Self-mated magnesia stabilized zirconia (Mg-PSZ) ceramic sliding couples have been investigated at 100 N load (P0max= 1324 MPa) in oscillating sliding conditions in different humidity conditions in air and in hot steam. Temperatures have been varied up to 400 °C and pressures up to 6 bars. The results show that the wear behavior of MgO-ZrO2 under high Hertzian contact pressures is strongly dependent on temperature and is similar for both dry oscillating and oscillating in hot steam. However, although the evolution in wear rates on temperature is similar and the wear rates of MgO-ZrO2 plunged above 300 °C in hot steam and air by nearly three orders of magnitude, SEM micrographs revealed in hot steam at 400 °C smooth wear tracks. In contrast, hot steam enhanced the tribochemistry of self-mated alumina couples and reduced wear rates. Hot steam decreased the coefficients of friction of MgO-ZrO2 with increasing temperature, but not the wear rates.
The wear rates of self-mated alumina couples show that friction as well as wear is largely determined by the above-mentioned hydro-thermal conditions. The presence of water and its amount available in the surrounding system either in liquid or in gaseous form plays a key role for friction and wear behavior and can be beneficial for the tribological profile of steam degradation resistant materials. Hot steam enhances the tribo-chemical formations of oxides and hydroxides on MgO-ZrO2 alumina and antimony impregnated carbon.
The slip-rolling resistances of hard and stiff thin films under high Hertzian contact pressures can be improved by optimizing the 'coating/substrate systems'. It is known from former investigations that the so-called 'egg-shell' effect is no general hindrance for high slip-rolling resistance of thin hard coatings. The coating stability depends more on specific deposition process and coating/substrate interface design. In this article it is experimentally shown, that pure amorphous carbon thin films with hardness between 15 and 63 GPa can be slip-rolling resistant several million load cycles under a maximum Hertzian contact pressures of up to 3.0 GPa. Whereas all coatings were stable up to 10 million load cycles in paraffin oil at room temperature, reduced coating lifetime was found in SAE 0W-30 engine oil at 120°C. It was shown how the coating hardness and the initial coating surface roughness influence the running-in process and coating lifetime. No clear correlation between coating hardness and coating lifetime could be observed, but friction coefficients seem to be reduced with higher coating hardness. Very low friction down to ~0.03 in unmodified engine oils was found for the hardest ta-C film.------------------------------------------------------------------------------------------------------------------------------------------------
Die Wälzbeständigkeit von harten und steifen Dünnschichten unter hohen Hertzschen Kontaktpressungen kann durch die Optimierung des 'Beschichtung/Substrat Systems' deutlich verbessert werden. Aus vorangegangenen Untersuchungen ist bekannt, dass der so genannte 'Eierschaleneffekt' kein generelles Hindernis für eine hohe Wälzbeständigkeit für harte Dünnschichten darstellen muss. Die Stabilität der Beschichtungen hängt vielmehr von dem spezifischen Prozessparametern und dem Schicht/Substrat Grenzflächendesign ab. In diesem Artikel wird experimentell nachgewiesen, dass reine amorphe Kohlenstoffdünnschichten mit Härtewerten zwischen 15 und 63 GPa für mehrere Millionen Lastzyklen unter maximalen Hertzschen Kontaktpressungen bis 3.0 GPa überrollbeständig sein können. Während alle Beschichtungen bis 10 Millionen Lastzyklen in Paraffinöl bei Raumtemperatur keine Defekte aufweisen wurde unter Verwendung eines SAE 0W-30 Motorenöls bei 120°C eine Verringerung der Überrollbeständigkeit nachgewiesen. Es wurde nachgewiesen, wie die Schichthärte und ursprüngliche Oberflächenrauheit der Beschichtung den Einlaufprozess und die Lebensdauer beeinflussen. Es konnte keine offensichtliche Korrelation zwischen Schichthärte und Lebensdauer festgestellt werden, allerdings wurde eine scheinbare Reduktion des Reibwertes mit steigender Schichthärte beobachtet werden. Dabei zeigte die härteste ta-C Schicht unter Verwendung des Motorenöls sehr geringe Reibwerte mit ~0.03.
