Wälzbeständigkeit von ta-C Dünnschichten unter hohen Hertzschen Beanspruchungen bis zu 3000 MPa
(2010)
Original equipment manufacturers (OEMs) and end-users perceive 'Zero Wear' differently. The 'Zero Wear' approach will be put into a general relation for different applications and illuminated by individual paths, either based on monolithic materials, thin film coatings or alternative base oils, featuring triboactive materials and lubricious oxides for tribological engine components and dry running foil bearings or specific DLC, ta-C and novel Zirconium-based thin film coatings for concentrated contacts above FZG 14 and alternative engine oils (NoSAP & bio-no-tox). The associated tribometric test equipments for these examples will also be detailed.
Some of the properties intrinsically present in the backbone of polyalkylene glycols (PAGs), which have nowadays attracted the automotive original equipment manufacturers (OEMs), are presented, such as bio-no-tox properties, heat capacity, extended drains, low friction, low AlSi-liner wear, fuel economy, and very high viscosity indices, and are achieved with metal-, ash-, and polymer-free formulations, which guarantee no adverse contamination of the lambda sensor and the active centers of the catalyzer as well as not to increase the exhaust back pressure of the particulate filter through ash deposits. This paper illuminates the latest results from OEM's engine bench and road testing supporting the following functional benefits: (a) bio-no-tox, (b) improvements of fuel economy, even when compared with latest hydrocarbon-based prototype oils, (c) reduced wear, (d) reduced engine friction, (e) extended drains, (f) suited for bio-fuels, (g) no adverse effects on after-treatment devices through ash-, metal-, and polymer-free formulations, etc.
Paraffinöl geschmierte Wälztests wurden an extrem harten Diamantschichten auf hartem SSiC Substrat, unterschiedlichen, harten DLC-Schichten auf 100Cr6 Substraten (HRC60) sowie ausgewählten DLC-Schichten auf ungehärtetem Stahl (HRC 20) durchgeführt. Die Wälztests wurden in einem Zweischeibentribometer vom Typ Amsler bei einer anfänglichen, maximalen Flächenpressung nach Hertz von P0=2,3 GPa ausgeführt. Als Abbruchkriterium für die Tests wurde das Erreichen von n=1.000.000 Überrollungen (Langzeittests n=10.000.000 Überrollungen) oder das Auftreten einer Schädigung mit einer zusammenhängenden Fläche von A>1 mm2 festgelegt. Die Wälztests zeigten, dass das harte SSiC Substrat zwar eine stützende Wirkung auf die Diamantschicht hat, diese aber aufgrund von Rissen im Substrat versagte. Ferner gibt es wenigstens zwei DLC-Schichten, die, aufgebracht auf 100Cr6 Scheiben (HRC60), den Wälztests bis n=10.000.000 Überrollungen ohne nennenswerte Schäden widerstanden. Diese Schichten passten sich auch den Verformungen des weichen, stickstofflegierten Stahls (HRC20) an, ohne das es zu größeren Abplatzungen kam (A>1 mm2).
Diamond-like carbon (DLC) coatings are perceived as part of a strategy for low frictional tribosystems. Especially the automotive industry anticipates a benefit in applying such coatings in association with the lightweight construction of mechanical parts, for instance in gear and engine components. Therefore, in previous investigations amorphous carbon (a-C) and tetragonal amorphous carbon (ta-C) coatings were inspected. For up to ten million cycles at Hertzian contact pressures P0max of 2.9 GPa it was shown that these coatings are slip-rolling resistant not only at room temperature in the presence of unaddivated paraffin oil, but also up to 120 °C oil temperature. The steel substrates in this investigation were made of the hardened and tempered steels 100Cr6H and Cronidur 30. The aim of the current work is manifold. The Hertzian contact pressures should be increased up to P0max of 4.2 GPa by using new steel metallurgies as substrates for thin film coatings. These steel metallurgies are also assessed, if they can compete as uncoated couples. Two high toughness spring steels and an ultra-high toughness aerospace steel were tested in a twin disc tribometer of the Amsler type as well as in an Optimol 2Disk test rig under mixed/boundary conditions in a factory fill SAE 0W-30 engine oil. Different factors such as influences of the lubrication, surface chemistry and wear behaviour were investigated.
The slip-rolling resistance of DLC, a-C and ta-C thin film coatings was improved considerably in the last years, but there is still room for improvements in relation to (a) the temperature stability and (b) initial surface roughness after deposition. This paper presents a novel coating-substrate system in comparison to recently developed DLC coatings in a bench-mark test procedure exerting slip-rolling conditions in the presence of liquid lubricants. One of the Zr-based thin film coatings can withstand at least 1 million cycles under initial Hertzian contact pressures of up to P0max = 3500 MPa and oil temperatures of at least 120 °C associated with low coefficients of friction under mixed/boundary conditions or ten million of cycles under P0max = 2940 MPa. In comparison, some of the newly developed DLC coatings are slip-rolling resistant for at least up to 10 million cycles at RT (some of them also at 120 °C oil temperature) under Hertzian contact pressures of Pmax = 2600/2940 MPa. In general, Zr-based thin film coatings do not require special formulated oil formulations and Zr(C,N) bear on a straight coating architecture suited for mass production with nanosized layers.
The light-weight approach and fuel economy targets in today's automotive engineering require tribosystems, which can withstand higher contact pressures associated with low coefficients of friction. The application of high-performance coatings represents one approach among others. This paper presents some recently developed DLC coatings (a-C:H and ta-C) as well as a novel coating-substrate system (Zr(C,N)) in a benchmark test procedure under slip-rolling conditions in the presence of liquid lubricants. Various coatings with different thickness, interlayer and substrates were evaluated for their slip-rolling resistance in different lubricants at ambient temperature and at 120 °C. Results indicate that some of these coating systems can withstand at least 10 million cycles under initial Hertzian contact pressures of up to Pmax = 3.500 MPa and oil temperatures of at least 120 °C associated with low coefficients of friction under mixed/boundary conditions. Surface of the coatings and the counter bodies were analysed and compared with untreated substrates.