We report on the use of a sprayable and thermogelating biomaterial (Poloxamer; a.k.a. Pluronic) in optical imaging of pH values, local oxygen and temperature. The material is highly biocompatible and easy to handle. We also show that the material is well permeable to oxygen (thus making it a good choice for use in oxygen sensors), and is stable in liquid solution and at elevated temperature. We demonstrate its applicability in optical sensors for oxygen, pH and temperature. This was accomplished by incorporating appropriate luminescent probes in various kinds of microparticles (which act as hosts for the probes and prevent dye leaching and aggregation), and then dispersing the microparticles in the thermogelating polymer. The resulting sensor gels were deposited on the surface of interest via spraying at temperatures of <20 °C. At these temperatures, the gels adhere well to the target, even on uneven surfaces such as skin, wounds, and bacterial cultures. If temperature is risen to above 25 °C, the gels form a thin and soft but solid sensing layer which, however, can be simply removed from surface of interest by cooling and wiping it off, or by washing with water. Sprayable thermogelating sensors present obvious advantages over other sensors by not causing damage to the surface of interest. In our perception, the sensing materials also have wide further applicability in sensors for other species including clinically relevant gases, enzyme substrates (such as glucose or lactate) and ions.
A strongly fluorescent organic semiconducting polymer doped with a highly
temperature dependent fluorescent europium(III) complex is converted into a
nanosized material that is capable of optically sensing temperature (T) in the
range from 0 to 50 °C via two-photon excitation at 720 nm. The nanosensors
are prepared from a blue-fluorescent polyfluorene that acts as both a lightharvesting
antenna (to capture two-photon energy) and an energy donor in a
fluorescence resonance energy transfer (FRET) system. The photonic energy
absorbed by the polymer is transferred to the T-sensitive red-luminescent
europium complex contained in the nanoparticles. The close spatial proximity
of the donor and the acceptor warrants efficient FRET. A poly(ethylene glycol)-
co-poly(propylene oxide) block copolymer is also added to render the particles
biocompatible. It is shown that T can be calculated from a) the intensity of
the luminescence of the europium complex, b) the ratio of the intensities of
the red and blue luminescence, or c) the T-dependent luminescence lifetime
of the Eu(III) complex.
We present a systematic study on the effect of surface ligands on the luminescence properties and colloidal stability of β-NaYF4:Yb3+,Er3+ upconversion nanoparticles (UCNPs), comparing nine different surface coatings to render these UCNPs water-dispersible and bioconjugatable. A prerequisite for this study was a large-scale synthetic method that yields ~2 g per batch of monodisperse oleate-capped UCNPs providing identical core particles. These ~23 nm sized UCNPs display an upconversion quantum yield of ~0.35% when dispersed in cyclohexane and excited with a power density of 150 W cm-2, underlining their high quality. A comparison of the colloidal stability and luminescence properties of these UCNPs, subsequently surface modified with ligand exchange or encapsulation protocols, revealed that the ratio of the green (545 nm) and red (658 nm) emission bands determined at a constant excitation power density clearly depends on the surface chemistry. Modifications relying on the deposition of additional (amphiphilic) layer coatings, where the initial oleate coating is retained, show reduced non-radiative quenching by water as compared to UCNPs that are rendered water-dispersible via ligand exchange. Moreover, we could demonstrate that the brightness of the upconversion luminescence of the UCNPs is strongly affected by the type of surface modification, i.e., ligand exchange or encapsulation, yet hardly by the chemical nature of the ligand.