Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (50)
- Zeitschriftenartikel (46)
- Vortrag (18)
- Beitrag zu einem Sammelband (14)
- Forschungsbericht (4)
- Corrigendum (1)
Schlagworte
- Geokunststoffe (25)
- Deponieverordnung (18)
- BAM-Zulassung (8)
- Kunststoffdichtungsbahnen (8)
- Geosynthetics (6)
- Kunststoff-Dränelemente (6)
- Deponie (5)
- Durability (5)
- Scherfestigkeit (5)
- Deponieabdichtungen (4)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (18)
An approach to achieve “zero leakage” is discussed with respect to the experience in Germany, where strict regulations for landfill lining and capping systems have been developed and issued because of large environmental problems related to landfills that accumulated in the 1970’s and 1980’s. Using a thick, high quality HDPE geomembrane (GMB), which is installed free of residual waves and wrinkles in intimate contact with a compacted clay liner (CCL) or geosynthetic clay liner (GCL) of very low permeability, by a qualified, experienced, well equipped and properly third-party controlled installer and which are protected by heavy protection layers designed with respect to long-term performance of the GMB, may result in a liner or capping system of practically no leakage. This is demonstrated by analyzing results of measurements obtained from permanently installed leak detection systems in combination with HDPE GMBs. The survey is based on 32 German landfills with 1,276,500 m² of installed HDPE GMB.
In diesem Beitrag soll in Kürze darüber informiert werden, welche Themen und Fragestellun-gen den Fachbeirat der BAM, seine Arbeitsgruppen und die BAM beschäftigt haben. Bereits in den letzten Jahren wurde an dieser Stelle über die Anforderungen an Kunststoff Drän-elemente berichtet. Vor dem Hintergrund unserer Beiträge zu diesem Thema, kam eine in-tensive Fachdiskussion im Fachbeirat der BAM und in weiteren Fachgremien in Gang. So wurden die Bemessungsgrundsätze der DGGT (Deutsche Gesellschaft für Geotechnik), die GDA (Geotechnik der Deponien und Altlasten) E (Empfehlung) 2-20 (Entwässerungsschich-ten in Oberflächenabdichtungssystemen), in einigen Punkten angepasst. Eine Musterverle-geanleitung für Kunststoff Dränelemente wurde erarbeitet. Der aktuelle Bearbeitungsstand soll hier vorgestellt werden. In diesem Zusammenhang wurde ein Untersuchungsprogramm zum Einfluss von Überlappstößen auf das Wasserableitvermögen von Kunst-stoff Dränelementen angestoßen. Die Ergebnisse sollen hier in Kürze vorgestellt und die Bedeutung für die Abminderungsfaktoren und damit für die Bemessung erläutert werden. Zu welchem Zeitpunkt muss ein Kunststoff Dränelement überbaut werden und welche weiteren Regelungen müssen hier beachtet werden? Was steckt eigentlich hinter diesen strengen Regelungen? Diese Fragen sollen im Folgenden diskutiert werden.
Die Deponieverordnung (DepV) fordert eine Akkreditierung der fremdprüfenden Stellen nach verschiedenen Normen. Die fachlichen Anforderungen an den „Fremdprüfer-Kunststoff“ legt die Richtlinie Fremdprüfer der BAM fest. Um diese Anforderungen im Akkreditierungsprozess ausreichend berücksichtigen zu können, wurde nun eine sogenannte DAkkS Regel erarbeitet, die die Anforderungen der Richtlinie spiegelt. Über den aktuellen Bearbeitungsstand soll berichtet werden.