Downsizing (power-to-weight ratio) and higher speeds lead to a rise in Hertzian contact pressures in combination with an increase in surface or oil temperatures. Under such conditions, commonly used bearing steels, such as 100Cr6, reach their limits, creating a demand for alternative slip-rolling resistant steel alloys. The present work therefore compares the slip-rolling performance of various steel types with Maraging- and PM-type steel alloys such as e.g. CSS-42L™, ASP2012, BIMAX42+, in the Hertzian contact pressure range up to P0max of 4 GPa. Through-hardened 100Cr6H (AISI 52100), case-hardened 20MnCr5 (AISI 5120H) and nitrogen alloyed Croni-dur30 (AMS 5898) still compete in terms of slip-rolling and wear resistance and load carrying capacity, whereas Maraging- and PM-type steel alloys offer superior strength and toughness properties.
The tribological profile of rotating disks made in binder-less niobium Carbide (hot-pressed NbC) and cobalt-bonded NbCs (NbC-8Co and NbC-12Co) mated against alumina (99.7%) were determined under unidirectional sliding tests (0.1 m/s to 8.0 m/s; 22°C and 400°C) as well as in oscillation tests (f= 20 Hz, Ax= 0.2 mm, 2/50/98% rel. humidity, n= 105/l 06 cycles) under unlubricated (dry) conditions. In addition, the microstructure and mechanical properties of HPNbCl and NbC bonded with 8 vol.-% and 12 vol.-% cobalt were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where the NbCs bonded with 8% and 12% Co presented above 7 m/s the lowest wear rates so far in such a bench mark. HP-NbCl, NbC-8Co and NbC-12Co exhibited low wear rates under dry sliding associated with PV high load carrying capacities. The tribological profile established revealed a strong position of NbC bearing materials under tribological considerations and for closed tribo-systems against traditional references.
The tribological and mechanical properties of niobium carbides (NbC) bonded with cobalt of Fe3Al
(2014)
The tribological and mechanical properties of niobium carbide bonded with 8 vol.-% (NbC-8Co), 12 vol.-% of cobalt (NbC-12Co) or 12 vol.-% of Fe3Al (NbC-12Fe3Al) are presented. Rotating discs made of metal-bonded niobium carbide were mated against alumina (99.7%) under unlubricated (dry) unidirectional sliding tests (0.1 m/s to 12.0 m/s; 22 °C and 400 C) as well as in oscillation tests (f=20 Hz, Δx=0.2 mm, 2/50/98% rel. humidity, n=105/106 cycles). Microstructure and phase compositions were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where NbC bonded with 8% and 12% Co presented above 7 m/s the lowest wear rates so far in such a benchmark. Binderless NbC (HP-NbC1) and the metal-bonded NbCs exhibited low wear rates under dry sliding associated with P·V high load carrying capacities. NbC-based hard metal bonded with 12 vol.-% of Fe3Al resulted in a higher hardness level than for 12 vol.-% cobalt. The tribological profile established revealed a strong position of NbC-bearing materials under tribological considerations and for closed tribosystems against established reference tribo-couples.
Das tribologische Profil von binderlosem NbC und mit 8% bzw. mit 12% Cobalt oder 12% Fe3Al gebundenem NbC wird unter unidirektionaler Gleitreibung (v= 0,1-10 m/s, T= 22°C und 400°C) und unter oszillierender Gleitreibung vergleichend gegenüber Ingenieurkeramiken und Hartmetallen dargestellt. Zusätzlich werden die 4-Punkt-Biegebruchfestigkeit, elastische Eigenschaften (E,G) bis 1.000�C die lastabhängige Mikrohärte sowie die Phasenzusammensetzung und Gefügestrukturen vorgestellt. Die Verschleißkoeffizienten des binderlosen NbC lagen bei T unterhalb von 10-6 mm³/N?m, während diejenigen der cobaltgebundenen NbCs mit ansteigender Gleitgeschwindigkeit von 2-4 10-6 mm³/N?m bei 0,1 m/s auf 5-7 10-7 mm³/N.m bei 10 m/s abnahmen. Die Verschleißkoeffizienten bei 400°C lagen für die NbCs generell unterhalb von 10-6 mm³/N.m. Das tribologische Lasttragevermögen im Trockenlauf, ausgedrückt als PV-Wert, nimmt mit ansteigender Gleitgeschwindigkeit auf 100 W/mm² zu. Bedingt durch die geringe Löslichkeit von NbC in Legierungen offenbarten erste Zerspanversuche mit verschiedenen Stählen eine gegenüber WC-basierten Schneidstoffen signifikant angehobene Zerspanungsvolumina. Somit offenbart NbC in offenen und geschlossenen Tribosystemen Anwendungspotentiale.