Filtern
Dokumenttyp
Sprache
- Englisch (27) (entfernen)
Schlagworte
- Compression set (6)
- Elastomer (6)
- Dynamic mechanical analysis (5)
- DSC (4)
- Glass transition (4)
- Low temperature behaviour (4)
- Sealing material (4)
- Ultrasound (4)
- Curemeter (3)
- Dichtungen (3)
- Prepreg (3)
- Vulcanization (3)
- Cross-linking (2)
- Cure process (2)
- DMA (2)
- EVA (2)
- Elastomere (2)
- Low temperature (2)
- Tieftemperaturverhalten (2)
- Acoustic propagation (1)
- Autoclave (1)
- Bauteilversuche (1)
- CFC (1)
- Carbon fibre (1)
- Component test (1)
- Composites (1)
- Cross linked polyethylene insulation (1)
- Crosslinking (1)
- Crystal melting (1)
- Cure monitoring (1)
- Curing (1)
- Degree of cure (1)
- Degree of curing (1)
- Dielectric relaxation (1)
- Druckverformungsrest (1)
- Elastomers (1)
- Epoxy (1)
- Ethylene vinyl acetate (1)
- Ferroelectric polymer (1)
- Gelation (1)
- Injection moulding (1)
- Leakage rate (1)
- Mechanical variables measurement (1)
- Natural rubber (1)
- O-Ringe (1)
- O-ring (1)
- On-line monitoring (1)
- Online control (1)
- P(VDF-HFP) (1)
- Poly(vinylidene(fluoride - hexafluoropropylene) (1)
- Rheology (1)
- Rubber seals (1)
- Seal (1)
- Silicone rubber (1)
- Sound velocity (1)
- TMDSC (1)
- Thermal analysis (1)
- Tiefe Temperatur (1)
- Ultrasonic (1)
- Uniaxial stretching (1)
- Vitrification (1)
- Vulcanisation (1)
Partial discharges may cause damage to electrical insulation of high voltage equipment. They initiate elastic waves in the insulating material, e.g. in the stress cone of an outdoor termination. Localisation of the origin of such elastic waves can help to predict serious damaging processes in the electrical insulation. In order to measure and evaluate the wave propagation effects in typical multilayered elastomeric structures, knowledge of the material properties is required. The propagating velocity and the attenuation of longitudinal waves are important parameters. Values for these quantities found in the literature were not appropriate. Therefore, for cross-linked polyethylene (XLPE) and cured liquid silicone rubber (LSR), the longitudinal wave velocity and the attenuation were evaluated in the temperature interval from -20°C to 50°C and in the frequency range from 200 kHz to 600 kHz using a two-sample ultrasound technique. The loss factor was determined from these measured quantities. Additionally, low frequency Dynamic Mechanical Thermal Analysis (DMTA) was applied to investigate LSR and XLPE in a temperature interval between -100 and 50°C and to check qualitatively the ultrasound data.
The temperature dependences of dielectric permittivity and elastic modulus of poly(vinylidene fluoride - hexafluoropropylene) (P(VDF-HFP)) are compared and explained by use of structural data obtained by differential scanning calorimetry and X-ray analysis. Special emphasis is put on the effect of uniaxial stretching which renders the polymer ferroelectric. It is shown that dielectric and mechanical relaxations at the glass transition (aa relaxation) are closely related and not significantly affected by stretching. It is further confirmed that stretching destroys the non-polar spherulitic crystalline structure and produces relatively small-sized polar crystallites. This manifests in the disappearence of the so-called ac relaxation which is associated to molecular motions within the spherulitic crystalline lamellae. However, there are discrepancies between dielectric and mechanical losses above the glass transition which point towards a still not described structural transition.
Today rubber is due to its unique property profile one of the most important materials for the production of bearings, dampers or also tires and tubes. In the production of rubber goods a chemical cross-linking reaction (vulcanisation) generates the final material properties. This process takes place during the shape giving of the rubber compound in the mould and can proceed for several minutes. The cross-linking process is influenced by the mixture of the basic polymer, the cross-linking agent, the influence of catalysts and inhibitors and especially the processing conditions. The quality of every ingredient, the reproducibility of the mixing ratio, the homogeneity of the mixture and the accurateness in temperature control can have a direct influence on the cross linking reaction. To control the quality of a rubber compound and verify the processing conditions in industry moving die rheometers, named curemeter, are involved in the production process. Starting from our experience in cure monitoring of thermosetting materials by measuring ultrasound velocity in the mould we extended the measuring principle to rubber vulcanisation monitoring. After first investigations using a compression mould we dealt here with on-line monitoring of vulcanisation in an injection moulding process which is one of the most used techniques in rubber industry.
Rubbers are often used for seal applications due to their special material properties and easy use. In many applications the material is exposed to low temperatures during Operation. Therefore it is important to know the material behavior at low temperatures to determine the temperature ränge that allows a Safe Operation of the seal, e.g. in storage and transport Containers for radioactive materials.
The seal function of an elastomer is limited in temperature by the rubber-glass transition during which the material properties change from rubber-like to stiff and glass-like. For a given application this correlation is not trivial and therefore needs an in-depth investigation under consideration of the physical properties and the
application conditions.
In this work different analytical methods are used to characterize the material behavior at low temperature in the ränge of the glass-rubber-transition and are compared with the quality of Operation of a component which is here defined by the detected leakage rate.
In consideration of the influence of the curing reaction on the material properties of elastomers, it is very important to control the vulcanization process properly.
As shown previously [1], the effects of the vulcanization reaction of an elastomer can be monitored by use of ultrasonic sound waves. This technique has to a certain degree a high similarity to the standard curemeter test according to ISO 6502 but can be applied also inside a production tool.
So far, the method was only applied to the vulcanization of one compound at a given temperature and sample thickness. This is now complemented with measurements on another compound system at different temperatures and sample thicknesses.
The expected effects of temperature and thickness on the curing behaviour were found by use of the ultrasound online control.
Monitoring the vulcanization of elastomers: Comparison of curemeter and ultrasonic online control
(2009)
The vulcanization of elastomeric materials has a high impact on the properties of the final product. Therefore, it is important to monitor and control this crosslinking process. A common technique to attain the necessary curing time is the use of a curemeter in accordance with ISO 6502 in order to determine the time for full cure of a sample with a standardized geometry. Based on this result and a lot of practical experience, the required curing time for a given product geometry is estimated. Within the scope of this work, a new analysis technique will be compared with the standard procedure. The ultrasonic online control employs ultrasound waves to measure the changes in material properties caused by vulcanization. For this study, a natural rubber compound with a conventional curing system was investigated by both techniques. It was found that the results of the ultrasonic technique show good agreement with the results of the curemeter.
The investigation of low temperature properties of elastomeric sealing materials by means of thermo-analytical methods is a sound way to get information about the glass transition process.
The breakdown temperature of the sealing function of O-ring seals was measured in a component test setup depending on material and degree of compression.
An in depth explanation of the observed component tests behaviour is currently in preparation. It requires the results of thermo-analytical methods and measurements as the compression set (not shown here). With that, a model was developed to describe the correlation between physical material parameters and observed component behaviour.