Auch über die aktuelle Arbeit in Zusammenhang mit den Kunststoffdichtungsbahnen (KDB) soll berichtet werden. Der Prüfhinweis B14 (Bestimmung der Maßhaltigkeit von geosyntheti-schen Dichtungsbahnen aus Polyethylen hoher Dichte (PEHD)) wurde überarbeitet. Voran-gegangen war eine intensive Entwicklung der Prüfeinrichtung sowie ausgiebige Ringversuche im AK GWS (Arbeitskreis Grundwasserschutz). In diesem Zusammenhang wurden neue Anforderungen an die Produkte gestellt. Die Hintergründe dazu sollen kurz vorgestellt werden. Die DVS (Deutscher Verband für Schweißen und verwandte Verfahren) Richtlinie 2225-4 regelt das Schweißen der KDB auf der Deponiebaustelle. Werden KDB im strukturierten Bereich miteinander verschweißt, werden die Strukturen in der Regel vorher abgetragen. Die DVS Richtlinie 2225-4 sieht unter bestimmten Voraussetzungen von einem Abtragen der Strukturen ab. Vor diesem Hintergrund wurde ein Untersuchungsprogramm initiiert, das die Auswirkungen aufzeigen soll. Der Bearbeitungsstand wird vorgestellt.
Testing of the oxidative resistance of polyolefin based geosynthetics in
autoclaves at high oxygen pressure has been suggested as an alternative method to
conventional forced-air oven aging. The intention is to shorten considerably the testing
time and to ensure that aging is performed under the condition of rate-controlled
and not diffusion-limited oxidation. We compare data from high pressure autoclave
tests (HPAT) with data from oven aging and water immersion tests at 80 °C. For this,
the stabilization of the samples has to be taken into account. Polyolefin based geosynthetics
are usually stabilized by two types of “packages” of antioxidants (AO), designated
here as P1 and P2. P1 consists of phenols and phosphites, P2 of hindered amine
stabilizers (HAS) in addition to a marginal stabilization P1 of the resin for the manufacturing
process. Phenolic and phosphite AO are quickly consumed in the HPAT.
Failure time is tremendously reduced compared to forced-air oven aging or water
immersion. The results are discussed within the framework of a basic autoxidation
scheme (Wise et al., 1997). The reduction is much greater than expected from theoretical
considerations. Therefore, a direct and degrading reaction of oxygen with the AO
has to be assumed. In case of HAS, the time dependence of the degradation of tensile
properties in the HPAT is significantly different from the dependence observed in
conventional forced-air oven aging and their effectiveness is likewise strongly reduced.
A conclusive interpretation of HPAT results needs a better understanding of
what happens to the AO at high oxygen pressure.
An approach to achieve 'zero leakage' is discussed with respect to experience in Germany, where strict regulations for landfill lining and capping Systems have been developed and issued because of large environmental Problems related to landfills that accumulated in the 1970s and 1980s. Using a thick, high-quality high-density Polyethylene (HDPE) geomembrane (GM) that is installed free of residual waves and wrinkles in intimate contact with a compacted clay liner or geosynthetic clay liner of very low permeability, by a qualified, experienced, well-equipped and properly third-party-controlled installer, and which is protected by heavy protection layers designed with respect to the long-term performance of the GM may result in a liner or capping system of practically no leakage. This is demonstrated by analysing results of measurements obtained from permanently installed leak-detection Systems in combination with HDPE GMs. The survey was based on 32 German landfills with 1.276.500 m² of installed GMs.
Accurate and reproducible measurement of the structure and properties of high-value nanoparticles is extremely important for their commercialization. A significant proportion of engineered nanoparticle systems consist of some form of nominally core-shell structure, whether by design or unintentionally. Often, these do not form an ideal core-shell structure, with typical deviations including polydispersity of the core or shell, uneven or incomplete shells, noncentral cores, and others. Such systems may be created with or without intent, and in either case an understanding of the conditions for formation of such particles is desirable. Precise determination of the structure, composition, size, and shell thickness of such particles can prove challenging without the use of a suitable range of characterization techniques. Here, the authors present two such polymer core-shell nanoparticle systems, consisting of polytetrafluoroethylene cores coated with a range of thicknesses of either polymethylmethacrylate or polystyrene. By consideration of surface energy, it is shown that these particles are expected to possess distinctly differing coating structures, with the polystyrene coating being incomplete. A comprehensive characterization of these systems is demonstrated, using a selection of complementary techniques including scanning electron microscopy, scanning transmission electron microscopy, thermogravimetric analysis, dynamic light scattering, differential centrifugal sedimentation, and X-ray photoelectron spectroscopy. By combining the results provided by these techniques, it is possible to achieve superior characterization and understanding of the particle structure than could be obtained by considering results separately.
