The automotive industry places significant importance on downsizing components to achieve greater efficiency. The goal of reducing CO2 emissions has led to the development of lightweight materials that are also able to enhance performance. In light of these aspirations, the aim of this study is to characterize two novel, high-performance steels, as well as a 'classical' gear steel for comparison with each other and currently applied materials. The gear steel underwent carburization and subsequent deep freezing treatments in an attempt to yield discrete sample groups with respect to residual austenite. The high-performance steels were heat treated as recommended by their respective manufacturers, and were not carburized. Elemental analyses were conducted by multiple methods to ensure accurate results. Residual austenite contents of the steels and the depth profiles of residual stresses were determined by X-ray diffraction (XRD). Hardness profiles were taken from the testing surfaces into the material core. The carburization of 20MnCr5 led to higher hardness and the greater concentration of carbon in the carburization zone more representative of a hardened SAE E52100, or 100Cr6/102Cr6, than of a non-carburized 20MnCr5. Residual austenite contents ranging from approximately 6–14 vol% were generated, though effectively providing only two, rather than the desired four discrete sample groups. Residual stresses from machining and carburization were measured directly at the sample surface, and from carburization alone below the surface. The high-performance steels fulfilled manufacturer expectations in terms of elemental content, hardness between 50 and 55 HRC and strongly martensitic microstructure character. Finally, slip-rolling endurance testing (T=+120 °C, 10,000,000 cycles, approximately 19 days in a factory fill engine oil) was carried out on all materials, whereby coefficient of friction distributions during testing and wear coefficients after testing were calculated. Testing was performed up to and including P0Mean=1.94 GPa (P0Max=2.91 GPa, FN=2000 N). Ultimately, the non-carburized high-performance steels showed competitive wear performance and better friction behaviour than the carburized 20MnCr5, which has been attributed to their work hardening capability.
The running-in phase of mechanical systems is critical from a tribological standpoint, though poorly understood. Microcracks accelerate material failure and wear during this phase of heightened friction. With this in mind, the ultimate goal of this current work is to transfer the running-in phase into the final step of the mechanical finishing process through the targeted pre-conditioning of novel, high toughness steel bearings without thermo-chemical treatments and compare these to conventional, case-hardened steels. This pre-conditioning involved the targeted implementation of two specific lubricant packages, the first with CaCO3 as the active ingredient and the second with MoDTC as the active ingredient, to generate chemically reactive tribolayers (tribofilms) on twin disk testing rigs. Pre-conditioning was carried out up to 104 load cycles (approximately 25 min). The films generated in pre-conditioning were analyzed by SEM-EDX with Element-Mapping, Raman spectroscopy, and XPS to elucidate their molecular composition and concentration on the sample surfaces. The combination of these methods of analysis gave a clear indication that 104 cycles were sufficient to generate stable chemical tribofilms. CaO and CaCO3 were the main components of the tribofilm from the first lubricant package, while MoS2, MoO2 and MoO3 were the main components from the second lubricant package. Tribofilm-protected samples were then subjected to slip-rolling endurance testing (T=+120 °C, 10,000,000 cycles, approximately 19 days in a factory fill engine oil) to determine any changes in friction behavior or wear performance. Some significant reductions in coefficients of friction at the end of endurance testing were observed, though in certain cases, no definitive improvement was observed. In contrast, very strong reductions in wear were observed across the entire spectrum of materials and testing loads. In some cases, sample surface wear reduction from pre-conditioning via tribofilms reached over 90%. The observed improvements to friction behavior and wear performance are indicative of a technically simple, cost- and energy-efficient pre-conditioning method that may prove to be competitive with existing thermochemical treatments for steel alloys.
The origin of the intrinsic wear resistance of NbC-based materials is investigated through an assessment of the tribological performance of fully dense, crack-free spark plasma sintered Nb2O5 (here as a reduced polymorph: monoclinic Nb12O29 or NbO2.416). The most likely wear mechanism on NbC is the tribo-oxidation to Nb2O5. The unlubricated (dry) friction and wear behavior of alumina (99.7%) mated against rotating disks of crack-free niobium(V)oxide (Nb2O5) under unidirectional sliding (0.03–10m/s; 22°C and 400°C) and oscillation (f=20 Hz, dx=200 mm, 2/50/98% rel. humidity, n=105/106 cycles) will be presented. The microstructure and mechanical properties of the crack-free Nb2O5 are assessed. The tribological data obtained are benchmarked with different NbC grades, ceramics, cermets and thermally sprayed coatings.
