3.2 Gefahrguttanks und Unfallmechanik
Filtern
Dokumenttyp
- Posterpräsentation (10) (entfernen)
Referierte Publikation
- nein (10)
Schlagworte
- LNG (3)
- LH2 (2)
- Polyethylene (2)
- Ageing (1)
- B10 exposure (1)
- Commodities (1)
- Damage (1)
- Degree of damage (1)
- Distributed acoustic sensing (1)
- Energy dissipation (1)
Organisationseinheit der BAM
- 3 Gefahrgutumschließungen; Energiespeicher (10)
- 3.2 Gefahrguttanks und Unfallmechanik (10)
- 6 Materialchemie (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.4 Prozessanalytik (1)
- 2 Prozess- und Anlagensicherheit (1)
- 2.1 Sicherheit von Energieträgern (1)
- 6.1 Oberflächen- und Dünnschichtanalyse (1)
- 6.7 Materialsynthese und Design (1)
- 8 Zerstörungsfreie Prüfung (1)
The monitoring of oil and gas pipelines by means of distributed fibre optic sensors is becoming common. The most recent development in the field of fibre optic sensing is the distributed acoustic sensing (DAS), which allows to detect and to localize third party threats to pipelines. For this purpose, fibre optic telecommunication cables located close to the pipelines are usually used. However, DAS carries a far greater potential for continuous condition monitoring of pipelines.
The interdisciplinary research project AGIFAMOR (Ageing Infrastructures – Fibre Optic Monitoring of Pipes) at BAM investigates a new technical approach to extend the application field of DAS towards the detection and localization of acoustic signals that indicate critical alterations and certain damage scenarios originated from within the pipeline or the pipe wall. Therefore, the optical fibre sensors are applied onto the pipe itself and the application procedure towards an optimal acoustic signal transduction is optimized.
A number of laboratory scale experiments were performed focusing on the signal transmission of acoustic signals as well as the detection of damage in the pipe wall by means of DAS. Furthermore, real-scale tests on a pipeline DN100 of 38 m length have been carried out at the BAM test site for technical safety (BAM-TTS) to study the detection and localization of leaks and of changing flow profiles due to corrosion or sedimentation processes.
Commodities and rail damage
(2018)
The normalized contact-mechanics fourth-power law approach for the
dynamic loads, suggest: worst railway use situation (double deck at 65 km/h) is 350 times that of the less rail damage situation (flat car at 45 km/h).
The normalized dispersion approach for the dynamic loads (Dynamic Load Coefficient), suggest that the worst railway use situation (double deck at 65 km/h) is about 4 times that of the less rail damage Situation (flat car at 45 km/h).
The potential effect of the different types of cars on the railway fatigue life could be significant, as a function of the vehicle speed.
The experimental validation of these outputs will be carried out as a continuation of this research effort. In addition to that, it should be mentioned that the associated simplified model could be used to analyze some other situations, related with the transport safety of different products.
Tanks for heating oil made of polyethylene grades have been on the market since the early 1970s in Germany. Tank manufacturers recommend the replacement of the tanks after a period of 30 years due to guarantee safety. Polyethylene grades are subject to ageing by alteration of the properties during their life cycle. The degree of ageing and the nature of the degradation process mainly depend on the chemical degradation of the polyethylene, the wall thickness of the tank and the environmental conditions. There are no results available on the long-term behavior of the polyethylene grades, especially after a service life of more than 30 years. The aim of this investigation was the determination of the factual degree of damage in comparison to the uncontaminated polyethylene grades. Material data of the used polyethylene grades are available because the BAM was the competent authority for the tests and expert reports for the approval of these tanks until the middle of the 1990s.
The determination of the Melt Flow Rate (MFR) and the Fourier Transmission IR Spectroscopy (FTIR) of tank sections from the bottom, the shell and the roof of 10 segregated heating oil storage tanks produced of polyethylene grades A and B were used as tests methods.
