Filtern
Dokumenttyp
- Zeitschriftenartikel (9) (entfernen)
Sprache
- Englisch (9) (entfernen)
Referierte Publikation
- nein (9) (entfernen)
Schlagworte
- Compression set (1)
- Dynamic mechanical analysis (1)
- Elastomer (1)
- Fertigungskontrolle (1)
- Gelation (1)
- Injection moulding (1)
- Low temperature behaviour (1)
- Mould (1)
- Mould wall coupling (1)
- On-line monitoring (1)
- Qualitätssicherung (1)
- Rtm (1)
- Schallgeschwindigkeit (1)
- Sealing material (1)
- Sensors (1)
- Sound velocity (1)
- Thermoset (1)
- Thermoset manufacturing (1)
- Ultraschall (1)
- Ultrasonic (1)
- Ultrasound (1)
- Ultrasound sensors (1)
- Vernetzungsreaktion (1)
- Vitrification (1)
- Vulcanisation (1)
In processing fibre-reinforced composites, the curing reaction can be significantly retarded if the temperature and reaction time are not optimally set. In such situations, complete curing is sometimes impossible under practically relevant conditions. It is difficult for processors to recognize or detect incomplete curing. The equilibrium glass transition temperature plays an important role in complete curing in the production process.
Ultrasound on-line NDT methods have been demonstrated as a useful tool for monitoring the curing reaction of thermosets. In order to achieve this ultrasound sensors are incorporated into compression, injection and RTM (resin transfer) mould. For many commercial products imprints or any surface markings upon the moulded product are undesirable. Due to its physical properties ultrasound has a large advantage over other techniques for similar applications. The sound wave can pass through the wall of the mould and direct contact with the moulded part is not required. In this particular case one fundamental problem is a good coupling of the sensors to the mould wall. Several mediums came into question but because of the high technical (e. g. temperature and long time stability) and practical demands, it was decided that dry (non-fluid) coupling would be the most promising candidate. A handful of coupling foils suitable also at high temperatures and for long time application under industrial conditions were tested and are presented in this paper.
Ultrasound waves penetrate solid objects without damaging them. Their fields of application range from the imaging of internal organs in medicine, to interior testing of mechanical and chemical engineering components. However, ultrasonic systems can also be used to visualise the way the mechanical properties of reactive resins change during processing in the mould.
The curing conditions play an important role in the quality assurance of composite products.
Especially as composite materials are widely used in high tech areas so that they are required to fulfil high quality Standards. Some problems which occur during curing, for instance undercuring, can hardly be detected using Standard NDT investigations, mainly because they are manifested only at high temperatures, particularly close to glass-rubber-transition. On-line eure monitoring has the outstanding advantage that it can monitor the material parameters even at the highest temperatures possible.
In recent years eure monitoring with ultrasonic methods has become more populär. In comparison to dielectric methods mechanical parameters are measured directly. The quantities to be measured are the velocity and the attenuation of the sound wave. On this basis the storage and loss modulus can be calculated. Depending on the form of excitation with longitudinal or transversal waves these moduli are referred to as long wave or shear modulus.
Well developed Computer based technology and sensor materials are available in the non-destructive testing (NDT) market. The measuring equipment employed a commercial NDT System, which worked computer-aided. With a special Software the demands of automatic Operation under industrial conditions was accomplished. This measurement equipment was tested on composites. Its structure, performance and some practical results will be presented in the following paper.
Today rubber is due to its unique property profile one of the most important materials for the production of bearings, dampers or also tires and tubes. In the production of rubber goods a chemical cross-linking reaction (vulcanisation) generates the final material properties. This process takes place during the shape giving of the rubber compound in the mould and can proceed for several minutes. The cross-linking process is influenced by the mixture of the basic polymer, the cross-linking agent, the influence of catalysts and inhibitors and especially the processing conditions. The quality of every ingredient, the reproducibility of the mixing ratio, the homogeneity of the mixture and the accurateness in temperature control can have a direct influence on the cross linking reaction. To control the quality of a rubber compound and verify the processing conditions in industry moving die rheometers, named curemeter, are involved in the production process. Starting from our experience in cure monitoring of thermosetting materials by measuring ultrasound velocity in the mould we extended the measuring principle to rubber vulcanisation monitoring. After first investigations using a compression mould we dealt here with on-line monitoring of vulcanisation in an injection moulding process which is one of the most used techniques in rubber industry.
Elastomers are widely used as the main sealing materials for containers for low and intermediate level radioactive waste and as an additional component to metal seals in spent fuel and high active waste containers. The safe encapsulation of the radioactive container inventory has to be guaranteed according to regulation and appropriate guidelines for long term storage periods as well as for temperatures as low as -40°C during transport. Therefore, the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance. It is known that the material properties of elastomers are strongly temperature dependent. At low temperatures, this is caused by the rubber-glass transition (abbreviated: glass transition). During continuous cooling, the material changes from a rubber-like entropy elastic to a stiff energy elastic behaviour, which allows nearly no strain or retraction. Hence, rubbers are normally used above their glass transition, but the minimum working temperature limit is not defined precisely; this can cause problems during the above noted applications. Therefore, the lower operation temperature limit of elastomer seals must be determined in dependence of the material properties. Differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA) are combined with standardised measurements to determine the compression set according to ISO 815. To reduce the test time of the standard tests, a faster technique than normally used was developed. Additionally, the breakdown temperature of the sealing function of complete O ring seals was measured in a component test set-up to compare it with the results of the other tests. The experimental set-up is capable of measuring the leakage rate at low temperatures by the pressure rise method. A fluorocarbon rubber (FKM) was selected for this investigation as it is often used for radioactive waste containers. The materials (seals and test sheets) were purchased from a commercial seal producer.