3.4 Sicherheit von Lagerbehältern
Filtern
Dokumenttyp
- Vortrag (75)
Referierte Publikation
- nein (75)
Schlagworte
- Ring Compression Test (10)
- Spent Nuclear Fuel (9)
- Cladding Embrittlement (8)
- Compression set (8)
- Metal seal (8)
- Ageing Management (7)
- Extended Storage (7)
- Seal (7)
- Ageing (6)
- Cladding (6)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (75) (entfernen)
Embrittlement of spent fuel claddings during long-term dry interim storage - Current approach at BAM
(2019)
In this presentation, the actual situation of long-term dry interim storage of spent nuclear fuel in Germany is reported. An extension of the interim storage period between 40 and 100 years for at least a relevant number of casks is foreseeable. To demonstrate the integrity of fuel rods and cladding tubes throughout the extended dry interim storage, a potential cladding embrittlement should be investigated. The current approach at BAM is a research project on experimental and numerical investigations of sudden failure of unirradiated pre-hydrided cladding tubes after hydride reorientation at small deformation under Ring Compression Test conditions. A fracture mechanics based failure analysis and suggested failure criteria for a potential brittle failure of spent fuel claddings after long-term dry interim storage under mechanical loads are discussed.
In this presentation, the history and actual situation of the German nuclear waste management policy of spent fuel (SF) and high-level waste (HLW) is reported. Beside the description of the restructuration of responsible authorities and organizations in Germany, the principle of dry interim storage of SF and HLW in dual purpose casks is explained. The need for extended interim storage towards disposal implicates additional challenges for the nuclear waste management strategy in Germany. (Extended)interim storage, subsequent transportation, and final disposal are closely linked. Integrated approaches concerning waste package designs and operations are supposed to be beneficial for the establishment of efficient long-term SF and HLW management strategies. Knowledge management and staff recruiting, education and training during phase out and beyond nuclear power plant operation are major issues.
Three-dimensional finite element analysis of O-ring metal seals considering manufacture tolerances
(2019)
Metal seals are widely used in various industrial branches with severe working conditions (e.g. high pressure, high temperature, corrosion, or radioactive radiation). For example, O-ring metal seals are applied in the closure lid system of transport and storage casks for radioactive materials to guarantee an approved specified leak-tightness and the safe enclosure of the radioactive inventory. Within safety assessments of those casks under normal or accident conditions during transport and long-term interim storage for several decades, numerical simulations of the thermo-mechanical behavior of metal seals by using finite element (FE) analyses are suitable and effective.
In general, finite element codes provide the possibility to construct a complex three-dimensional (3D) modelling of metal seals with solid elements, cf., where all components of the metal seals are modeled in detail. This modelling is complex but allows the consideration of underlying physical effects such as elastic-plastic deformation, thermal expansion, creep/relaxation, friction and possible local damage. Therefore, this approach permits the investigation and understanding of the complex behavior of metal seals in detail which can hardly be measured for all seal components.
In a prior work, the complex 3D modelling approach was applied to investigate the influence of each seal component on the global seal force by considering varying material properties and different seal diameters. In the present contribution, the influence of manufacturing tolerances is discussed. At first, the results of prior work are summarized. After that, the manufacturing tolerances of the studied O-ring metal seal types are described and the corresponding FE model with all individual components is introduced. Finally, the influence of varying manufacturing tolerances of each seal component on the global seal force is analyzed and discussed.
Safety of long term containment and storage of radioactive waste is an essential issue, which is increasingly gaining international attention. Extending interim storage beyond initial license periods is one of the major challenges worldwide.
BAM has been involved in all kinds of radioactive waste container safety evaluation for storage and transportation including their long term performance from the very beginning. Today, all work related to the safe management of radioactive waste is linked by the activity field “Nuclear Waste Management” within the Focus Area “Energy” at BAM and in conjunction with a research strategy and agenda. Most recently, the working group “Long Term Safety of Container Systems and Components” was established to launch and perform research projects related to safety issues concerning the extended interim storage of radioactive waste.
