE (UHMW) reveals modifications of the molecular structure. Characteristic absorption bands are changed if the two materials are exposed by γ-Co60 radiation up to 600 kGy and subsequently stored at an annealing temperature of 398 K until for 729 days.
Low temperature performance of rubber seals - Influence of crystallite formation on seal performance
(2018)
Rubbers are widely used as sealing materials in various applications. In many fields the function of seal materials at low temperatures is necessary. Therefore, the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance.
It is known that rubbers possess strongly temperature dependent material properties. At low temperatures high changes in the material properties are observed which can be caused by the rubber-glass transition (abbr. glass transition) or for some rubbers also by partial crystallisation at lower temperatures. During continuous cooling the material changes during rubber-glass transition from rubber-like entropy-elastic behaviour to stiff energy-elastic behaviour. In case of (thermal-) crystallisation the formed crystallites act as additional (physical) crosslinks within the material but the molecules in the amorphous phase can still behave like a rubber. Hence, rubbers are normally used above rubber-glass transition and (thermal-) crystallization temperature but the minimum working temperature limit is heavily depending on the application conditions. Therefore, the lower operation temperature limit of rubber seals is under investigation.
In the past we have investigated material properties and sealing behaviour of rubber seals at low temperatures. As the initial work was dedicated to purely static sealing conditions we started to investigate the effect of a small partial release of rubber seals at low temperatures to study the influence of dynamic events on leak tightness. In addition, other groups report on the influence of counterpart surface and adhesion.
In this contribution we focus on the difference between purely amorphous elastomers and elastomers which become partially crystalline at low temperatures. The influence of partial crystallization on the low temperature performance of rubber seals is discussed.