Thermosetting moulding compounds are synthetic materials which can be easily formed in the molten state and achieve high temperature stability due to a cross-linking process which takes place during manufacture. To ensure thermal and mechanical properties, post-curing of moulded phenolic resin components is necessary for high quality applications. In the industrial practice, post-curing time-temperature-programs are heuristically acquired. In this paper, dynamical mechanical thermal analysis is employed to determine optimal post-curing conditions for injection moulded parts from phenolic resin.
Ultrasound waves penetrate solid objects without damaging them. Their fields of application range from the imaging of internal organs in medicine, to interior testing of mechanical and chemical engineering components. However, ultrasonic systems can also be used to visualise the way the mechanical properties of reactive resins change during processing in the mould.
In recent years eure monitoring with ultrasonic methods became more important. An on-line measurement System for industrial applications is presented in this paper. It operates in through-transmission and the measured parameters are the sound velocity and the attenuation of the sound wave. An objective of this paper is to establish the ränge of possible applications for an ultrasonic eure monitoring System.
Elastomers are widely used as the main sealing materials for containers for low and intermediate level radioactive waste and as an additional component to metal seals in spent fuel and high active waste containers. The safe encapsulation of the radioactive container inventory has to be guaranteed according to regulation and appropriate guidelines for long term storage periods as well as for temperatures as low as -40°C during transport. Therefore, the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance. It is known that the material properties of elastomers are strongly temperature dependent. At low temperatures, this is caused by the rubber-glass transition (abbreviated: glass transition). During continuous cooling, the material changes from a rubber-like entropy elastic to a stiff energy elastic behaviour, which allows nearly no strain or retraction. Hence, rubbers are normally used above their glass transition, but the minimum working temperature limit is not defined precisely; this can cause problems during the above noted applications. Therefore, the lower operation temperature limit of elastomer seals must be determined in dependence of the material properties. Differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA) are combined with standardised measurements to determine the compression set according to ISO 815. To reduce the test time of the standard tests, a faster technique than normally used was developed. Additionally, the breakdown temperature of the sealing function of complete O ring seals was measured in a component test set-up to compare it with the results of the other tests. The experimental set-up is capable of measuring the leakage rate at low temperatures by the pressure rise method. A fluorocarbon rubber (FKM) was selected for this investigation as it is often used for radioactive waste containers. The materials (seals and test sheets) were purchased from a commercial seal producer.
Viscoelastic properties of cellular polypropylene ferroelectrets (PP FEs) were studied at low
frequencies (0.3–33 Hz) by dynamic mechanical analysis and at high frequencies (250 kHz) by laser Doppler vibrometry. Relaxation behavior of the in-plane Young’s modulus (Y´
11~1500 MPa at room temperature) was observed and attributed to the viscoelastic response of polypropylene matrix.
The out-of-plane Young’s modulus is very small (Y´33≈0.1 MPa) at low frequencies, frequency- and stress-dependent, evidencing nonlinear viscoelastic response of PP FEs. The highfrequency mechanical response of PP FEs is shown to be linear viscoelastic with Y´33≈0.8 MPa. It is described by thickness vibration mode and modeled as a damped harmonic oscillator with one degree of freedom. Frequency dependence of Y*33 in the large dynamic strain regime is described by the broad Cole-Cole relaxation with a mean frequency in kHz range attributed to the Dynamics of the air flow between partially closed air-filled voids in PP FEs. Switching-off the relaxation contribution causes dynamic crossover from the nonlinear viscoelastic regime at low frequencies to the linear viscoelastic regime at high frequencies. In the small strain regime, contribution of the air flow seems to be insignificant and the power-law response, attributed to the mechanics of polypropylene cell walls and closed air voids, dominates in a broad frequency range. Mechanical Relaxation caused by the air flow mechanism takes place in the sound and ultrasound frequency range (10 Hz–1MHz) and, therefore, should be taken into account in ultrasonic applications of the PP FEs deal with strong exciting or receiving signals.