For example, within our project LaMEP, we investigate ageing effects of metal and elastomer seals as well as polymeric neutron shielding materials, which are container components that fulfil major safety functions. The results of the experiments help to understand the long term behaviour of these components. Likewise, our project BRUZL started at BAM in 2018 with the aim of developing a fracture mechanics approach to understand and describe a potential brittle failure mechanism of fuel cladding during long-term interim storage. BAM also contributes to the GRS project “Development of methods and models and international exchange for safety evaluation in the frame of interim storage of radioactive waste”. Additionally, BAM is involved in several international research programmes dealing with extended interim storage, such as the European Joint Programme on Radioactive Waste Management (EURAD), the Extended Storage Collaboration Program (ESCP) and IAEA Coordinated Research Projects.
The present contribution provides a comprehensive overview of BAM research activities contributing to national and international gap analyses and to filling knowledge gaps regarding the safe long term management of radioactive waste.
The investigation of the long-term performance of sealing systems employed in containers for radioactive waste and spent nuclear fuel is one research focus area for division 3.4 “Safety of Storage Containers” at the Bundesanstalt für Materialforschung und -prüfung (BAM). Our investigations comprise investigations on metallic and elastomeric seals and covers experimental investigations to get a database on the component/material behaviour, work on analytical descriptions and numerical analysis. Our aim is to understand the long-term behaviour of the sealing systems for evaluation of their performance during possible extended interim storage and subsequent transportation.
Die Verfügbarkeit von Behältern für die Entsorgung nicht Wärme entwickelnder radioaktiver Abfälle im Endlager Konrad stellt ein wesentliches Element des nationalen Entsorgungskonzeptes für diese Abfallart dar. Grundlage für die Verfügbarkeit geeigneter Behälter sind typspezifische Bauartprüfungen, auf deren Grundlage eine Eignungs-feststellung in Form eines Prüfzeugnisses durch die Bundesgesellschaft für Endlagerung mbH (BGE), vormals Bundesamt für Strahlenschutz (BfS), erfolgt. Die Prüfgrundlagen sind in den durch das BfS (heute BGE) veröffent-lichten „Anforderungen an endzulagernde radioaktive Abfälle“ (Endlagerungsbedingungen) sowie der zugehörigen „Produktkontrolle radioaktiver Abfälle, radiologische Aspekte“ (PK) verankert. Die Eignungsfeststellung für eine Behälterbauart ist gleichzeitig die Grundlage für eine Behälterserienfertigung entsprechend den im Prüfzeugnis verankerten Spezifikationen und Randbedingungen.
Mit den Gesetzen zur Neuordnung der Organisationsstruktur im Bereich der Endlagerung (Mitte 2016) und zur Neuordnung der Verantwortung in der kerntechnischen Entsorgung (Mitte 2017) mit der Finanzierung des Kern-energieausstiegs wurden wesentliche Weichenstellungen im Hinblick auf den anstehenden Rückbau der bereits stillgelegten und in den kommenden Jahren noch stillzulegenden deutschen Kernkraftwerke vorgenommen. Bezüg-lich der nicht Wärme entwickelnden radioaktiven Abfälle führt dies zu einer spürbaren Intensivierung der Anstren-gungen zur Bereitstellung qualifizierter Gebinde für das Endlager Konrad, das nach aktueller Planung bis 2027 sei-nen Einlagerungsbetrieb aufnehmen soll. Dies wiederum führt zu einer erheblichen Verdichtung der Verfahren zur Behälterbauartprüfung, die allen Seiten (Antragsteller, BGE, Gutachter) erhebliche Anstrengungen abfordert.