The MFR measurements of the tank sections showed differences in the values depending on the weight which was used (5 kg or 21.6 kg). A reduction of the MFR values was measured for most of the sections of tanks made of polyethylene grade B after a service life of the tanks of more than 30 years. This grade is mainly subject to the internal ageing by cross-linkages, increased degree of branched molecules and loss of the plasticizer, and to a lesser extent by oxidative degradation. The FTIR analysis, especially of tank sections of the bottom and the shell showed that the intensity of the CH2 asymmetric and symmetric stretching vibrations in the range: 2800 - 2900 cm-1 and the CH2 bending deformation vibration at 1400 cm-1 increased due chain scissions. The intensity of the carbonyl stretching vibration C=O at 1740 cm-1 is low. The carbonyl index characterizes the degree of oxidation.
Motivation:
- Reduktion der CO 2 Emissionen von Verbrennungsmotoren durch den Einsatz von LNG als alternativer Kraftstoff
- Aktuell werden doppelwandige Edelstahltanks mit Vakuumisolation für den Transport eingesetzt
- Reduktion des Tankgewichts und Vereinfachung der Konstruktion soll durch die Substitution mit GFK inklusive einer Isolationsschicht erreicht werden
- Leichtere Überprüfung von einwandigen Tankkonstruktionen
- Günstiges Versagensverhalten von GFK im Brandfall
Zusammenfassung:
- Thermische Performance kann mit Isolation aus PU Schaum erreicht werden
- Messung der Abdampfrate bildet einfache Möglichkeit zur Bestimmung der thermischen Performance
- Mikrorisse in der Matrix führen zur Leckage -> Liner notwendig
- Biegemodul bis 30 MPa vergleichbar, danach Abfall um ca. 50 % bei tiefen Temperaturen
Ausblick:
- Prüfung von GFK Proben mit Fasern in 0°-Orientierung
- Prüfung der thermischen Performance mit Demonstratoreinheiten verschiedene Größen
- Entwicklung einer Skalierungsfunktion, um Ergebnisse von druckloser Prüfung auf Druckanstieg zu übertragen
Heating oil storage tanks made of polyethylene grades have been on the market in Germany since the early 1970s. To ensure safety, their replacement is recommended by tank manufacturers after a period of 30 years. Polyethylene is subject to ageing by alteration of the properties during its life cycle. The degree of degradation and the nature of the process mainly depend on the chemical alteration of the polyethylene, the wall thickness of the tank and the environmental conditions. There are no data available on the long-term behaviour of the polyethylene grades, especially after a service life of more than 30 years.
The aim of this investigation was to find a suitable test method to determine the factual degree of damage in comparison to the uncontaminated polyethylene grades. Material data of the used polyethylene grades are available because the BAM was the competent authority for the tests and expert reports for the approval of these tanks until the middle of the 1990s. Therefore, tank sections from the bottom, the shell and the roof of 22 individual storage tanks produced of polyethylene grades A and B have been examined by Melt Flow Rate (MFR) and Attenuated Total Reflectance (ATR). Their service life was in the range between 20 and 41 years.
The MFR measurements of the tank sections showed differences in the values depending on the weight which was used (5 kg or 21.6 kg). An increase of the MFR was determined for the samples of polyethylene grade A, whereas a reduction of the MFR values was measured for most samples of polyethylene grade B. This grade is mainly subject to the internal ageing by cross-linkages, increased degree of branched molecules and loss of the plasticizer.
ATR analysis exhibits an absorption band at 909 cm‒1 predominantly in samples of polyethylene grade A indicating chain scission and concomitantly formed terminal vinyl groups. This absorption band can be used for the characterization of the ageing of the polyethylene grades.
The volumetric energy density of a gas can be increased by liquefaction, which occurs when the gas is cooled below the saturation point. Liquefied gases of great importance to the energy transition are Liquefied Hydrogen (LH2) and Liquefied Natural Gas (LNG), which can be liquefied at temperatures below 160°C. Systems for storing these gases typically must be overpressure resistant and require thermal super insulations (TSI) to hold cryogenic conditions and minimize boil-off losses from evaporation. TSI with vacuum and MLI or perlites are suitable for many applications involving LNG and LH2. Such systems are typically double-walled structures where the inner wall is in contact with the cryogenic liquefied gas. MLI or perlites are located in the gap between the inner and the outer wall, that is kept under vacuum conditions. This combination of insulations strongly reduces the heat transfer between the environment and the cryogenic liquefied gas. From an economic point of view the systems are well sophisticated. However, knowledge of the behavior of this kind of systems in a typical event such as a fire is limited, but necessary to evaluate the safety of the increasing number of applications.
