In order to reduce experimental effort, tribological tests are performed for coating selection, simulating the friction, wear and scuffing behaviour between the piston ring and cylinder liner, as well as lubricant evaluation. The creation of test standards in piston ring/cylinder liner simulation is discussed. PVD coatings, HVOF coatings and nitriding treatments have been applied to piston rings as alternative for chromium coatings. CrN/TiN coating seems very effective for increasing the wear and scuffing resistance. Biodegradable engine oils based on esters and polyglycols reduce friction and exceed the wear resistance of reference engine oils based on hydrocarbons for the new generation engines with high cylinder pressures.
The slip-rolling resistances of hard and stiff thin films under high Hertzian contact pressures can be improved by optimizing the 'coating/substrate systems'. It is known from former investigations that the so-called 'egg-shell' effect is no general hindrance for high slip-rolling resistance of thin hard coatings. The coating stability depends more on specific deposition process and coating/substrate interface design. In this article it is experimentally shown, that pure amorphous carbon thin films with hardness between 15 and 63 GPa can be slip-rolling resistant several million load cycles under a maximum Hertzian contact pressures of up to 3.0 GPa. Whereas all coatings were stable up to 10 million load cycles in paraffin oil at room temperature, reduced coating lifetime was found in SAE 0W-30 engine oil at 120°C. It was shown how the coating hardness and the initial coating surface roughness influence the running-in process and coating lifetime. No clear correlation between coating hardness and coating lifetime could be observed, but friction coefficients seem to be reduced with higher coating hardness. Very low friction down to ~0.03 in unmodified engine oils was found for the hardest ta-C film.------------------------------------------------------------------------------------------------------------------------------------------------
Die Wälzbeständigkeit von harten und steifen Dünnschichten unter hohen Hertzschen Kontaktpressungen kann durch die Optimierung des 'Beschichtung/Substrat Systems' deutlich verbessert werden. Aus vorangegangenen Untersuchungen ist bekannt, dass der so genannte 'Eierschaleneffekt' kein generelles Hindernis für eine hohe Wälzbeständigkeit für harte Dünnschichten darstellen muss. Die Stabilität der Beschichtungen hängt vielmehr von dem spezifischen Prozessparametern und dem Schicht/Substrat Grenzflächendesign ab. In diesem Artikel wird experimentell nachgewiesen, dass reine amorphe Kohlenstoffdünnschichten mit Härtewerten zwischen 15 und 63 GPa für mehrere Millionen Lastzyklen unter maximalen Hertzschen Kontaktpressungen bis 3.0 GPa überrollbeständig sein können. Während alle Beschichtungen bis 10 Millionen Lastzyklen in Paraffinöl bei Raumtemperatur keine Defekte aufweisen wurde unter Verwendung eines SAE 0W-30 Motorenöls bei 120°C eine Verringerung der Überrollbeständigkeit nachgewiesen. Es wurde nachgewiesen, wie die Schichthärte und ursprüngliche Oberflächenrauheit der Beschichtung den Einlaufprozess und die Lebensdauer beeinflussen. Es konnte keine offensichtliche Korrelation zwischen Schichthärte und Lebensdauer festgestellt werden, allerdings wurde eine scheinbare Reduktion des Reibwertes mit steigender Schichthärte beobachtet werden. Dabei zeigte die härteste ta-C Schicht unter Verwendung des Motorenöls sehr geringe Reibwerte mit ~0.03.
Downsizing (power-to-weight ratio) and higher speeds lead to a rise in Hertzian contact pressures in combination with an increase in surface or oil temperatures. Under such conditions, commonly used bearing steels, such as 100Cr6, reach their limits, creating a demand for alternative slip-rolling resistant steel alloys. The present work therefore compares the slip-rolling performance of various steel types with Maraging- and PM-type steel alloys such as e.g. CSS-42L™, ASP2012, BIMAX42+, in the Hertzian contact pressure range up to P0max of 4 GPa. Through-hardened 100Cr6H (AISI 52100), case-hardened 20MnCr5 (AISI 5120H) and nitrogen alloyed Croni-dur30 (AMS 5898) still compete in terms of slip-rolling and wear resistance and load carrying capacity, whereas Maraging- and PM-type steel alloys offer superior strength and toughness properties.