Die Bundesanstalt für Materialprüfung und –forschung (BAM) ist auf Grundlage des Kap. 7 der o. g. „Produktkon-trolle …“ (PK) von der BGE mit den Behälterbauartprüfungen für das Endlager Konrad beauftragt. Hierbei ist eine Vielzahl von Anforderungen zu berücksichtigen, wozu neben den Anforderungen an Abfallbehälter gemäß Kap. 5 der Endlagerungsbedingungen weitere Anforderungen an die Verpackung (Kap. 3.2.2 PK), Kenngrößen (Kap. 3.5.1 PK) und schließlich die eigentliche Prüfung von Behältern/Verpackungen zählt (Kap. 7 PK). Letzteres beinhaltet die umfassende Behälterbeschreibung und –spezifikation, die Behälterauslegung, die thermischen und mechanischen Baumusterprüfungen (z.B. Brand- und Fallprüfungen), und schließlich die qualitätssichernden Maßnahmen für Her-stellung und Betrieb der Behälter. Neben der klassischen Bauartprüfung neuer Behältertypen spielt auch die Prü-fung bereits hergestellter Behälter, sog. Altbehälter, eine wesentliche Rolle, da sich etliche tausend Gebinde be-reits in der Zwischenlagerung befinden und nach Möglichkeit für das Endlager Konrad qualifiziert werden sollen.
Dieser Beitrag berichtet aktuell über den Umfang und Stand der laufenden Bauartprüfungen bei der BAM unter Be-rücksichtigung der besonderen Herausforderungen und der zuletzt erzielten Fortschritte. Dabei erfordert die paral-lele Bearbeitung der zahlreichen Verfahren einen verstärkten Koordinierungsbedarf hinsichtlich vergleichbarer fach-licher Aspekte sowie hinsichtlich Priorisierung und Ressourceneinsatz. Bei den experimentellen Nachweisen (Fall- und Brandversuche) betrifft das hinsichtlich der Nutzung der Versuchseinrichtungen bei der BAM die Koordination mit anderen Prüfaufträgen, wie z. B. verkehrsrechtliche Baumusterprüfungen. Schließlich erfordern diverse Fach-fragen zur Interpretation der Anforderungen aus Endlagerungsbedingungen und Produktkontrolle intensive Abstim-mungsprozesse zwischen BAM, BGE und Antragstellern. Wichtige Ergebnisse mit übergeordneter Bedeutung wer-den in Form erläuternder Fachnotizen durch die BGE veröffentlicht und können so bei zukünftigen Antragsverfahren berücksichtigt werden.
Packages for the transport and storage of radioactive materials are often sealed with elastomer or metal seals. These seals are basic components to meet the leak tightness criteria for these kind of packages. An overview over ongoing research and development concerning metal and elastomer seals is given in the presentation. Introductions in the fundamental functionality of elastomer and metal seals are presented. Ageing processes are shown for both components regarding to different ageing effects.
Accident safe packages for the transport of spent nuclear fuel and high-level waste shall fulfil international IAEA safety requirements. Compliance is shown by consecutive mechanical and thermal testing. Additional numerical analysis are usually part of the safety evaluation. For damage protection some package designs are equipped with wood filled impact limiters encapsulated by steel sheets. The safety of these packages is established in compliance with IAEA regulations. Cumulative mechanical and fire tests are conducted to achieve safety standards and to prevent loss of containment. Mechanical reliability is proven by drop tests. Drop testing might cause significant damage of the impact limiter steel sheets and might enable sufficient oxygen supply to the impact limiter during the fire test to ignite the wood filling. The boundary conditions of the fire test are precisely described in the IAEA regulatory. During the test the impact limiter will be subjected to a 30 minute enduring fire phase. Subsequent to the fire phase any burning of the specimen has to extinguish naturally and no artificial cooling is allowed. At BAM a large-scale fire test with a real size impact limiter and a wood volume of about 3m³ was conducted to investigate the burning behaviour of wood filled impact limiters in steel sheet encapsulation. The impact limiter was equipped with extensive temperature monitoring equipment. Until today burning of such impact limiters is not sufficiently considered in transport package design and more investigation is necessary to explore the consequences of the impacting fire. The objective of the large scale test was to find out whether a self-sustaining smouldering or even a flaming fire inside the impact limiter was initiated and what impact on the cask is resulting. The amount of energy, transferred from the impact limiter into the cask is of particular importance for the safety of heavy weight packages. With the intention of heat flux quantification a new approach was made and a test bench was designed. A first computational simulation of transport package temperatures taking into account the results of the conducted fire test was performed.
