Open Access

Clustering of magnetic nanoparticles can drastically change their collective magnetic properties, which in turn may influence their performance in technological or biomedical applications. Here, we investigate a commercial colloidal dispersion (FeraSpinTMR), which contains dense clusters of iron oxide cores (mean size around 9 nm according to neutron diffraction) with varying cluster size (about 18–56 nm according to small angle x-ray diffraction), and its individual size fractions (FeraSpinTMXS, S, M, L, XL, XXL). The magnetic properties of the colloids were characterized by isothermal magnetization, as well as frequency-dependent optomagnetic and AC susceptibility measurements. From these measurements we derive the underlying moment and Relaxation frequency distributions, respectively. Analysis of the distributions shows that the clustering of the initially superparamagnetic cores leads to remanent magnetic moments within the large clusters. At frequencies below 105 rad s−1, the relaxation of the clusters is dominated by Brownian (rotation) relaxation. At higher frequencies, where Brownian relaxation is inhibited due to viscous friction, the clusters still show an appreciable magnetic relaxation due to internal moment relaxation within the clusters. As a result of the internal moment relaxation, the colloids with the large clusters (FSL, XL, XXL) excel in magnetic hyperthermia experiments.

Electrochromic thin films of metallo-supramolecular polyelectrolytes based on Fe(OAc)2 and 1,4-bis(2,2':6',2''-terpyridin-4'-yl)benzene are readily prepared by layer-by-layer (LbL) deposition or dip-coating on transparent conducting electrode surfaces. By applying a potential, we can switch the color of the films from blue to colorless. Because of the strong absorption and the fast switching speed, the color change can be observed with the eye. The devices show reversible switching and cycle stability.

Flexible electrochromic devices (ECDs) based on Fe(II)-metallo-supramolecular polyelectrolytes (Fe-MEPE) and vanadium oxide are studied in operando by means of x-ray absorption fine structure (XAFS) spectroscopy. The ECDs are blue-purple in the colored state at 0.0 V and become light yellow when a voltage of 1.6 V is applied. The XAFS studies at the K-edge of Fe(II) reveals that the absorption edge is shifted toward higher energies by 1.8 eV in the transparent state. Comparison of two different ECDs and different charge cycles demonstrates the reversibility and repeatability of the process. We attribute the shift to a charge transfer and a change of oxidation state of the ions from Fe2+ to Fe3+. The transition is not accompanied by a noticeable structural change of the octahedral coordination geometry as confirmed by analysis of the extended x-ray absorption fine structure (EXAFS) data. (C) 2015 Elsevier B.V. All rights reserved.

With the increase in the awareness of the public in the environmental impact of oil shale utilization, it is of interest to reveal the mobility of potentially toxic trace elements in spent oil shale. Therefore, the Cr and As oxidation state in a representative Jordanian oil shale sample from the El-Lajjoun area were investigated upon different lab-scale furnace treatments. The anaerobic pyrolysis was performed in a retort flushed by nitrogen gas at temperatures in between 600 and 800 °C (pyrolytic oil shale, POS). The aerobic combustion was simply performed in porcelain cups heated in a muffle furnace for 4 h at temperatures in between 700 and 1000 °C (burned oil shale, BOS). The high loss-on-ignition in the BOS samples of up to 370 g kg–1 results from both calcium carbonate and organic carbon degradation. The LOI leads to enrichment in the Cr concentrations from 480 mg kg–1 in the original oil shale up to 675 mg kg–1 in the ≥850 °C BOS samples. Arsenic concentrations were not much elevated beyond that in the average shale standard (13 mg kg–1). Synchrotron-based X-ray absorption near-edge structure (XANES) analysis revealed that within the original oil shale the oxidation states of Cr and As were lower than after its aerobic combustion. Cr(VI) increased from 0% in the untreated or pyrolyzed oil shale up to 60% in the BOS ash combusted at 850 °C, while As(V) increased from 64% in the original oil shale up to 100% in the BOS ash at 700 °C. No Cr was released from original oil shale and POS products by the European compliance leaching test CEN/TC 292 EN 12457-1 (1:2 solid/water ratio, 24 h shaking), whereas leachates from BOS samples showed Cr release in the order of one mmol L–1. The leachable Cr content is dominated by chromate as revealed by catalytic adsorptive stripping voltammetry (CAdSV) which could cause harmful contamination of surface and groundwater in the semiarid environment of Jordan.

The photocatalytic (PC) performance of titanium dioxide (TiO2) nanoparticles strongly depends on their specific surface, the presence of crystal defects, their crystal phase, and the exposed crystal facets. In order to understand which of these factors contributes most significantly to the PC activity of TiO2 colloids, all of them have to be individually analyzed. This study entails the synthesis of five anatase nanocrystal samples. By maintaining the same reactant ratios as well as hydrothermal sol–gel synthesis route and only varying the autoclaving time or temperature, different crystallite sizes are obtained under comparable experimental conditions. A decrease in PC performance with increase in specific surface area is found. Such an unexpected counterintuitive result establishes the basis for a better understanding of the crucial factors that ultimately determine the PC activity. These are investigated by studying nanocrystals bulk and surface structure and morphology using a selection of complementary analysis methods (X-ray photoelectron spectroscopy (XPS), X-ray absorption fine structure (XAFS), X-ray diffraction (XRD)…). It is found that a change in the nanocrystal morphology from an equilibrium state truncated tetragonal bipyramid to a more elongated rod-like structure accompanied by an increase in oxygen vacancies is responsible for an augmented PC activity of the TiO2 nanocrystals.