The feasibility of microbial hydrogen consumption to mitigate the hydrogen embrittlement (HE) under different cathodic potentials was evaluated using the Devanathan-Stachurski electrochemical test and the hydrogen permeation efficiency h. The hydrogen permeation efficiency h in the presence of strain GA-1 was lower than that in sterile medium. The cathodic potential inhibited the adherence of strain GA-1 to AISI 4135 steel surface, thereby reducing the hydrogen consumption of strain GA-1. The adherent GA-1 cells were capable of consuming ‘cathodic hydrogen’ and reducing the proportions of absorbed hydrogen, indicating that it is theoretically possible to control HE by hydrogen-consuming microbes.
The hydrogen permeation current increase was noticed for carbon steel in 0.5 mol/L NaCl solution under strong anodic potentials, which is contrary to the common understanding. Hydrogen permeation under cathodic potentials has been widely studied because of possible hydrogen embrittlement failures of high strength steels in seawater, but investigations of anodic polarization on hydrogen permeation are fairly rare, as the hydrogen evolution reaction shall be retarded. To corroborate the observed phenomenon, experiments were conducted using both as-received and vacuum-annealed sheet specimens. It was verified that the observed phenomena originated from the released hydrogen in traps by metal dissolution under anodic polarization.
The influence of interfacial pH between AISI 4135 steel and seawater under different polarization potentials on the formation of calcareous deposits has been studied. An interfacial pH of 9.61 at −0.9 V vs. SCE using state of the art iridium oxide microelectrode was found to be the critical pH for the precipitation of magnesium hydroxide. Calcareous deposits with a double-layer structure comprising an inner-brucite layer and an outer-aragonite layer were found to form at potentials between −1.0 V and −1.2 V vs. SCE. Furthermore, the facilitation of hydrogen permeation into steel induced by the formation of calcareous deposits was verified using the Devanathan-Stachurski electrochemical test. The mechanism of calcareous deposits facilitates hydrogen permeation into steel is related to its inhibition on hydrogen recombination and escape processes.