Low temperature performance of rubber seals - Influence of crystallite formation on seal performance
(2018)
Rubbers are widely used as sealing materials in various applications. In many fields the function of seal materials at low temperatures is necessary. Therefore, the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance.
It is known that rubbers possess strongly temperature dependent material properties. At low temperatures high changes in the material properties are observed which can be caused by the rubber-glass transition (abbr. glass transition) or for some rubbers also by partial crystallisation at lower temperatures. During continuous cooling the material changes during rubber-glass transition from rubber-like entropy-elastic behaviour to stiff energy-elastic behaviour. In case of (thermal-) crystallisation the formed crystallites act as additional (physical) crosslinks within the material but the molecules in the amorphous phase can still behave like a rubber. Hence, rubbers are normally used above rubber-glass transition and (thermal-) crystallization temperature but the minimum working temperature limit is heavily depending on the application conditions. Therefore, the lower operation temperature limit of rubber seals is under investigation.
In the past we have investigated material properties and sealing behaviour of rubber seals at low temperatures. As the initial work was dedicated to purely static sealing conditions we started to investigate the effect of a small partial release of rubber seals at low temperatures to study the influence of dynamic events on leak tightness. In addition, other groups report on the influence of counterpart surface and adhesion.
In this contribution we focus on the difference between purely amorphous elastomers and elastomers which become partially crystalline at low temperatures. The influence of partial crystallization on the low temperature performance of rubber seals is discussed.
Der Vortrag vermittelt einen Überblick über internationale Forschungsaktivitäten im Hinblick auf zukünftig deutlich zu verlängernde Zwischenlagerzeiträume für bestrahlte Brennelemente. Ausgehend von der aktuellen Entsorgungssituation werden die relevanten Fragestellungen skizziert. Davon ausgehend werden die FuE-Aktivitäten der IAEA vorgestellt sowie die wichtigsten Themen beim Extended Storage Collaboration Program (ESCP) in den USA. Schließlich wird das "European Joint Programme on Radioactive Waste Management and Disposal“ kurz vorgestellt und werden die nationalen Initiativen auf diesem Sektor diskutiert.
Elastomers show a high versatility which makes them ideal materials for sealing applications in various fields. Especially under changing application conditions the high recovery potential of this class of material is beneficial to compensate temperature or pressure fluctuation, and geometrical changes resulting from mechanical loads in e.g. accident conditions. Out of these reasons elastomers are also used in containers for low and intermediate level radioactive waste and for spent fuel transportation casks. In cask designed for low and intermediate level waste elastomer seals can act as primary seal responsible for the containment function whereas in spent fuel storage and transportation casks (dual purpose casks (DPC)) elastomer seals are used as auxiliary seals to allow leakage rate measurements of metal barrier seals. An inherent prerequisite for this kind of application is the long time-scale of operation without or with limited possibility of seal replacement. In Germany an interim storage license for DPC`s is typically issued for 40 years, a timeframe which might increase in future due to challenges of the final repository siting procedure. For low and intermediate level waste, also long time periods are required before final disposal can be achieved. Therefore, the performance of elastomer seals over extended time periods is, as for other applications, of high importance.
A typical approach to ensure long-term functionality is to perform accelerated aging tests to calculate an estimated lifetime by assuming e.g. Arrhenius like equations for the time-temperature relationship. This approach requires a suitable end of life criterion considering the application of interest. This often can represent a challenge on its own.
