Filtern
Erscheinungsjahr
- 2018 (3)
- 2017 (4)
- 2016 (17)
- 2015 (9)
- 2014 (7)
- 2013 (8)
- 2012 (9)
- 2011 (6)
- 2010 (6)
- 2009 (9)
- 2008 (11)
- 2007 (2)
- 2006 (4)
- 2005 (2)
- 2004 (12)
- 2003 (1)
- 2002 (13)
- 2001 (9)
- 2000 (5)
- 1999 (4)
- 1998 (3)
- 1997 (6)
- 1996 (12)
- 1995 (8)
- 1994 (4)
- 1993 (2)
- 1992 (4)
- 1991 (3)
- 1990 (4)
- 1989 (1)
- 1988 (2)
- 1987 (1)
- 1986 (2)
- 1984 (4)
- 1983 (6)
- 1981 (2)
- 1977 (1)
Dokumenttyp
- Zeitschriftenartikel (128)
- Beitrag zu einem Tagungsband (34)
- Beitrag zu einem Sammelband (31)
- Vortrag (6)
- Buchkapitel (2)
- Forschungsbericht (2)
- Dissertation (1)
- Sonstiges (1)
- Posterpräsentation (1)
Sprache
- Englisch (153)
- Deutsch (48)
- Mehrsprachig (5)
Schlagworte
- Third body (13)
- Tribofilm (13)
- TEM (10)
- Friction (8)
- Nanoparticles (8)
- Friction layer (6)
- Sliding simulation (6)
- FIB (5)
- Movable cellular automata (5)
- Nanostructure (5)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (6)
Optical and electron metallography have been used to investigate the development of different microstructures in Armco Fe after rolling reductions between 0 and 90%. Simultaneously, the orientation distribution functions have been calculated from pole figures obtained by X-ray diffraction. Different stages of texture development could be assigned to typical microstructures. Strain inhomogeneities, such as microbands and shear bands, caused some broadening of the texture and a slight deviation of one skeleton line from the predicted fibre texture component. The decomposition of orientations near {111} < 121 > , and the strengthening of {211} < 011 > after high rolling reductions, was not due to mechanical twinning but could rather be explained by assuming {211} < 111 > slip. 30 ref.--AA
The formation of a third body layer on a conventional friction material during braking tests was studied in some detail using TEM, SEM, and X-ray photoelectron spectroscopy (XPS) techniques. Plate shaped micro-contact areas representing a compositional mix of all components of the tribocouple and exhibiting a nanocry stalline microstructure were identified after a run-in period.
Die volle Leistung einer auf Reibung basierenden Bremse wird erst nach einem Einlaufvorgang erreicht. Dieser ist notwendig, um auf Belag und Scheibe eine sogenannte Reibschicht aufzubauen. Da diese Zwischenschicht das Reibungsverhalten des Systems maßgeblich bestimmt, ist es wichtig, sich Klarheit über ihre chemische Zusammensetzung, Mikrostruktur und die daraus resultierenden Eigenschaften zu verschaffen.
Als Basismaterial diente ein phenolharzgebundener Belag Jurid 57-62, der mit verschiedenen Parametern (Flächenpressung und Umdrehungsgeschwindigkeit) gegen eine Stahlscheibe getestet wurde. Es wurden Dauerbremsungen von jeweils einer Stunde bzw. bis zu einem maximalen Belagverschleiß von 1 mm simuliert, wobei die Entwicklung der Reibzahl und die Oberflächentemperatur der Scheibe registriert wurde.
Zur Analyse der Reibschichten auf dem Bremsbelag wurden mehrere Methoden parallel angewandt. So wurden Verschleißpartikel, die aus der Reibschicht stammen, gesammelt bzw. abgekratzt und nach Dispergieren auf Kohlefolien direkt im Transmissionselektronenmikros-kop (TEM) untersucht. Ferner wurden von einigen ausgesuchten Belagproben Mikrotom-schnitte sowie dünne Querschnittsfolien für die TEM-Untersuchung präpariert, um den Verbund Reibschicht-Grundmaterial darstellen zu können. Als Ergänzung wurden ferner oberflächenmorphologische und –analytische Verfahren wie REM/EDX und ESCA eingesetzt.