The research institution TEKNIKER has coordinated the EUROPEAN Project EREBIO, were different biodegradable lubricants have been formulated by FUCHS and BAM for heavy duty engines (GUASCOR), and passenger cars (RENAULT). In the frame of this article, it has been summarised the results obtained when developing biodegradable passenger car lubricants in combination with triboreactive materials.
Replacing hydrocarbon-based oils with biodegradable products is one of the ways to reduce adverse effects on the ecosystem caused by the use of lubricants. The application of low or no sulphur, ash and phosphorous (lowSAP) ester- or polyglycol-based oils, intended for passenger car engine lubricants as substitutes for hydrocarbon-based oils, required the preparation of a composition of lubricants with comparable tribological and functional properties.
The study is focussed on passenger car motor oils (PCMO) with reduced metal-organic additives. This is necessary in order to reduce the ash build-up in the after treatment system and therefore improve its efficiency and lifetime. High fuel efficiency and long drain intervals are requested, as well. To follow a line in a consequent way, these oils have to be biodegradable and non-toxic to the aqueous environment according to the directive EC/1999/45, coherent with other international standard. In a modern diesel or gasoline engine, the engine oils has to fulfil quite a number of different functions, such as lubricating and cooling the system, wear protection, soot and particle handling with less deposit tendency and so on.
In the paper a study of the biodegradability, toxicity and the tribological properties has been carried out for new developed prototype engine bio-oils. Also, some different plasma sprayed triboreactive coatings have been deposited on cast iron piston rings, being studied also their tribological properties. Finally, the behaviour of the new bio-oils selected and plasma sprayed triboreactive coatings on piston rings have been screened in a real engine.
Zero wear (Null Verschleiß)
(2013)
We review contact mechanics with emphasis on the rheological (time dependent) properties of polymers and their relations to surface roughness, material properties, and friction as well as wear behavior of rubbing polymer surfaces. The main concept of polymer mechanics related to tribology consists of three basic elements involved in friction: deformation resulting in the real area of contact of rough surfaces, contact adhesion, and shear and rupture of materials in the contact during the sliding friction. The results of classical work are included, which addresses the real contact area calculation and the description of adhesion interaction between rough surfaces. A brief review of experimental investigations concerning the surface characterization by means of bearing curves, the intermolecular force interaction using the adhesion parameter, the effect of temperature on the real contact area, the formation of transferred polymer film during friction, and tribological behavior of ultrathin polymer layers are presented and their implications discussed.
A novel tribometer has been designed using commercially available components for sliding motion at 40kHz with amplitude between 2.5 and 5µm. The tribometer is equipped with means to measure amplitude, frequency, power required to keep the sample in motion and load applied. The effective motion between the two contacting bodies is monitored. These data are used to evaluate the coefficient of friction. The wear rate was determined after the tests. The set-up was tested using novel, non-commercial substrates such as AlFeCrTi-alloys and tungsten carbide-based coatings as well as Magnéli-type coatings (Tin-2Cr2O2n-1 and TinO2n-1). This paper presents the principle of the ultra-high frequency tribometer and first tribological quantities of materials and coatings tested.
The use of alternative base oils, like esters or polyglycols, with more intrinsic properties for the lubrication of automobile engines has a potential for ecological and technical advantages. Being in competition with hydrocarbon-based formulations, detailed knowledge of several thermophysical and viscometric properties as well as tribological properties over a large temperature range are required (mapping). The tested polymer-free polyglycols and ester-based formulations displayed no visible tribological weaknesses regarding wear resistance and EP-behavior as well as offering significant advantages in order to meet metal- and ash-free and bio-no-tox criteria. Especially the formulated polyglycols without friction modifiers also showed an intrinsic retention of low coefficients of friction and a hydrodynamic film forming behavior comparable to hydrocarbon-based factory-fill oils. The wear resistance and EP-behavior of low-additivated polyglycols, but also of esters, can be enhanced by means of triboactive materials. Lubricious oxides or triboactive materials and polar base oils, or a combination thereof, may substitute the EP and AW properties realized by the additives, thus enabling long drains and responding to eco-tox or bio-no-tox requirements as well as restrictions from the chemical box.
In the present work it was shown that the tribologcal profiles of special model oxides under dry unidirectional sliding have shown, that sub-oxides have a contribution to the tribological behavior of carbides and cermets, when they are tribo-oxidatively formed, because their tribological profiles as monolithic materials are homologous in part or totally, or compete with hardmetals or cermets, depending from the operating conditions regarded.