As BAM is involved in most of the cask licensing procedures and especially responsible for the evaluation of cask-related long-term safety issues we initiated several test programs for investigating the behavior of elastomer seals. Experiments concerning the low temperature performance down to -40°C and the influence of gamma irradiation have been started first. Currently the thermal aging behavior of elastomer seals, which is the topic of this contribution, is examined.
For our aging investigations we use a broad approach to first determine the property changes in different elastomer materials due to thermo-oxidative aging at elevated temperatures and secondly we test how the typical methods of lifetime extrapolation can be applied to these results. This approach enables us to detect and exclude undesired side effects which very often influence lifetime estimations. In this contribution, our recent results are discussed.
The Bundesanstalt für Materialforschung und –prüfung (BAM) runs an investigation program on the long-term behavior of multi-component metal seals. Such seals are used in a wide area of applications including transport and storage casks for spent nuclear fuel and high level radioactive waste. The seal function is mainly based on the compression of the inner helical spring, which generates the necessary seal force to keep the sealing surfaces in close contact. This in turn leads to a plastic deformation of the outer jacket of the seal, comprised of highly ductile aluminum or silver that adapts to the sealing surfaces of cask body and bolted lid, thus providing high level leak tightness. In Germany, those casks are licensed for interim storage periods of up to 40 years or more if extended interim storage would become necessary before a final repository is available. Thus, the sealing performance has to be evaluated, including factors like elevated temperature due to decay heat or mechanical loads due to transport under normal as well as accident conditions. Long-term investigations at BAM have been running over the last nine years to identify and evaluate the seal performance by measuring the remaining seal force, the useable resilience and the leakage rate after various time intervals at temperatures ranging from room temperature up to 150 °C. It was found that the seal force and useable resilience decrease with time and temperature, caused by creep deformation of the outer jacket. In order to obtain an analytical description for the seal behavior and to achieve more information on the material behavior under application conditions a comprehensive investigation program with focus on aluminum as outer jacket material was launched. The program includes material investigations such as compression and tension creep tests with representative basic materials. An additional test setup allows for the continuous measurement of the remaining seal force at temperatures of up to 150 °C. Furthermore, seal segments are compressed and stored in heating chambers, thus producing segments at different stages of the aging process. The segments are investigated regarding the development of the contact area width, jacket thickness and microstructural changes. This data will be used to develop material models and an analytical description of the time and temperature dependent long-term sealing behavior. This paper explains the current status of gained test results and modelling approaches and closes with an outlook to the future project plans.
Among other mechanical tests the 1 meter drop onto a steel puncture bar shall be considered for accident safe packages for the transport of radioactive material. According with the IAEA regulations “the bar shall be of solid mild steel of circular section, 15.0 ± 0.5 cm in diameter and 20 cm long, unless a longer bar would cause greater damage…”. The most damaging puncture bar length can be estimated by iterative processes in numerical simulations. On the one hand, a sufficient puncture bar length has to guarantee that shock absorbers or other attachments do not prevent or reduce the local load application to the package, on the other hand, a longer and thus less stiff bar causes a smaller maximum contact force. The contrary influence of increasing puncture bar length and increasing effective drop height shall be taken into account if a shock absorber is directly placed in the target area. The paper presents a numerical approach to identify the bar length that causes maximum damage to the package. Using the example of two typical package masses the sensitivity of contact forces and puncture bar deformations to the initial length are calculated and assessed with regard to the international IAEA package safety requirements.
Verbundvorhaben KoBrA: Ausblick zur Umsetzung von Anforderungen in Technische Behälterkonzepte
(2018)
Als Ausblick auf noch ausstehende Arbeiten zum Verbundvorhaben "KoBrA" zur Erfassung nationaler und internationaler Anforderungen und Konzepte für Behälter zur Endlagerung wärmeentwickelnder radioaktiver Abfälle in den potentiellen Wirtsgesteinformationen Kristallin, Ton und Salz werden die grundlegenden Anforderungen und Schutzziele der Endlagerbehälter untersucht und der konzeptionelle Weg von Anforderungen hin zu Konzepten erläutert.