The objective of the research is to determine how TSI behaves at different fire temperatures during fire exposure and afterwards. Special attention is paid to changes in the heat flux, the material properties and vacuum state over time. For this purpose, thermogravimetric analysis (TGA) studies have been carried out. In addition, a test rig was developed that allows testing of TSI at temperatures up to 1000°C under realistic integration conditions and subsequent analysis of the TSI samples. In the test rig the double-wall with vacuum and MLI or perlites inside is simulated. The fire conditions are simulated on one side of the double-wall by adjustable electrical heating elements. This process allows the implementation of repeatable heat flows of up to 100 kW/m². On the other side of the double-wall, cold or cryogenic conditions are simulated with a heat exchanger through which water or the vapor of liquid nitrogen (approx. -196°C) flows. The heat exchanger is also used to determine the heat flux through the double-wall. Thus, the test rig allows thermal loading and performance analysis of TSI samples at the same time.
Compared to tests with real cryogenic systems, tests with this experimental setup have the advantage that, first, the instrumentation is easier to realize, and a higher repeatability is ensured. Second, the local heat flow can be determined over time, and the sample of a TSI can be taken non-destructively and thus analyzed. Third, the tests are less risky as well as time+ and material intensive, so that more tests and variants can be investigated with the same budget.
Preliminary results obtained considering several types of MLI under vacuum show that all observed typs of MLI can be damaged under strong thermal loading. The damages observed were outgassing, melting, shrinkage, cracking, lump formation, and concomitant local loss of the MLI's function as a radiation shield. However, the study also shows that a damage does not always have an extreme effect on the insulating performance.
Turning maneuvers of rail vehicles involve demanding situations for the infrastructure because of the steering forces generated and the resultant lateral load transfers. Such forcing situation involves increased tangential forces that consume kinetic energy from the vehicle. While much attention has been paid in the literature to the damage in such infrastructure segments, the energy that is dissipated in these maneuvers, has not been explicitly addressed. In this paper, a specialized scale-down infrastructure is used to characterize the effect of the initial speed of the vehicle and its mass, on the magnitude of both the rail forces developed and the amount of dissipated energy during turning maneuvers. The outputs of the experiments suggest that most of the original kinetic energy is dissipated at the first portion of the turn. Also, that the magnitude of the wheel forces and the amount of dissipated energy, correlate. That is, a greater rail damage would correspond to greater energy dissipation.
Liquefied Hydrogen (LH2) or Liquefied Natural Gas (LNG)
establish themselves as important energy carriers in the transport
sector. Its storage requires tanks with Thermal Super Insulations
(TSI) to keep the transported fluid cold. TSI has proven itself in
various applications over a long time, but not in the land
transport sector, where accidents involving collisions, fires, and
their combination are to be expected. The focus of this study is
to investigate the behavior of different types of TSI when
exposed to a heat source that represents a fire. Therefore, a High-
Temperature Thermal Vacuum Chamber (HTTVC) was used that
allows the thermal loading of thermal insulation material in a
vacuum and measuring the heat flow through the TSI in parallel.
Within this study, 5 samples were tested regarding 3 different
types of MLI, rock wool, and perlites. The thermal exposure
caused different effects on the samples. In practice, this can be
connected to the rapid release of flammable gases as well as a
Boiling Liquid Expanding Vapour Explosion (BLEVE). These
results are relevant for the evaluation of accident scenarios, the
improvement of TSI, and the development of emergency
measures.
Biofuels, particularly biodiesel, have gained significant attention as an alternative to traditional fossil fuels in recent years. Unlike diesel, which contains hundreds of compounds, biodiesel only contains a few compounds in the C16-C18 carbon chain. However, the use of biodiesel in automobile and transportation applications can result in problems of degradation or even damage in materials. Among the commonly used polymer materials, fluorocarbon (FKM) shows excellent performance and high stability and compatibility towards oil, diesel, ethanol, and other chemicals. FKM is a family of fluorocarbon-based fluoroelastomer materials, which provide excellent high-temperature and chemical stability compared to other elastomers. As a result, FKM is widely used in chemical processes such as petroleum refining, where it is used for sealings, pumps, and other components.