This is a corrigendum to the original article "Determining the thickness and completeness of the shell of polymer core-shell nanoparticles by X-ray photoelectron spectroscopy, secondary ion mass spectrometry, and transmission scanning electron microscopy" that was published in "The journal of physical chemistry C", vol. 123 (2019), no. 49 pp. 29765-29775.
The fluorolytic sol–gel synthesis is applied with the intention to obtain two different types of core–shell nanoparticles, namely, SrF2–CaF2 and CaF2–SrF2. In two separate fluorination steps for core and shell formation, the corresponding metal lactates are reacted with anhydrous HF in ethylene glycol. Scanning transmission electron microscopy (STEM) and dynamic light scattering (DLS) confirm the formation of particles with mean dimensions between 6.4 and 11.5 nm. The overall chemical composition of the particles during the different reaction steps is monitored by quantitative Al Kα excitation X-ray photoelectron spectroscopy (XPS). Here, the formation of stoichiometric metal fluorides (MF2) is confirmed, both for the core and the final core–shell particles. Furthermore, an in-depth analysis by synchrotron radiation XPS (SR-XPS) with tunable excitation energy is performed to confirm the core–Shell character of the nanoparticles. Additionally, Ca2p/Sr3d XPS intensity ratio in-Depth profiles are simulated using the software Simulation of Electron Spectra for Surface Analysis (SESSA). In principle, core–shell like particle morphologies are formed but without a sharp interface between calcium and strontium containing phases.
Surprisingly, the in-depth chemical distribution of the two types of nanoparticles is equal within the error of the experiment. Both comprise a SrF2-rich core domain and CaF2-rich shell domain with an intermixing zone between them. Consequently, the internal morphology of the final nanoparticles seems to be independent from the synthesis chronology.
Bei den von der Bundesanstalt für Materialforschung und ‐prüfung (BAM) zugelassenen Kunststoff‐Dränelementen sind drei verschiedene Varianten von überlappenden Querstößen nach den Einbauanleitungen zulässig. Das Wasserableitvermögen innerhalb dieser Querstöße wurde vom SKZ – Das Kunststoffzentrum und von der KIWA Deutschland GmbH in Abstimmung mit der BAM gemessen. Dabei zeigte sich bei den gewählten Prüfbedingungen (einem hydraulischer Gradienten i = 1, Auflasten von 20 und 50 kPa sowie den Bettungen hart/weich und weich/weich) praktisch keine Verringerung gegenüber dem Wasserableitvermögen im Kunststoff‐Dränelement selbst. Eine solche war insbesondere dann nicht zu beobachten, wenn die Dränkerne im Überlappungsbereich direkt aufeinandergelegt wurden (Variante A). Werden die Kunststoff‐Dränelemente als Ganzes entweder dachschindelartig hinsichtlich der Strömungsrichtung (Variante B) oder in einer gerade umgekehrten Anordnung (Variante C) übereinandergelegt, so genügt dabei eine Überlappungslänge von 20 cm, damit ausreichend Wasser durch die zwischen den Dränkernen liegende Trennschicht aus Filter‐ und Trägergeotextil strömt. Der bisher in der GDA‐Empfehlung E2‐20 für die Bemessung angesetzte Abminderungsfaktor von 1,2 für Querstöße kann daher für die hier untersuchten, zugelassenen Produkte bei einer genügend großen Überlappung entfallen. Entsprechende Hinweise werden zukünftig in den Zulassungsscheinen gegeben.