Under the Comité Consultatif pour la Quantité de Matière (CCQM), a key comparison, CCQM-K104, was coordinated by the National Institute of Metrology (NIM). The comparison was designed to demonstrate a laboratory's performance in determining the mass fraction of the main component in a complex high purity organic material. Nine NMIs or DIs participated in the comparison. Eight participants reported their results. An additional impurity was resolved from the avermectin B1a peak and was tentatively identified as an unknown impurity by NMIA (National Measurement Institute (Australia)). It was subsequently identified by NIM as a diastereoisomer of avermectin B1a at the C-26 position. Final reference value (KCRV) = 924.63 mg/g, with uncertainty (k=1) = 3.89 mg/g, and expanded uncertainty = 8.97 mg/g. The degrees of equivalence with the avermectin B1a KCRV for each participant were reported. The measurement results and degrees of equivalence should be indicative of the performance of a laboratory's measurement capability for the purity assignment of organic compounds of high structural complexity (relative molecular mass range of 500 Da -1000 Da and low polarity (-log KOW ≤ -2).
Particle size gradation is regarded as an effective method for overcoming the contradicting requirements in three-dimensional printing (3DP). In present work, particle size gradation was optimized to obtain both acceptable flowability of the powder material and high-strength 3D-printed glass-ceramic products. The effect of gradation on the printing process, sintering process and performance of the 3D-printed glass-ceramic products was investigated comprehensively. The glass-ceramic powders with three size ranges were mixed in certain proportions and applied to print parts. The result showed parts printed with powder mixed by 60 wt% 45–100 µm and 40 wt% 0–25 µm particles had satisfactory density of 1.60 g/cm³ and bending strength of 13.8 MPa. The flowability decreased with an increasing proportion of fine particles. Part density was determined by the powder bulk density in the powder bed as well as the shrinkage during sintering while strength of part was found to be dependent on the sintering degree.