Polymeric membranes represent a cost- and energy efficient solution for gas separation. Recently superglassy polymers with high free volume outperform many conventional dense polymers in terms of gas permeability and selectivity. However, such materials with a high fractional free volume (FFV) are prone to pronounced physical aging. The initial microporous structures approach a denser state via local chain rearrangements which results in a dramatic reduction in the gas permeability. For the first time, dielectric spectroscopy with state-of-the-art high-resolution analyzers was employed to investigate the molecular mobility and physical aging of two representative groups of superglassy polymers: PIMs (PIM-1 & PIM-EA-TB) and Si-containing polynobornenes (PTCNSi1 & PTCNSi2). The dielectric behavior of the solution-cast polymeric films was measured by isothermal frequency scans during the different heating cycles in a broad temperature range. Structural relaxation of the films was observed during the measurements. Multiple dielectric processes following Arrhenius behavior were observed for all the investigated polymers. Moreover, they all showed conductivity in the glassy state. The significant increase in the conductivity with increasing temperature especially for PIMs is explained in terms of the formation of local intermolecular agglomerated structures due to interaction of π-electrons in aromatic moieties of the polymer backbone.
Thermal and dynamic glass transition of ultrathin films of homopolymers and a miscible polymer blend
(2017)
Despite the decade long controversial discussion on the effect of nanometer confinement on the glass transition temperature (Tg) of ultrathin polymer films, there is still no consistent picture. Here, the dynamic calorimetric glass transition of ultrathin films of a blend, which is miscible in the bulk, is directly investigated by specific heat spectroscopy. By a self-assembling process, a nanometer thick surface layer with a higher molecular mobility is formed at the polymer/air interface. By measuring the dynamic calorimetric Tg in dependence on the film thickness, it was shown that the Tg of the whole film was strongly influenced by that nanometer thick surface layer, with a lower Tg. Since the observed thickness dependence of the dynamic Tg is similar to the thickness dependence of the Tg for thin films of homopolymers, it is concluded that also for homopolymer a highly mobile surface layer is relevant for the widely observed Tg depression.