Die Ergebnisse deuten darauf hin, dass die Reibschicht nanokristallin ist, und dass fast alle anorganischen Bestandteile des Bremsbelags sowie Eisenoxid von der Bremsscheibe in sehr fein verteilter Form vorliegen. Bei Belägen ohne Metallanteil bildet eine Barium-Eisen-Sulfatphase offenbar die Grundstruktur der Reibschicht, während auf eisenhaltigen Belägen Eisenoxid dominierend ist. Die nanokristalline Mikrostruktur entsteht, ähnlich wie beim mechanischen Legieren, durch einen Mahlvorgang von Verschleißpartikeln zwischen den Reibpartnern. Bei Überlastung des Belags tritt Zersetzung der Polymer-Bindephase ein, was zu einem raschen Anstieg der Verschleißrate führt.
A rather new tool, the focused ion beam (FIB) technique, was used to characterise superficial layers at micro-contact areas of a commercial brake pad. The friction material was a polymer matrix composite (PMC) with approximately 50% metal content (semi-metallic) and the counter part was a cast iron rotor. Though the contact areas were not visible as topographic features, they could be identified with the aid of their increased secondary electron emission during FIB-scanning of the surface after tribological activation. Target preparation of micron-sized cross-sections with the FIB enabled the study of superficial layers at predetermined sites at high magnification.
Depending on the constituent of the pad, one, two or three layers were identified. The three layer structure comprised: (i) a 100 nm thick friction film containing nanocrystalline metal oxides and an amorphous phase which was enriched with sulphur, (ii) a nanocrystalline friction layer of compacted wear debris accommodating surface roughness and (iii) a severely deformed layer if the supporting constituent was a metal particle. Though the majority of loose wear particles was iron oxide, the friction film which adhered tightly to the pad surface contained a large amount of copper and sulphur, whereas zinc was transferred to the cast iron rotor.
The surfaces of a brake pad and rotor were investigated after a run-in period during which a stable coefficient of friction had developed. The Focused Ion Beam Technique (FIB) was used to reveal tribologically induced surface films and for cross-sectional preparation of superficial layers. Additional information was obtained by TEM/EDS of thin lamellae prepared with the FIB and by surface analytical methods (GDOS, XPS and RS). Microscopic contact areas of the pad showed bright contrast in Scanning Ion Microscopy (SIM). This was attributed to severe plastic deformation finally leading to a nanocrystalline microstructure. Metallic particles of the pad, the so-called primary contact areas, were mostly covered with a smooth oxide layer of less than 1 µm thickness. Above this layer a thin (100 nm) partly amorphous film was often observed. The film was not only restricted to the metal particles, but also spread over adjacent regions, suggesting that secondary plateaus had formed. Similar layers and films, although with slightly different composition and structure, were also observed at the surface of the rotor.
Patches of white etching layers on rail surfaces were investigated using sophisticated techniques like cross-sectional transmission electron microscopy (XTEM) and synchroton X-ray diffraction. Optical microscopy failed to resolve the microstructure, but in the TEM submicron grains with high dislocation densities and occasional twins, which are characteristic features of high carbon martensite, were observed. The martensitic structure was confirmed by evaluation of synchroton X-ray diffraction line profiles. The latter technique also allowed to determine dislocation densities of the order of 1012 cm-2 and residual compressive stresses of about 200 MPa.
Cross-sectional transmission electron microscopy, in combination with energy dispersive X-ray spectroscopy and focused beam microdiffraction, was applied to study the solid-state reactions taking place during contact formation of the system Ge(115 nm)/Pd(50 nm)In0.53Ga0.47As. In order to get information about the sequence of the different processes, rapid thermal, annealing experiments in the range 225400 °C were performed. The following features were observed: at 225 °C Pd reacted with the substrate forming the quaternary phase PdxIn0.53Ga0.47As (x 4), and with the Ge-layer forming mainly PdGe and Pd2Ge. Between PdxIn0.53Ga0.47As and In0.53Ga0.47As, a 5 nm thick amorphous Pd-In-Ga-As layer remained, indicating that the first reaction step was solid-state amorphization. After annealing at 350 °C, PdxIn0.53Ga0.47As disappeared and regrowth of In0.53Ga0.47As occured. Finally, at 400 °C, residual Ge from the amorphous top layer diffused to the interface and grew epitaxially on the regrown In0.53Ga0.47As, thus separating the IIIV compound semiconductor from the Pd-Ge reaction products. The interface remained flat, while only about 10 nm of the active In0.53Ga0.47As layer had been modified during the annealing processes.
