The current knowledge about fatigue behavior of concrete is still incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. Therefore, the process of fatigue itself under cyclic compressive loading was investigated in a systematic and comprehensive way. The aim of this investigation was to obtain a deeper insight and to provide a better understanding of the damage process occurring within the material during fatigue loading. Concrete cylinders were tested with a number of cycles to failure between 106 and 107. To investigate macroscopic and microscopic changes in the material, various methods of non-destructive and destructive testing were used. One main result was, in contrast to other authors, that the investigated changes in macroscopic material behavior could not be explained only by a development of micro-cracks. The results indicated rather, that the related changes in the fatigue behavior are mainly a result of viscous processes in the hardened cement paste, similar to the processes of creep. Based on the experimental results a description of the possible processes was derived which take place in the material structure during fatigue loading and also leads to the observed macroscopic changes in the material behavior. In this context, the results have shown that in case of isotropic material behavior a stiffness reduction related to a scalar value could not capture the damage effect on the stress-strain-relationship caused by fatigue.
The current knowledge about fatigue behavior of concrete is still incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. Therefore, the process of fatigue itself under cyclic compressive loading was investigated in a systematic and comprehensive way. The aim of this investigation was to obtain a deeper insight and to provide a better understanding of the damage process occurring within the material during fatigue loading. Concrete cylinders were tested with a number of cycles to failure between 106 and 107. To investigate macroscopic and microscopic changes in the material, various methods of non-destructive and destructive testing were used. One main result was, in contrast to other authors, that the investigated changes in macroscopic material behavior could not be explained only by a development of micro-cracks. The results indicated rather, that the related changes in the fatigue behavior are mainly a result of viscous processes in the hardened cement paste, similar to the processes of creep. Based on the experimental results a description of the possible processes was derived which take place in the material structure during fatigue loading and also leads to the observed macroscopic changes in the material behavior. In this context, the results have shown that in case of isotropic material behavior a stiffness reduction related to a scalar value could not capture the damage effect on the stress-strain-relationship caused by fatigue.
Fatigue is of relevance not only for metals but also for concrete. The current knowledge about fatigue behaviour of concrete is, however, incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. Some macroscopic effects of this process are well known but the governing material changes behind them are still less studied. The focus of the present contribution lay on a systematic and comprehensive investigation of the fatigue process under cyclic compressive loading. The aim was to obtain a deeper insight and to provide a better understanding of the damage process in the material. Cylindrical specimens were tested with a number of cycles to failure between 106 and 107. Various methods of non-destructive and destructive testing were used to investigate macroscopic and microscopic changes in the material. One main result was that the changes in the macroscopic material behaviour could not be explained only by the development of micro cracks. The results indicated that the related changes in the fatigue behaviour originate rather from viscous processes in the cement stone, similar to the process of creep. A sound description of the possible processes was derived from the obtained experimental results which concerns material structure during fatigue loading. It has been shown that in case of isotropic material behaviour a stiffness reduction related to a scalar value could not capture the damage effect on the stress-strain relationship caused by fatigue.