Broadband dielectric spectroscopy (BDS), specific heat spectroscopy (HCS) and capacitive scanning dilatometry (CSD) are used to study the glass transition and segmental dynamics in thin supported polystyrene (PS) films. Different molecular weights (Mw = 50 kg/mol, Mw = 260 kg/mol, Mw = 1408 kg/mol) and annealing protocols are employed in the study. The segmental dynamics is independent of the film thickness for each Mw in the temperature window of the dielectric measurement. The thermal glass transition temperature, Tg, measured by CSD depends on the film thickness and shows also a dependence on Mw. These observations are explained in terms of the formation of irreversibly adsorbed layer due to chain adsorption on the Al substrates during annealing.
Broadband dielectric spectroscopy (BDS), capacitive scanning dilatometry (CSD) and differential ac-chip calorimetry (DACC) were used to examine the glass transition and segmental dynamics of ultrathin poly(bisphenol A carbonate) (PBAC) films. An increase of Vogel temperature (T0) as well as glass transition temperature (Tg) with decreasing film thickness was observed when the thickness is less than 20 nm. Moreover, the segmental relaxation time at a fixed temperature was found to increase for the aluminium (Al) capped PBAC films (<20 nm) in the BDS measurements, whereas in the DACC measurements no thickness dependency of the segmental dynamics was detected within the experimental error limit for the supported PBAC films (10-55 nm). These properties are discussed in terms of the thin film geometry and the relevant interfacial interaction between the polymer and the substrate.
Specific heat spectroscopy in the frequency range from 1 Hz to 10³ Hz with a sensitivity of pJ K-1 was employed to study the glass transition behavior of ultrathin poly(bisphenol A carbonate) (PBAC) films with thicknesses ranging from 192 nm down to 10 nm. The amplitude and the phase angle of the complex differential voltage as a measure of the complex heat capacity were obtained as a function of temperature at a given frequency simultaneously. Both spectra are used to determine the dynamic glass transition temperature as a function of both the frequency and the film thickness. As the main result no thickness dependence of the dynamic glass transition temperature was observed down to a film thickness of 10 nm within the experimental uncertainty of ±3 K. The obtained data were compared with literature results in detail.
Specific heat spectroscopy in the frequency range typically from 1 Hz to 1 kHz with a sensitivity of pJ/K was employed to study the glass transition behavior of ultrathin poly(vinyl methyl ether) (PVME) films with thicknesses ranging from 218 nm down to 12 nm. The amplitude and the phase angle of the complex differential voltage as a measure of the complex heat capacity were obtained as a function of temperature at a given frequency simultaneously. Both spectra are used to determine the dynamic glass transition temperature as a function of both the frequency and the film thickness. As main result no thickness dependence of the dynamic glass transition temperature was observed down to a film thickness of 12 nm within the experimental uncertainty of ±2 K. Further the width of the glass transition is independent of the film thickness which indicates that the extent of the cooperativity is essentially smaller than 12 nm.
The molecular dynamics of the discotic liquid crystal pyrene-1,3,6,8-tetracarboxylic tetra(2-ethylhexyl)ester is studied by dielectric relaxation and specific heat spectroscopy. Dielectric spectroscopy shows 3 processes: a β-relaxation at low temperatures and an α-relaxation in the temperature range of the mesophases followed by conductivity. The dielectric α-relaxation is assigned to a restricted glassy dynamics in the plastic crystal as well as in the liquid crystalline phase. The obtained different Vogel–Fulcher–Tammann laws (different Vogel temperatures and fragility) are related to the different restrictions of the dipolar fluctuations in the corresponding phases. By means of specific heat spectroscopy glassy dynamics is also detected in the plastic crystalline phase but with quite a different temperature dependence of the relaxation times. This is discussed considering the different probes involved and how they are influenced by the structure. In the frame of the fluctuation approach a correlation length of glassy dynamics is calculated to 0.78 nm which corresponds to the core–core distance estimated by X-ray scattering.
Glass transition behavior of thin poly(bisphenol A carbonate) (PBAC) films capped between two aluminum (Al) layers is investigated by means of dielectric expansion dilatometry and dielectric relaxation spectroscopy accompanied by contact angle measurements. The thermal glass transition temperature is more or less independent of the film thickness down to 20 nm. For thickness below 20 nm, an increase of Tg is observed. Meanwhile, an increase of the relaxation time at a fixed temperature is observed for the film with the thickness of 19 nm on the basis of a careful analysis of the temperature dependence of the relaxation rates. A more detailed analysis of the relaxation map reveals that the Vogel temperature increases and the fragility decreases systematically with decreasing film thickness. These properties are discussed in terms of the formation of a boundary layer with PBAC segments adsorbed onto the Al electrode due to the strong interaction between the Al and PBAC layers (2.51 mJ/m²), which results in a reduced molecular mobility with regard to bulk PBAC behavior. As the dielectric strength is proportional to the number of segments fluctuating on the time and length scale of the dynamic glass transition, it is used as a unique probe of the deviations from bulk behavior. The temperature dependence of the penetration depth of the interfacial interactions on the structural relaxation is further quantitatively determined. The dynamic length scale of the perturbations into the chain conformations responsible for the deviation from bulk behavior is estimated to be smaller than 9 nm.
