The appropriate strength of steels used for saline aquifer carbon capture and storage sites (CCS) is usually achieved by applying heat treatments. Thus, heat treatment influences the corrosion resistance for injection pipe steels with 13% chromium and different carbon content: 1.4034/X46Cr13 and 1.4021/X20Cr13 in CO2 saturated saline aquifer water at 60 °C, 1 and 100 bar. X46Cr13 shows better corrosion resistance with respect to corrosion rate, number of pits and maximum intrusion depth. Low corrosion rates are obtained for steels with martensitic microstructures exposed to supercritical CO2 at 100 bar, whereas normalized steels show better corrosion resistance at ambient pressure.
To resist the corrosive geothermal environment during carbon capture and storage CCS -such as: heat, pressure, salinity of the aquifer, CO2-partial pressure, properties of pipe steels-require certain specification. For evaluation samples of differently heat treated high alloyed stainless injection-pipe steels AISI 420 X46Cr13, AISI 420J X20Cr13 as well as X5CrNiCuNb16–4 AISI 630 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h up to 8000 h in a CO2-saturated synthetic aquifer environment similar to a possible geological situation in the northern German Basin. Corrosion rates and scale growth are lowest after long term exposure for steels hardened and tempered at 600 °C to 670 °C and pits -indicating local corrosion- decrease in diameter but increase in number as a function of carbon content of the steel. Martensitic microstructure is preferred with respect to these particular conditions.