Broadband dielectric spectroscopy (BDS), capacitive scanning dilatometry (CSD) and differential ac-chip calorimetry (DACC) were used to examine the glass transition and segmental dynamics of ultrathin poly(bisphenol A carbonate) (PBAC) films. An increase of Vogel temperature (T0) as well as glass transition temperature (Tg) with decreasing film thickness was observed when the thickness is less than 20 nm. Moreover, the segmental relaxation time at a fixed temperature was found to increase for the aluminium (Al) capped PBAC films (<20 nm) in the BDS measurements, whereas in the DACC measurements no thickness dependency of the segmental dynamics was detected within the experimental error limit for the supported PBAC films (10-55 nm). These properties are discussed in terms of the thin film geometry and the relevant interfacial interaction between the polymer and the substrate.
Specific heat spectroscopy in the frequency range from 1 Hz to 10³ Hz with a sensitivity of pJ K-1 was employed to study the glass transition behavior of ultrathin poly(bisphenol A carbonate) (PBAC) films with thicknesses ranging from 192 nm down to 10 nm. The amplitude and the phase angle of the complex differential voltage as a measure of the complex heat capacity were obtained as a function of temperature at a given frequency simultaneously. Both spectra are used to determine the dynamic glass transition temperature as a function of both the frequency and the film thickness. As the main result no thickness dependence of the dynamic glass transition temperature was observed down to a film thickness of 10 nm within the experimental uncertainty of ±3 K. The obtained data were compared with literature results in detail.
The molecular dynamics of the discotic liquid crystal pyrene-1,3,6,8-tetracarboxylic tetra(2-ethylhexyl)ester is studied by dielectric relaxation and specific heat spectroscopy. Dielectric spectroscopy shows 3 processes: a β-relaxation at low temperatures and an α-relaxation in the temperature range of the mesophases followed by conductivity. The dielectric α-relaxation is assigned to a restricted glassy dynamics in the plastic crystal as well as in the liquid crystalline phase. The obtained different Vogel–Fulcher–Tammann laws (different Vogel temperatures and fragility) are related to the different restrictions of the dipolar fluctuations in the corresponding phases. By means of specific heat spectroscopy glassy dynamics is also detected in the plastic crystalline phase but with quite a different temperature dependence of the relaxation times. This is discussed considering the different probes involved and how they are influenced by the structure. In the frame of the fluctuation approach a correlation length of glassy dynamics is calculated to 0.78 nm which corresponds to the core–core distance estimated by X-ray scattering.
Glass transition behavior of thin poly(bisphenol A carbonate) (PBAC) films capped between two aluminum (Al) layers is investigated by means of dielectric expansion dilatometry and dielectric relaxation spectroscopy accompanied by contact angle measurements. The thermal glass transition temperature is more or less independent of the film thickness down to 20 nm. For thickness below 20 nm, an increase of Tg is observed. Meanwhile, an increase of the relaxation time at a fixed temperature is observed for the film with the thickness of 19 nm on the basis of a careful analysis of the temperature dependence of the relaxation rates. A more detailed analysis of the relaxation map reveals that the Vogel temperature increases and the fragility decreases systematically with decreasing film thickness. These properties are discussed in terms of the formation of a boundary layer with PBAC segments adsorbed onto the Al electrode due to the strong interaction between the Al and PBAC layers (2.51 mJ/m²), which results in a reduced molecular mobility with regard to bulk PBAC behavior. As the dielectric strength is proportional to the number of segments fluctuating on the time and length scale of the dynamic glass transition, it is used as a unique probe of the deviations from bulk behavior. The temperature dependence of the penetration depth of the interfacial interactions on the structural relaxation is further quantitatively determined. The dynamic length scale of the perturbations into the chain conformations responsible for the deviation from bulk behavior is estimated to be smaller than 9 nm.
We investigate the segmental dynamics and glass transition temperature (Tg) of polystyrene (PS) thin films. The former is investigated by alternating current (AC) calorimetry and dielectric spectroscopy (BDS). The Tg, underlying the equilibrium to out-of-equilibrium crossover from the supercooled liquid to the glass, is obtained by differential scanning calorimetry (DSC) and capacitive dilatometry (CD). We show that the intrinsic molecular dynamics of PS are independent of the film thickness both for the freestanding and supported films, whereas Tg decreases with film thickness from several microns down to 15 nm. This result is found for complementary methods and in a simultaneous measurement in BDS and CD. This questions the widespread notion that segmental mobility and the equilibrium to out-of-equilibrium transition are, under any experimental conditions, fully interrelated. For thin films, it appears that the molecular mobility and Tg are affected differently by geometrical factors.