Zero wear (Null Verschleiß)
(2013)
We review contact mechanics with emphasis on the rheological (time dependent) properties of polymers and their relations to surface roughness, material properties, and friction as well as wear behavior of rubbing polymer surfaces. The main concept of polymer mechanics related to tribology consists of three basic elements involved in friction: deformation resulting in the real area of contact of rough surfaces, contact adhesion, and shear and rupture of materials in the contact during the sliding friction. The results of classical work are included, which addresses the real contact area calculation and the description of adhesion interaction between rough surfaces. A brief review of experimental investigations concerning the surface characterization by means of bearing curves, the intermolecular force interaction using the adhesion parameter, the effect of temperature on the real contact area, the formation of transferred polymer film during friction, and tribological behavior of ultrathin polymer layers are presented and their implications discussed.
The tribological profile of rotating disks made in binder-less niobium Carbide (hot-pressed NbC) and cobalt-bonded NbCs (NbC-8Co and NbC-12Co) mated against alumina (99.7%) were determined under unidirectional sliding tests (0.1 m/s to 8.0 m/s; 22°C and 400°C) as well as in oscillation tests (f= 20 Hz, Ax= 0.2 mm, 2/50/98% rel. humidity, n= 105/l 06 cycles) under unlubricated (dry) conditions. In addition, the microstructure and mechanical properties of HPNbCl and NbC bonded with 8 vol.-% and 12 vol.-% cobalt were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where the NbCs bonded with 8% and 12% Co presented above 7 m/s the lowest wear rates so far in such a bench mark. HP-NbCl, NbC-8Co and NbC-12Co exhibited low wear rates under dry sliding associated with PV high load carrying capacities. The tribological profile established revealed a strong position of NbC bearing materials under tribological considerations and for closed tribo-systems against traditional references.
The tribological and mechanical properties of niobium carbides (NbC) bonded with cobalt of Fe3Al
(2014)
The tribological and mechanical properties of niobium carbide bonded with 8 vol.-% (NbC-8Co), 12 vol.-% of cobalt (NbC-12Co) or 12 vol.-% of Fe3Al (NbC-12Fe3Al) are presented. Rotating discs made of metal-bonded niobium carbide were mated against alumina (99.7%) under unlubricated (dry) unidirectional sliding tests (0.1 m/s to 12.0 m/s; 22 °C and 400 C) as well as in oscillation tests (f=20 Hz, Δx=0.2 mm, 2/50/98% rel. humidity, n=105/106 cycles). Microstructure and phase compositions were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where NbC bonded with 8% and 12% Co presented above 7 m/s the lowest wear rates so far in such a benchmark. Binderless NbC (HP-NbC1) and the metal-bonded NbCs exhibited low wear rates under dry sliding associated with P·V high load carrying capacities. NbC-based hard metal bonded with 12 vol.-% of Fe3Al resulted in a higher hardness level than for 12 vol.-% cobalt. The tribological profile established revealed a strong position of NbC-bearing materials under tribological considerations and for closed tribosystems against established reference tribo-couples.
The automotive industry places significant importance on downsizing components to achieve greater efficiency. The goal of reducing CO2 emissions has led to the development of lightweight materials that are also able to enhance performance. In light of these aspirations, the aim of this study is to characterize two novel, high-performance steels, as well as a 'classical' gear steel for comparison with each other and currently applied materials. The gear steel underwent carburization and subsequent deep freezing treatments in an attempt to yield discrete sample groups with respect to residual austenite. The high-performance steels were heat treated as recommended by their respective manufacturers, and were not carburized. Elemental analyses were conducted by multiple methods to ensure accurate results. Residual austenite contents of the steels and the depth profiles of residual stresses were determined by X-ray diffraction (XRD). Hardness profiles were taken from the testing surfaces into the material core. The carburization of 20MnCr5 led to higher hardness and the greater concentration of carbon in the carburization zone more representative of a hardened SAE E52100, or 100Cr6/102Cr6, than of a non-carburized 20MnCr5. Residual austenite contents ranging from approximately 6–14 vol% were generated, though effectively providing only two, rather than the desired four discrete sample groups. Residual stresses from machining and carburization were measured directly at the sample surface, and from carburization alone below the surface. The high-performance steels fulfilled manufacturer expectations in terms of elemental content, hardness between 50 and 55 HRC and strongly martensitic microstructure character. Finally, slip-rolling endurance testing (T=+120 °C, 10,000,000 cycles, approximately 19 days in a factory fill engine oil) was carried out on all materials, whereby coefficient of friction distributions during testing and wear coefficients after testing were calculated. Testing was performed up to and including P0Mean=1.94 GPa (P0Max=2.91 GPa, FN=2000 N). Ultimately, the non-carburized high-performance steels showed competitive wear performance and better friction behaviour than the carburized 20MnCr5, which has been attributed to their work hardening capability.
