Research and development of WC grades is 90 years ahead of niobium carbide-based hard materials, which showed already as light-weight and unexplored material a very high potential for many technical applications, especially for wear protection and machining. NbC evoluted recently from lab scale to pilot scale, especially in areas where established WC-based materials are causing economic, environmental or technical concerns. Benchmark trials of NbC-based hard metals indicated already a favorable performance in machining of steel components.
The present paper illuminates the metallurgical progress on niobium carbide based hard metal developments, which are characterized by: a.) the substitution of cobalt binder by nickel, b.) the change from SPS to conventional sintering and c.) by switching from lab to pilot scale. The toughness was increased in the frame of these developments without loosening the hardness level. The hardness-toughness profile of NbC grades match those of WC and cermet grades. Apart from the aforementioned parameters, the properties depend from the powder processing and sintering conditions.
The functional profile of nickel and NiMo bonded NbC versus cobalt bondedWC grades bonded by cobalt and nickel are benchmarked under dry sliding wear (T= 22/400°C; v= 0,1-10 m/s), abrasive wear (G65) and under dry turning and dry milling against different work piece alloys (C45E, 42CrMo4, 300WA, GG35, AlSi9Cu4Mg). The different elements explaining the wear resistance of NbC over WC will be illuminated.
The present paper illuminates the metallurgical progress on niobium carbide based hard metal developments, which are characterized by: a.) the substitution of cobalt binder by nickel, b.) the change from SPS to conventional sintering and c.) by switching from lab to pilot scale. The toughness was increased in the frame of these develop¬ments without loosening the hardness level. Stoichiometric and sub-stoichiometric, submicron NbC powders were used. The hardness-toughness profile of NbC grades match those of WC and cermet grades. Apart from the aforementioned parameters, the properties depend from the powder processing and sintering conditions. The functional profile of NbC and WC grades bonded by cobalt and nickel are benchmarked by 4-point bending strength, elastic moduli and hot hardness until 1000°C, dry sliding wear (T= 22/400°C; v= 0,1-10 m/s), abrasive wear (G65) and cutting performances under emulsion and coolant-free turning and milling against different alloys (C60, 100Cr6, 42CrMo4, X90CrMoV18, 300WA, GG35).
The present work deals with Niobcarbid (NbC). Strategic reflections on tungsten carbide and more and more stringent toxicological restrictions for cobalt associated for both with spiraling stock market prices have attracted recently some attention for Niobium carbide as a substitute for tungsten carbide in machining.
The present work deals with Niobcarbid (NbC). Strategic reflections on tungsten carbide and more and more stringent toxicological restrictions for cobalt associated for both with spiraling stock market prices have attracted recently some attention for Niobium carbide as a substitute for tungsten carbide in machining.
The process window and range of functional properties of NbC is wide, because micro-hardness, hot hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, because Nb4C3, Nb6C5 and other short and long range ordered phases occur in the region of homogeneity of NbCx (0,75≤ x ≤1.0) in the binary Phase diagram, and by the type of binder. Further improvements enable the addition of secondary carbides. Supporting results from literature and different grades with varying C/Nb ratio or binder types were illuminated. Thus, the NbC system offers to producers a wider process window, than WC. The impact of these tailored properties on sliding wear and cutting performance was illuminated by tribological and machining results. NbC can be synthesized by carbothermal conversion of Nb2O5 or be metallurgically grown in melts and leached out as coarse NbC cubes. NbC provides comparably lower friction in many relevant tribo-contacts and displays low wear. NbC and Nb2O5 have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO3 and Co3O4.
In this present study, the mechanical properties (strength, hardness, moduli) and the dry sliding properties of stoichiometric and sub-stoichiometric NbC were compared. Microhardness and elastic properties of NbC depend from the C/Nb ratio, because the binary phase diagram Nb-C shows a region of homogeneity of NbCx of 0,72≤ x ≤1.0. At RT, hard metals of stoichiometric NbC have an elastic modulus E of ~440 GPa, those of substochiometric NbC0,88 an E of 405 GPa. The hot hardness of sub-stoichiometric NbC is above 600°C higher than of WC. The dry sliding wear resistance (0,1-7/10 m/s) of the present Fe3Al-NbC0,94 with ~61 vol.-% NbC as hard phase was close to those known of NbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks of the Fe3Al-NbC composite (MMC), as a metallurgical interphase was formed between matrix and NbC grains. Stoichiometric and sub-stoichiometric niobium carbides have at RT and 400°C under dry sliding a prone intrinsic wear resistance more or less independent from sliding speed, either as hardmetal or as hard phase in metal matrix composite, associated with an exceptional high load carrying capacity.