Two types of commercially applied Ethylene/Vinyl Acetate Copolymers (EVA) for encapsulation of photovoltaic modules were investigated by the thermal analysis methods of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) in the temperature range from -150 °C to 200 °C. Glass transition, crystal melting and cross-linking were analyzed. The aims of the investigations were to gain more information for incoming goods control and to get information about the whole temperature dependent material properties in the investigated temperature range, starting at very low temperatures up to the crosslinking temperature region.
Thermoanalytische Charakterisierung von Ethylen-Vinylacetat-Copolymer (EVA) für Photovoltaikmodule
(2011)
Das Ziel der Untersuchungen war mit Hilfe von DSC und DMA EVA-Folien im Anlieferungszustand hinsichtlich der Lage der Glasübergangstemperatur, des Schmelzverhaltens und der Temperaturabhängigkeit der Vernetzungsreaktion zu charakterisieren. Auf dieser Basis sollte die Lieferstabilität im Sinne einer Wareneingangskontrolle auf eine messtechnische Basis gestellt werden. In einem 2. Schritt sollte die vernetzte Folie dahingehend charakterisiert werden, ob infolge der Vernetzung eine Änderung der
Carbon fibre prepregs have found widespread application in lightweight constructions. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. DMA measurements under temperature conditions similar to an autoclave programme were carried out using commercially available prepreg material with a high glass transition temperature. The characteristic of the temperature programme was a dynamic heating segment at 1.5 K/min followed by a longer isothermal segment at 180 °C. The courses of the storage modulus E', loss modulus E'' and tanδ were recorded. The measuring frequency was varied between 1 Hz and 33.3 Hz. Gelation and vitrification are assigned. The influence of the measuring frequency on the time to vitrification and the correlation with DSC are discussed. The reaction does not end even after 10 h curing at 180 °C, which is interpreted as the slow cessation of the reaction caused by vitrification.