The running-in phase of mechanical systems is critical from a tribological standpoint, though poorly understood. Microcracks accelerate material failure and wear during this phase of heightened friction. With this in mind, the ultimate goal of this current work is to transfer the running-in phase into the final step of the mechanical finishing process through the targeted pre-conditioning of novel, high toughness steel bearings without thermo-chemical treatments and compare these to conventional, case-hardened steels. This pre-conditioning involved the targeted implementation of two specific lubricant packages, the first with CaCO3 as the active ingredient and the second with MoDTC as the active ingredient, to generate chemically reactive tribolayers (tribofilms) on twin disk testing rigs. Pre-conditioning was carried out up to 104 load cycles (approximately 25 min). The films generated in pre-conditioning were analyzed by SEM-EDX with Element-Mapping, Raman spectroscopy, and XPS to elucidate their molecular composition and concentration on the sample surfaces. The combination of these methods of analysis gave a clear indication that 104 cycles were sufficient to generate stable chemical tribofilms. CaO and CaCO3 were the main components of the tribofilm from the first lubricant package, while MoS2, MoO2 and MoO3 were the main components from the second lubricant package. Tribofilm-protected samples were then subjected to slip-rolling endurance testing (T=+120 °C, 10,000,000 cycles, approximately 19 days in a factory fill engine oil) to determine any changes in friction behavior or wear performance. Some significant reductions in coefficients of friction at the end of endurance testing were observed, though in certain cases, no definitive improvement was observed. In contrast, very strong reductions in wear were observed across the entire spectrum of materials and testing loads. In some cases, sample surface wear reduction from pre-conditioning via tribofilms reached over 90%. The observed improvements to friction behavior and wear performance are indicative of a technically simple, cost- and energy-efficient pre-conditioning method that may prove to be competitive with existing thermochemical treatments for steel alloys.
Das tribologische Profil von binderlosem NbC und mit 8% bzw. mit 12% Cobalt oder 12% Fe3Al gebundenem NbC wird unter unidirektionaler Gleitreibung (v= 0,1-10 m/s, T= 22°C und 400°C) und unter oszillierender Gleitreibung vergleichend gegenüber Ingenieurkeramiken und Hartmetallen dargestellt. Zusätzlich werden die 4-Punkt-Biegebruchfestigkeit, elastische Eigenschaften (E,G) bis 1.000�C die lastabhängige Mikrohärte sowie die Phasenzusammensetzung und Gefügestrukturen vorgestellt. Die Verschleißkoeffizienten des binderlosen NbC lagen bei T unterhalb von 10-6 mm³/N?m, während diejenigen der cobaltgebundenen NbCs mit ansteigender Gleitgeschwindigkeit von 2-4 10-6 mm³/N?m bei 0,1 m/s auf 5-7 10-7 mm³/N.m bei 10 m/s abnahmen. Die Verschleißkoeffizienten bei 400°C lagen für die NbCs generell unterhalb von 10-6 mm³/N.m. Das tribologische Lasttragevermögen im Trockenlauf, ausgedrückt als PV-Wert, nimmt mit ansteigender Gleitgeschwindigkeit auf 100 W/mm² zu. Bedingt durch die geringe Löslichkeit von NbC in Legierungen offenbarten erste Zerspanversuche mit verschiedenen Stählen eine gegenüber WC-basierten Schneidstoffen signifikant angehobene Zerspanungsvolumina. Somit offenbart NbC in offenen und geschlossenen Tribosystemen Anwendungspotentiale.