Copper is a major ingredient in friction materials used for automotive braking. The purpose of this study was to find out how copper contributes to good brake performance properties in addition to providing good thermal conductivity. Microstructural investigations of copper chips at the surfaces of brake pads revealed a zone of severe plastic deformation which provides high hardness, but there is also evidence of recrystallized copper nano-particles which are incorporated into friction layers as soft ingredient once detached from the pad surface. Thus copper seems to play a dual role, firstly as reinforcing element of the brake pad providing primary contact sites, and secondly as solid lubricant by contributing to the formation of a layer of granular material providing velocity accommodation between the rotating disc and fixed pad. Confirmation for this hypothesis was obtained by modelling contact sites on the nanometre scale with the method of movable cellular automata. Results show both, the similarity of steel fibres and copper macro-particles in respect to providing primary contact sites, as well as similar sliding behaviours of friction layers containing either copper or graphite as soft inclusions. Furthermore, it is shown that not only material properties, but also the concentration of solid lubricant particles in the friction layers, determine conditions for friction force stabilization and smooth sliding behaviour.
The unique nanostructure formed during severe as well as moderate braking on the surface of brake discs was investigated by conventional and analytical Transmission Electron Microscopy. In both cases nanocrystalline magnetite mixed with carbon nanoinclusions and minor amounts of other pad constituents were identified. On the basis of these observations the friction performance of a single micro-contact was simulated with the method of Movable Cellular Automata. Inspite of a simplified nanostructure which was examined in two dimensions only, the calculated mean coefficient of friction fitted well to the value usually demanded for automotive braking. Furthermore, the model predicts that oxide films without soft nanoinclusions are not capable of providing smooth velocity accommodation at the pad–disc interface and thus lead to unstable friction behaviour.
Different, partly complementary and partly redundant characterization methods were applied to study the transition of magnetite, graphite and MoS2 powders to mechanically alloyed nanostructures. The applied methods were: Transmission electron microscopy (TEM), Mössbauer spectroscopy (MS), Raman spectroscopy (RS), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The main objective was to prepare a model material providing the essential features of a typical tribofilm forming during automotive braking, and to assess the impact of different constituents on sliding behaviour and friction level. Irrespective of the initial grain size, the raw materials were transferred to a nanocrystalline structure and mixed on a nanoscopic scale during high energy ball milling. Whereas magnetite remained almost unchanged, graphite and molybdenum disulphide were transformed to a nanocrystalline and highly disordered structure. The observed increase of the coefficient of friction was attributed to a loss of lubricity of the latter ingredient due to this transformation and subsequent oxidation.
The sliding behaviors of two simplified tribofilms with amorphous structure consisting either of SiO₂ molecules or C atoms were simulated by molecular dynamics modeling. The objective was to identify mechanisms explaining the experimentally observed lubricating properties of the two amorphous films. The impacts of layer thickness, normal pressure, temperature and different substrate materials were studied systematically, while the sliding velocity was kept constant at 30 m/s. While the layer thickness was not critical, all the other parameters showed special effects under certain conditions. Normal pressure impeded void formation and could even eliminate voids if applied at high temperature. Stick-slip sliding was changed to smooth sliding at high temperature due to void healing. Considering the carbon film, high friction forces and shearing of the entire film was observed with diamond substrates, whereas interface sliding at low friction forces and an amorphous layer of iron mixed with carbon was observed if the supporting substrates consisted of α-Fe. Both films show a decrease of friction forces and smooth sliding behavior at elevated temperature, corresponding well to the tribological behavior of and advanced nanocomposite sliding against a steel disc under severe stressing conditions when high flash temperatures can be expected.
XTEM and TFXRD investigations of ohmic Ti/Al/Ti/Au/WSiN contacts on AlGaN/GaN HFET layer systems
(2002)
The microstructural features of the high-temperature-stable ohmic contact system Ti/Al/Ti/Au/WSiN on AlGaN/GaN were investigated using analytical transmission electron microscopy and thin film x-ray diffraction. For two typical rapid thermal annealing steps at 750 °C (non-ohmic behaviour) and 850 °C (ohmic behaviour) the intermetallic phases at the metal-semiconductor interface are presented. Increased annealing leads to the transformation of an Al2Au-AlAuTi phase mixture to a mixture of Al2Au-Al3Au8 phases and the formation of Ti-Al-nitride layers at the interfaces. In light of these results the electrical contact properties are discussed.
Residual stress depth profiles of a cast nickel-base superalloy were measured by regarding the deflections occurring in plate-shaped specimens while successively removing layers from the machined or treated surface by electropolishing. The results are in good agreement with previous findings showing (i) the influence of grinding parameters on the width of so-called white layers, which correspond to steep gradients of residual tensile stress, and (ii) a broad zone of compressive residual stress in the case of shot peening.
