Particle size gradation is regarded as an effective method for overcoming the contradicting requirements in three-dimensional printing (3DP). In present work, particle size gradation was optimized to obtain both acceptable flowability of the powder material and high-strength 3D-printed glass-ceramic products. The effect of gradation on the printing process, sintering process and performance of the 3D-printed glass-ceramic products was investigated comprehensively. The glass-ceramic powders with three size ranges were mixed in certain proportions and applied to print parts. The result showed parts printed with powder mixed by 60 wt% 45–100 µm and 40 wt% 0–25 µm particles had satisfactory density of 1.60 g/cm³ and bending strength of 13.8 MPa. The flowability decreased with an increasing proportion of fine particles. Part density was determined by the powder bulk density in the powder bed as well as the shrinkage during sintering while strength of part was found to be dependent on the sintering degree.
The quantitative nanomechanical characterization of soft materials using the nanoindentation technique requires further improvements in the performances of instruments, including their force Resolution in particular. A micro-machined silicon nanoforce transducer based upon electrostatic comb drives featuring the force and depth resolutions down to 1 nN and 0.2 nm, respectively, is described.
At the end of theMEMStransducer’s main shaft, a pyramidal tip is fabricated using a focused ion beam facility. A proof-of-principle setup with this MEMS nanoindenter has been established to measure the mechanical properties of soft polydimethylsiloxane. First measurement results demonstrate that the prototype measurement system is able to quantitatively characterize soft materials with elastic moduli down to a few MPa.
The magneto-mechanical memory (MMM) method, that is often referred to as the metal magnetic memory method, has been reported to be a non-destructive testing technique capable of quantifying stress concentrations and detecting defects in ferromagnetic materials. The underlying mechanism behind MMM has been explained in the literature, but the sensitivity to stress concentration has not been satisfactorily investigated. In this paper, both the normal and tangential components of the stress-induced MMM signal were measured by permanently installed magnetic sensor arrays on specimens made from three grades of L80 alloy steel and 20 other structural steels; tests were also carried out on a pipe made from the 4140-L80 steel. As expected, the stress history affects the MMM signal, but the experimental results show that significant irreversible change of magnetization always occurs only in the first cycle of loading regardless whether the deformation is purely elastic or partially plastic. If the peak stress level is increased at a given point during cycling, the immediately following next cycle acts as a new “first” cycle at that peak stress level and causes additional significant irreversible change of magnetization, but there is no evidence that plastic deformation might build up a cumulative magnetization. The MMM effect is very small in the steel samples tested, indicating that it will not be useful in field applications. In un-notched specimens the irreversible change in magnetization caused a proportional change in the measured external magnetic field on the order of only 5–10 A/m, while in the case of notched specimens the leakage field was on the order of 30–60 A/m.
A mono-component intumescent flame retardant named ethylenediamine-modified ammonium polyphosphate (MAPP) is used in polyethylene-octene elastomer (POE). Insight into the flame-retardant mechanisms of the MAPP is provided from a new perspective. The fire performance of POE/MAPP composites is investigated by oxygen index (OI) and vertical burning (UL-94) tests. POE Composite containing 35 wt% MAPP achieves a V-0 rating, and its OI is 29.3 vol%. The thermogravimetric Analysis (TGA) and Fourier transform infrared spectra (FTIR) confirm that the incorporation of ethylenediamine changes the thermal decomposition of APP, mainly resulting in the formation of char layer with a thermally stable structure. Cone calorimeter analysis revealed the flame-retardant modes of action of MAPP in POE under forced-flaming conditions. Quantitative analysis illustrates that both the residue due to charring and the fuel dilution/flame Inhibition resulting from the release of incombustible products/ phosphorus species decrease the total heat release (fire load) by 20e28%. The residue increases linearly with increasing MAPP content, whereas the reduction in effective heat of combustion levels off. Moreover, the flame-retardant effect resulting from the protective properties of the char is discovered to be the dominant mode of action (up to 85% reduction) with respect to the peak heat release rate, leading to the excellent flame retardancy of POE/MAPP.