Formgedächtnispolymere werden durch thermomechanische Vorbehandlung, die Programmierung, in eine temporäre Form überführt. In die Ursprungsform kehren sie dann erst nach externer Stimulierung, durch Auslösen des Formgedächtniseffekts, wieder zurück. Um diesen Effekt zu optimieren, werden in dieser Arbeit thermomechanische Designoptionen analysiert und Stellschrauben der Programmierung diskutiert. Quantifiziert wird das Materialverhalten eines physikalisch vernetzten Polyurethans mit semikristalliner Polyester-Weichsegmentphase (PEU) in thermomechanischen Messungen, in denen das Polymer Dehnungen bis über 1000% fixiert.
Deformationen im breiten Schmelzübergangsbereich der Weichsegmentphase ermöglichen die präzise Kontrolle über die Temperaturen der Dehnungs- und Spannungsrückstellung, den bekannten Temperaturgedächtniseffekt (TGE). Erst durch eine neuartige Programmierung wird jedoch der Beginn der Rückstellung einstellbar. Für diesen Onset-TGE wird das PEU direkt nach dem Recken entlastet und danach unter die Kristallisationstemperatur abgekühlt. In situ Röntgenstreuung zeigt, dass durch den frühen Entlastungszeitpunkt nur der Teil der kristallinen Weichsegmentphase zur Fixierung beiträgt, der auch beim Recken kristallin ist. Die Kristallinität bietet daher eine Stellschraube, um das thermomechanische Verhalten zu veredeln. Über die Optimierungsparameter Reckrate, Temperaturhaltezeit und maximale Dehnung erzielt das PEU hohe Fixierbarkeiten und Rückstellspannungen, ohne die Rückstellung und den Onset-TGE zu beeinträchtigen. Durch die Erweiterung der Programmierung des Onset-TGEs hin zu einer zweiten Deformation und Entlastung innerhalb des Schmelzübergangs zeigt das PEU einen bisher nicht berichteten zweistufigen Spannungsanstieg während der Rückstellung. Ein Temperaturlimit für den Onset-TGE stellt die Peak-Schmelztemperatur aus der dynamischen Differenzkalorimetrie dar. Durch die verbleibende Kristallinität oberhalb dieser Temperatur führt die Deformation und Entlastung direkt zur thermoreversiblen Aktuation mit Dehnungsänderungen bis zu 28%.
Die Ergebnisse werden auf einen Miniaturisierungsansatz für schaltbare Informationsträger übertragen, mit denen eine maschinenlesbare Information von nichtlesbar nach lesbar geschaltet werden kann. In einer Machbarkeitsstudie wird der für Sensoranwendungen vielversprechende Onset-TGE genutzt, um die Lesbarkeit der Informationsträger bei einer vordefinierten Temperatur zu schalten. Das erweitert das potentielle Anwendungsfeld der Technologie vom Produkt- und Markenschutz zur Überwachung von Kühlketten.
The aim of this thesis was the development of switchable information carriers based on shape memory polymers (SMPs) and the investigation of their durability. Deployed as a new kind of security label, such technology may be an effective tool to prevent counterfeiting and product piracy.
Thermoplastic as well as thermoset SMPs turned out to be applicable as a specific substrate for the fabrication of switchable information carriers. In particular, a physically cross-linked and semi-crystalline poly(ester urethane) (PEU), and a chemically cross-linked epoxy-based polymer were investigated. Both SMPs were able to undergo distinct changes in shape upon triggering, which is commonly known as the shape memory effect (SME).
A key step for the fabrication of switchable information carriers was the development of a suitable technique for a surface-specific coloring of the polymeric base material. In particular, it was necessary to have a thin coat of paint in order to assure sufficient surface contrasts within the subsequently laser-engraved barcodes (e.g. quick response (QR) codes). In detail, coloring was conducted by diffusion of staining solutions, based on organic dyes, into the polymeric matrix. As a result of properly selected exposure times, homogenous layers of paint having thicknesses of about 100 μm, could be produced.
In order to obtain room temperature stable, temporary shapes with non-decipherable code information, various programming procedures were applied to the information carriers. These were either based on tensile or on compressive deformation. For instance, when using plane steel plates in the course of compressive deformation, code areas were randomly distorted. By contrast, selective distortions could be achieved using a steel ball type indenter. However, the triggering of the SME resulted in almost complete shape recoveries. As a result, the information carriers could reliably be switched back to readable states.
Before the developed information carriers can be brought onto the market, it is important to evaluate their durability against various environmental impacts. Artificial weathering was conducted exemplarily on blue and black colored QR code carriers based on PEU. Various scenarios were selected: exposure to UVA irradiation and aging in aqueous solution. In both cases, the durability was investigated at temperatures below and above the switching temperature of the employed SMP. It turned out, that the limiting factor for the usage of switchable information carriers was a lack of contrast and thus was dye-related. In the case of UV irradiation, the color of the dyes started fading, culminating in unreadable QR codes. For hydrolytic degradation, the non-colored code regions were stained in the course of aging. This originates from the fact that the organic dyes used for coloring were soluble in water. As a consequence, they were able to diffuse easily in and out of the swollen polymeric matrix. For both scenarios, aging at elevated temperature caused acceleration of the observed effects. However, the shape memory properties of the PEU were only slightly influenced by the applied aging scenarios.
Next, an additional thermo-responsive security feature was added to the information carriers. Therefore, thermochromic pigments (T-PIGs) were embedded into a PEU matrix. However, in contrast to the organic dyes, the size of the thermochromics microcapsules was too large to diffuse into the polymeric matrix. Thus, another procedure for a surface-specific coloring of the PEU was developed. This mainly included the preparation of a PEU-paste doped with T-PIG by solution mixing. The thermochromic paste was deposited by means of a solvent casting technique as thin layer atop the PEU plaque. After solvent evaporation, tightly connected PEU/PEU-T-PIG laminates were obtained. Beyond that, the layer thickness was adjustable by using a doctor blade for the paste deposition. Subsequent laser ablation finalized the QR code carriers. These were readable at room temperature, but unreadable above the color switching temperature of the employed T-PIGs due to a lack of contrast. Hence, the obtained multifunctional information carriers were characterized by distinct shape memory properties and tunable color switching performances. Furthermore, the combination of several T-PIGs having different colors and switching temperatures resulted in surfaces with multiple and unique temperature-dependent changes in color. Besides that, information carriers with temporarily concealed information could be obtained by covering the QR code with an additional layer doped with T-PIG.