Eine umfangreiche Darstellung der bisherigen Ergebnisse des ersten Arbeitspaketes im FuE-Vorhaben "KoBrA": Ziele und Anknüpfungspunkte des AP1; Ableitung von Kriterien und Kategorien; internationale Kernenergienutzung; Quellenbasis und Literaturrecherche; Selektion und Sortierung der Dokumentensammlung; Beispiele internationaler Endlagerprogramme
This presentation focusses on the thermal test of a typical storage container design for the German final storage repository KONRAD. The preparation of the container, the conduction of the fire test itself and results like the temperature evolution and as-sumptions for thermal material properties are shown.
As thermal test final storage containers have to be exposed to a fire of 800 °C (1472 °F) for 1 hour according to the final storage conditions provided by the federal com-pany for radioactive waste disposal (BGE). The here discussed cask contains a steel covered concrete layer of a thickness of 100/150 mm. Heating up concrete is a highly nonlinear process since the vaporization of residual water consumes high amounts of thermal energy and produce vast amounts of steam.
The constantly measured temperatures provide the basis to adjust common models of thermal properties for concrete esp. for FEAs. Finally in a later step this will allow predictions of similar designed container with different sizes.
der Vortrag stellt den aktuellen Bearbeitungsstand und Ergebnisse des laufenden Drittmittelvorhabens LaMEP vor. Hierbei geht es um Alterungsprozesse an sicherheitsrelevanten Behälterkomponenten während der langfristigen trockenen Zwischenlagerung bestrahlter Brennlemente und hochradioaktiver Abfälle. Die Untersuchungen umfassen Metall- und Elstomerdichtungen sowie Polymerkomponenten zur Neutronenabschirmung.
The presentation provides an overview about the understanding of fuel cladding failure mechanisms dominated by hydride embrittlement during long term dry storage. A currently launched research project focuses on the development of a fracture mechanics approach to describe brittle failure of fuel cladding during long term interim storage (BRUZL)“. Finally, the BAM contribution to the current European Joint Program (EJP) on radioactive waste management is illustrated.
Ongoing R&D work at BAM
(2018)
The presentation provides an update on the German nuclear waste management policy towards final disposal and related reasearch at BAM. Topics include long term investigations of metal seals, investigations of fuel cladding failure mechanisms, and the development of requirements and concepts for high level radioactive waste and spent fuel disposal containers.
Dichtungsverhalten bei niedrigen Temperaturen - Untersuchung der unteren Temperatureinsatzgrenze
(2018)
Elastomere werden vielfach in Produkten eingesetzt, die bei verschiedenen Temperaturen verwendet werden. Dabei sind O-Ringe kostengünstige Dichtelemente, die allerdings für die Funktionsfähigkeit und Sicherheit eines Produkts entscheidend sind. Die untere Temperatureinsatzgrenze ist dabei durchaus relevant und aus wissenschaftlicher Sicht nicht allgemeingültig zu definieren, da diese einerseits durch die Änderungen der Materialeigenschaften im Zuge des Gummi-Glas-Übergangs definiert werden, die Temperaturlage dieses Übergangs jedoch sehr stark von den jeweiligen Einsatzbedingungen (z.B. Frequenz) abhängt. Dadurch ergeben sich große Unterschiede zwischen statischen und dynamischen Anwendungen. Verschiedene Untersuchungen sollen vorgestellt und interpretiert werden, um das Auditorium auf verschiedene Herausforderungen aufmerksam zu machen und Lösungsansätze vorzustellen...
For many sealing applications rubbers are applied due to their special material properties and easy use. In many applications as e.g. in aviation, traffic or process technology the material can be exposed to low temperatures during operation. Therefore, it is important to know the material behaviour at those low temperatures to determine the temperature range that allows a safe operation of the seal.