Mechanical and thermal response of a nickel-base superalloy upon grinding with high removal rates
(1997)
Turbine components from conventionally cast nickel-base alloy René 80 show different hot cracking susceptibilities depending on their heat treatment conditions leading to slightly different microstructures. Electron probe micro-analysis, focused ion beam technique and analytical transmission electron microscopy were applied to reveal and identify grain boundary precipitates and the γγ'-microstructure. The distribution of borides along grain boundaries was evaluated statistically by quantitative metallography. The following features could be correlated with an increase of cracking susceptibility: i) Increasing grain size, ii) increasing fraction of grain boundaries with densely spaced borides, iii) lack of secondary γ'-particles in matrix channels between the coarse cuboidal γ'-precipitates. The latter feature seems to be responsible for linking-up of cracked grain boundary precipitates which occurred as an additional cracking mechanism after one heat treatment, whereas decohesion at the boride-matrix-interface in the heat affected zone of laser-drilled holes was observed for both heat treatments.
This work focuses on surface changes induced by repeated brake applications and tries to provide explanations, how such material modifications might affect friction and wear properties of automotive disc brakes. Surface films were investigated locally by transmission electron microscopy (TEM) after having prepared thin cross-sections with a focused ion beam instrument (FIB). Since the observed friction layers revealed a nanocrystalline structure, modelling with the method of movable cellular automata (MCA) was performed by assuming an array of linked nanometer-sized particles. In spite of complicated material combinations at the pad surface, two very characteristic features were always observed at both the pad and disc surface, namely a steel constituenteither ferritic (pad) or pearlitic (disc), partly covered with patches of nanocrystalline iron oxide, on a zone of severe plastic deformation with fragmented grain structure. When using an automata size of 10 nm, reasonable values for the mean coefficient of friction (COF) were obtained, namely 0.35 and 0.85 for oxide-on-oxide and metal-on-metal contacts, respectively. Immediately after brake application mass-mixing and bond-breaking was observed within a narrow zone at both surfaces.
Tribological screening tests (simple, reciprocating ball-on-flat tests) were performed with the objective to identify an appropriate coating for the articulating surfaces of artificial hip joints whose acetabular cups and femoral stems are made from Ti6Al4V alloy, which is appreciated for its light weight, good biocompatibility and elastic properties similar to those of natural bone. Standard coatings like TiN or CrN performed better than more complicated multi-layer systems, though not as good as different types of amorphous carbon coatings, generally referred to as diamond-like carbon or DLC coatings. Among the latter, hydrogenated amorphous carbon (a-C:H) displayed the best properties, especially if the hydrogen content was increased by reducing the bias voltage during PA-CVD-deposition.
The optimised a-C:H coating revealed the most promising wear behaviour under the applied testing conditions, i.e. the increase of linear wear with the number of cycles was close to zero. Regarding the materials examined in this study, correlation of wear with mechanical properties obtained by nano-indentation revealed that high hardness was not an adequate criterion for selecting appropriate coatings. A high ratio of hardness and elastic modulus (H/E) proved to be more important. Microstructural and micro-analytical investigations revealed transformation of TiN and CrN to TiO2 and Cr2O3, respectively, and amorphous carbon was, at least partly, transformed to graphite. Furthermore, incorporation of Al2O3 from the ball was observed at a very fine scale. The wear debris of favourable coatings always formed agglomerates of nano-scale particles. It was shown that commercial nano-particles of Al2O3, Cr2O3 and carbon black are comparable to particles generated by the tribological tests. However, it is uncertain whether they are comparable to those formed during simulator studies or in vivo. Furthermore, the performance of the favourable coating has to be tested in a hip joint simulator before its potential for application in prostheses can be assessed.
An attempt was undertaken to obtain a better understanding of the tribological properties of two wear-resistant coatings on tool steel by structural and microchemical analysis of wear particles using a transmission electron microscope. Coatings were deposited by physical vapor deposition and plasma-assisted chemical vapor deposition techniques and tribological properties were derived from reciprocating sliding tests of the coatings against alumina balls. Three types of wear particles were identified by electron diffraction and energy dispersive X-ray spectroscopy: nanocrystalline rutile (TiO2), nanocrystalline graphite and microcrystalline graphite. Low coefficients of friction, of the order of 0.2, were attributed to the formation of solid lubricant films of sub-stoichiometric TiO2-x Magnéli phases and/or graphite.
