A new method for the evaluation of the low temperature properties of rubber materials is presented. The method emulates the standardized compression set measurement, which is frequently used for sealing materials, but can be performed within a considerably shorter time. The results are compared with the standard test and found to be qualitatively the same. Slight differences are discussed on the basis of the differences in the measurement procedures. Further data evaluation is done by fitting functions to describe the material behaviour.
Non-destructive evaluation (NDE) of composites: using ultrasound to monitor the curing of composites
(2013)
Typical composite materials for lightweight construction consist of a fibre (glass or carbon) reinforced thermosetting matrix. The impregnation of the fabric is made with liquid resin – usually epoxy resin or unsaturated polyester resin are used. The main processing methods are resin transfer moulding (RTM) and prepreg technology often used in combination with autoclave curing. After shaping, the resin must be cured. The final properties of the produced parts depend on the curing degree and the final glass transition temperature. Analytical methods and the use of ultrasound for online cure monitoring in the manufacturing process are introduced. Examples for the application of ultrasonic cure monitoring for the production of composite parts for traffic systems are also covered.
The method for the determination of compression set values with a Dynamic Mechanical Analysis (DMA) setup at low temperatures, which was presented previously, allows a much faster and readily automated procedure than the standardized compression set test according to ISO 815-2. This method is applied to a series of different elastomeric materials that are commonly used for sealing applications. The results of the compression set test are compared with results from thermal analysis to allow an in depth comparison of the material behaviour at low temperatures.
Furthermore, a comparison between two EPDM materials is presented. These materials show very similar properties determined by thermo analytical methods such as Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) but differ clearly in their compression set behaviour. This comparison shows the importance and value of information of the compression set test in addition to thermal analysis to judge the behaviour of sealing materials and confirms the relevance of the new compression set test method for the investigation of low temperature properties of elastomers.
Elastomers are widely used as the main sealing materials for containers for low and intermediate level radioactive waste and as an additional component to metal seals in spent fuel and high active waste containers. The safe encapsulation of the radioactive container inventory has to be guaranteed according to regulation and appropriate guidelines for long term storage periods as well as for temperatures as low as -40°C during transport. Therefore, the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance. It is known that the material properties of elastomers are strongly temperature dependent. At low temperatures, this is caused by the rubber-glass transition (abbreviated: glass transition). During continuous cooling, the material changes from a rubber-like entropy elastic to a stiff energy elastic behaviour, which allows nearly no strain or retraction. Hence, rubbers are normally used above their glass transition, but the minimum working temperature limit is not defined precisely; this can cause problems during the above noted applications. Therefore, the lower operation temperature limit of elastomer seals must be determined in dependence of the material properties. Differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA) are combined with standardised measurements to determine the compression set according to ISO 815. To reduce the test time of the standard tests, a faster technique than normally used was developed. Additionally, the breakdown temperature of the sealing function of complete O ring seals was measured in a component test set-up to compare it with the results of the other tests. The experimental set-up is capable of measuring the leakage rate at low temperatures by the pressure rise method. A fluorocarbon rubber (FKM) was selected for this investigation as it is often used for radioactive waste containers. The materials (seals and test sheets) were purchased from a commercial seal producer.
The temperature dependences of dielectric permittivity and elastic modulus of poly(vinylidene fluoride - hexafluoropropylene) (P(VDF-HFP)) are compared and explained by use of structural data obtained by differential scanning calorimetry and X-ray analysis. Special emphasis is put on the effect of uniaxial stretching which renders the polymer ferroelectric. It is shown that dielectric and mechanical relaxations at the glass transition (aa relaxation) are closely related and not significantly affected by stretching. It is further confirmed that stretching destroys the non-polar spherulitic crystalline structure and produces relatively small-sized polar crystallites. This manifests in the disappearence of the so-called ac relaxation which is associated to molecular motions within the spherulitic crystalline lamellae. However, there are discrepancies between dielectric and mechanical losses above the glass transition which point towards a still not described structural transition.
Rubber is widely used as sealing material in various applications. In many fields the sealing function at low temperatures is necessary. Therefore the understanding of failure mechanisms is of high importance. Rubbers are normally used above their glass-rubber transition region but the minimum working temperature limit is not defined precisely. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties. The results of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are combined with the results of the standardized compression set according to ISO 815 respectively a modified test using the DMA equipment.