In this work, we focus on the behaviour of elastomer seals at low temperatures with regard to potential decrease of leak-tightness or catastrophic seal failure of O-ring rubber seals. This is required as material properties of rubbers are strongly temperature dependent but their temperature application range is not always clearly defined.
Based on previous investigations which considered the physical material properties and the seal behaviour under purely static conditions we widen the focus on the sealing performance after a fast partial relief of compressed seals and additional materials.
For the investigations, different typical rubber seal materials were used as e.g. fluorocarbon (FKM), ethylene propylene diene (EPDM) and hydrogenated acrylonitrile-butadiene (HNBR) rubber.
The correlation of the physical material properties with seal performance is studied. This includes as well purely static sealing applications as the performance during/after fast partial relief of seals at low temperatures.
Component and material investigations on metal seals for high level radioactive waste containers
(2018)
In Germany casks for interim storage of spent nuclear fuel and high level radioactive waste are equipped with Helicoflex® metal seals as main sealing barrier of the double lid system. The long-term behaviour of those seals is investigated at Bundesanstalt für Materialforschung und –prüfung (BAM) in order to evaluate the safety function of the containment at different temperatures over storage periods of 40 years or more in case extended interim storage becomes necessary.
Long-term investigations have been done for ageing times of up to 8.5 years at temperatures ranging from room temperature to 150 °C. It was found that the seal force and useable resilience decrease over time, which is mainly caused by creep deformation of the aluminium (or silver) outer jacket of the seals. This effect becomes stronger with increasing temperature.
The ageing processes of the seal material and the overall seal behaviour is under investigation in order to derive analytical descriptions for the long-term seal performance. Thus, standardized tests on the basic seal materials, with focus on aluminium, and additional investigations on the seals as a component are conducted. The current investigations include compression and tension creep measurements as well as tensile testing. Furthermore, ageing of seal segments provides information on the development of the contact area width, jacket thickness and microstructural changes in dependence of time and temperature. The obtained data are used for the development of material models and an analytical approach to describe and predict the time and temperature dependent sealing behaviour in the long-term.
The paper focuses on the preliminary determination of the bar length and the experimental performance of the 1m-puncture test in compliance with the guidelines of the IAEA under the given boundary conditions. Following aspects have to be considered concerning the determination of an appropriate length of the bar to obtain maximum damage to the specimen: the design of the package, its drop orientation and the impact point as well as a pre-damage of the package resulting from a previous 9m drop test. According to the Regulations the minimum length of the bar is defined as 20 cm, which has to be adapted to the outer surface of the package, especially to packages with large impact limiters.
In this context, two main aspects are important: First, the realisation of a maximum puncture load applied to the package while no other component of the package has contact with the impact target. Second, the reduction of the risk of buckling and maximising the stiffness of the bar by a length which is as short as possible. In order to optimize the bar length, finite element calculations are often done by simulating the global behaviour of the package during the puncture test. The evaluation of the conducted puncture test regarding IAEA compliance is done by analysing deceleration measurements. The paper presents a possible approach to determine the length of the bar and the construction of a form-fitted connection to the target showing various examples of puncture tests.
Der Vortrag illustriert den Stand und die Herausforderungen im Rahmen der Behälter-Bauartprüfungen für das Endlager Konrad. Ausgehend von den Grundlagen der Bauartprüfung und die aktuelle Situation bei den Antragsverfahren werden die fachlichen Begutachtungsschwerpunkte sowie Maßnahmen zur Optimierung Prozess- und Verfahrenssteuerung erläutert.
This Presentation adresses the major needs and challenges of qualification processes for nuclear waste packages performed by BAM. Packages include those for high level radioactive waste like spent fuel as well as those for low and intermediate level waste to be disposed of in the Konrad repository.
Beginning with the current German nuclear waste management policy design testing capabilities and experience at BAM is explained followed by illustrating the major strategic process to identify future challenges including specific R&D needs.