We investigate the segmental dynamics and glass transition temperature (Tg) of polystyrene (PS) thin films. The former is investigated by alternating current (AC) calorimetry and dielectric spectroscopy (BDS). The Tg, underlying the equilibrium to out-of-equilibrium crossover from the supercooled liquid to the glass, is obtained by differential scanning calorimetry (DSC) and capacitive dilatometry (CD). We show that the intrinsic molecular dynamics of PS are independent of the film thickness both for the freestanding and supported films, whereas Tg decreases with film thickness from several microns down to 15 nm. This result is found for complementary methods and in a simultaneous measurement in BDS and CD. This questions the widespread notion that segmental mobility and the equilibrium to out-of-equilibrium transition are, under any experimental conditions, fully interrelated. For thin films, it appears that the molecular mobility and Tg are affected differently by geometrical factors.
Polymers of intrinsic microporosity (PIMs) are promising candidates for the active layer in gas separation membranes due to their high permeability and reasonable permselectivity. These appealing properties originate from a microporous structure as a result of inefficient segment packing in the condensed state due to a combination of a ladder-like rigid backbone and sites of contortion. However, this class of polymers suffers from a significant decrease in the permeability with time due to physical aging, whereby typically, the permselectivity increases. The initial microporous structures approach a denser state via local rearrangements, leading to the reduction of the permeability. Hence, a detailed characterization of the molecular mobility in such materials can provide valuable information on physical aging. In this work, the dielectric behavior of PIM-1 films and their behavior upon heating (aging) were revisited by isothermal frequency scans during different heating/cooling cycles over a broad temperature range between 133 and 523 K (−140 to 250 °C). In addition, the obtained results were compared with data of samples that were annealed at ambient temperatures over different time scales. Multiple dielectric processes were observed: several relaxation processes due to local fluctuations and a Maxwell−Wagner−Sillars polarization effect related to the microporosity. The temperature dependence of the rates of all processes follows the Arrhenius law where the estimated activation energy depends on the nature of the process. The influence of the thermal history (aging) on the processes is discussed in detail.
In this chapter broadband dielectric spectroscopy (BDS) is employed to polymeric blend systems. In its modern form BDS can cover an extraordinary broad frequency range from 10-4 to 1012 Hz. Therefore, molecular and collective dipolar fluctuations, charge transport, and polarization effects at inner phase boundaries can be investigated in detail including its temperature dependence. In the first part of the chapter, the theoretical basics of dielectric spectroscopy are briefly introduced covering both static and dynamic aspects. This section is followed by short description of the various experimental techniques to cover this broad frequency range. To provide the knowledge to understand the dielectric behavior of polymeric blend systems, the dielectric features of amorphous homopolymers are discussed in some detail. This concerns an introduction of the most important relaxation processes observed for these polymers (localized fluctuations, segmental dynamics related to the dynamic glass transition, chain relaxation), a brief introduction to the conductivity of disordered systems as well as polarization effects at phase boundaries. Theoretical models for each process are shortly discussed. In the last paragraph the dielectric behavior of polymer blends is reviewed where special attention is paid to binary systems for the sake of simplicity. In detail the dielectric behavior of binary miscible blends is described. The two most important experimental facts like the broadening of the dielectric relaxation spectra and the dynamic heterogeneity of the segmental dynamics are addressed in depth. Appropriate theoretical approaches like the temperature-driven concentration fluctuation model and the self-concentration idea are introduced.
The glass transition behavior of ultra-thin supported polymer films is discussed controversially in the literature for around 20 years. Substantial efforts have been archived to understand it. In this contribution, a combination of methods sensitive to bulk properties of a system, like dielectric or specific heat spectroscopy with surface analytics, for instance, atomic force microscopy (AFM), contact angle measurements, and X-ray photoelectron spectroscopy (XPS) were employed to study the glass transition of ultra-thin supported films. All investigations were carried out on identically prepared and treated samples. Different systems with different complexities going from more or less flexible homopolymers over rigid main chain macromolecules to polymer blends have been studied. For the investigated flexible macromolecules, the dynamic glass transition temperature estimated within the frame of the linear response approach is independent of the film thickness down to several nanometers and identical to the bulk value. For polystyrene it was found the thermal glass transition temperatures can depend on the film thickness. This different behavior is not well understood till now and needs further experimental clarification. For the investigated main chain polymers polycarbonate and polysulfone. Dynamic and thermal glass transition temperature estimated from the dielectric measurements increases with decreasing film thickness. This is discussed in the frame of a strong interaction of the polymer segments with the surface of the substrate. In general for homopolymers, the interaction energy of the polymer segments with the substrate surface cannot be considered as the only parameter, which is responsible for the change in the thermal glass transition with the film thickness. For the investigated miscible blend system of polystyrene/poly(vinyl methyl ether) at a composition of 50/50 wt-% a decrease of the dynamic glass transition temperature with decreasing film thickness is found. This is explained by the formation of a poly(vinyl methyl ether)-rich surface layer with a higher molecular mobility.