Tribofilms formed during dry sliding usually exhibit a nanocrystalline structure and complicated composition. In the present study, tribofilms consisting mainly of a solid lubricant, namely graphite nanoparticles, are considered. Systems providing such tribofilms are candidates for anti-friction applications. Since sliding action always leads to mixing of the materials at both sides of the tribological interface, it was of major interest to study the impact of different amounts of a hard constituent, SiC in the considered case, within the soft matrix systematically. Furthermore, the impact of normal pressure was considered. A mechanically mixed layer was observed for the whole range of normal pressures and SiC volume fractions. The calculated coefficient of friction decreased significantly with increasing thickness of this layer but was only marginally affected by SiC volume fraction, which is good news for anti-friction applications.
The resistance of structural steels against corrosion in CO2-H2O and CO2-H2O-O2
atmospheres at temperatures above 550°C was observed with high magnification methods.
The test atmosphere is the basic composition of an oxyfuel coal combustion atmosphere. The
analytical information base was applied to develop reaction schemes for the oxidation of
steels. It was demonstrated that the formation of phases and the kinetics of oxidation reactions
in this atmospheres is affected by the formation of intermediate iron hydroxide and a high
carbon activity. In the temperature regime above 550°C the thermal equilibrium between H2O,
CO2 and Fe reacted and formed CO. CO triggers the formation of FeO and carbides and
increases the reaction kinetics. Porosity at the interface is established by gaseous phases
such as Fe(OH)2 or H2O. H2 formation is not limited to the steel - oxide interface but can occur
in the whole oxide scale. Examples of the experimental results were compared with a
thermodynamic approach. The objective of the work was to derive qualitative rules of the basic
corrosion reactions.
Heat accumulation induced by a succession of railway brakings leads to changes of the friction conditions occurring in pad-disc contact. Infrared thermography observations show a progressive increase of surface temperature over the succession, as well as a modification of the hot band migration phenomenon. From a tribological point of view, the heat accumulation, accompanied by a wear increase, progressively modifies the friction behaviour from one braking to the next. Post-mortem observations of pads are performed on surface by scanning electron microscopy and in depth after Focus Ion Beam cut by scanning ion microscopy. Observations show that, with heat accumulation, the third body quantity rises inside the contact, in accordance with wear increase. It is concluded that source flows of third body, which increase with temperature, feed aplenty the contact and modify its load-bearing capacity.