Partial discharges may cause damage to electrical insulation of high voltage equipment. They initiate elastic waves in the insulating material, e.g. in the stress cone of an outdoor termination. Localisation of the origin of such elastic waves can help to predict serious damaging processes in the electrical insulation. In order to measure and evaluate the wave propagation effects in typical multilayered elastomeric structures, knowledge of the material properties is required. The propagating velocity and the attenuation of longitudinal waves are important parameters. Values for these quantities found in the literature were not appropriate. Therefore, for cross-linked polyethylene (XLPE) and cured liquid silicone rubber (LSR), the longitudinal wave velocity and the attenuation were evaluated in the temperature interval from -20°C to 50°C and in the frequency range from 200 kHz to 600 kHz using a two-sample ultrasound technique. The loss factor was determined from these measured quantities. Additionally, low frequency Dynamic Mechanical Thermal Analysis (DMTA) was applied to investigate LSR and XLPE in a temperature interval between -100 and 50°C and to check qualitatively the ultrasound data.
In processing fibre-reinforced composites, the curing reaction can be significantly retarded if the temperature and reaction time are not optimally set. In such situations, complete curing is sometimes impossible under practically relevant conditions. It is difficult for processors to recognize or detect incomplete curing. The equilibrium glass transition temperature plays an important role in complete curing in the production process.
Vernetzen statt Verglasen
(2000)
In recent years eure monitoring with ultrasonic methods became more important. An on-line measurement System for industrial applications is presented in this paper. It operates in through-transmission and the measured parameters are the sound velocity and the attenuation of the sound wave. An objective of this paper is to establish the ränge of possible applications for an ultrasonic eure monitoring System.
The application of microwave measurements to the characterisation of rubber compounds vulcanisation is considered. The behaviour of mechanical and microwave (20 GHz) dielectric parameters during vulcanisation was investigated for rubber compounds with different concentrations of active and non-active carbon black. An increase of concentration or activity of carbon black results in the increase of both dielectric permittivity ε?(T) and loss ε?(T) and in the increase of torsion modulus as well. The start of the vulcanisation reaction is indicated by an increase of dielectric permittivity and torsion modulus in all investigated unvulcanised compounds with carbon black. While for compounds with non-active carbon black the vulcanisation can be better indicated by the ε?(T) anomaly, for compounds with active carbon black it is more clearly seen by the change of ε?(T) behaviour.