The chemical and microstructural changes occurring during braking simulation tests at the surface of a conventional brake pad material were investigated mainly by scanning and transmission electron microscopy and surface analytical techniques. It can be shown that patches of a third body material develop, comprising a compositional mix of all constituents of the pad and iron oxides from the disk. Milled debris particles still have the crystal structure of barite, the major phase of the pad material, but the grain size is reduced drastically to the nanometer scale. The major wear mechanism is delamination of filler particles from the organic binder, supported by local degradation of the phenolic resin during asperity heating. Quartz crystals are preserved thereby adopting the function of primary contact areas.
We applied a combination of Raman spectroscopy (RS) and cross-sectional transmission electron microscopy (X-TEM) to identify silicone oil residues and tribofilms at steel disc surfaces after tribological testing. Neither chemical cleaning nor mechanical removal of a 50 µm thick surface layer produced a surface without any silicone residue. Nevertheless, long-term tribological properties are not affected due to silicone degradation which has been proved by Raman spectroscopy. Excellent anti-wear and anti-friction properties of a nanocomposite at severe stressing conditions correlated with the formation of a silica-based tribofilm containing amorphous and graphite-like carbon nanoparticles. Since reliable carbon quantification by analytical TEM is difficult, RS is a useful complementary method for carbon identification at wear scars.
TEM study on the effect of machining on the microstructure of a soft magnetic Ni76Fe17Cu5CrMo2 alloy
(1991)
X-ray photoelectron spectroscopy (XPS) and cross-sectional transmission electron microscopy (XTEM) were used to study the formation of AlN films by N+2 ion implantation of aluminium at energies of 3 keV and 100 keV. In both cases, a two-stage mechanism was found, comprising first the oriented precipitation of small particles of the hexagonal AlN-phase, followed by growth and coalescence finally forming a continuous AlN-layer while increasing the implantation dose from 1×1017 cm-2 to 2×1017 cm-2. The results of both methods are in excellent agreement and furthermore provide complementary information concerning chemical composition and binding energies as well as microstructural details.
Tribofilms formed during dry sliding usually exhibit a nanocrystalline structure and complicated composition. In the present study, tribofilms consisting mainly of a solid lubricant, namely graphite nanoparticles, are considered. Systems providing such tribofilms are candidates for anti-friction applications. Since sliding action always leads to mixing of the materials at both sides of the tribological interface, it was of major interest to study the impact of different amounts of a hard constituent, SiC in the considered case, within the soft matrix systematically. Furthermore, the impact of normal pressure was considered. A mechanically mixed layer was observed for the whole range of normal pressures and SiC volume fractions. The calculated coefficient of friction decreased significantly with increasing thickness of this layer but was only marginally affected by SiC volume fraction, which is good news for anti-friction applications.
Third bodies, also termed friction layers, tribofilms or secondary contact patches, are layers of more or less compacted wear debris between pads and rotor of a disc brake. Our approach of assessing the sliding behavior and friction properties induced by third bodies has been: i) structural characterization after AK-master test procedure, ii) sliding simulation of model structures similar to the observed ones but with simpler and well defined compositions, and iii) verification of simulation results by pin-on-disc tests with artificial third bodies showing the same microstructures and compositions as the model structures. The idea was to simulate structure formation during real braking conditions by high energy ball milling of appropriate powder blends. The final outcome of numerous parameter studies was that a third body containing 15 vol% soft ingredients and 0-20 vol % hard ingredients, both distributed homogeneously in a nanocrystalline iron oxide matrix, should be most desirable for braking. This general description of the optimum third body structure and several parameter studies performed by modelling enabled us to interpret a number of features of the AK-master test procedure, such as i) friction evolution during bedding, ii) the role of solid lubricants in respect to the initiation of smooth sliding behavior, and iii) friction evolution during a single braking event (in-stop behavior).
Automotive braking is based on dry friction between fixed pads and a rotating disc. Besides macroscopic thermo-physical properties, the development of topographic features on the mesoscopic scale and the nanostructure of the third body formed by wear processes, determine brake performance properties. Whereas modelling on the atomistic scale is suitable to understand mechanisms leading to nanocrystalline surface films, the properties of such films can be assessed best with a model based on movable cellular automata (MCA). It turned out that the presence of at least 10% of soft nanoinclusions is most essential in respect to smooth sliding conditions. It made no major difference whether graphite or copper particles were assumed as soft nanoinclusions. The third body material is not only the stuff which spreads over contact areas, but it also contributes to contact size by wear particle compaction and formation of secondary contact areas. The evolution of contact size is the major feature of mesoscopic modelling and thus it is capable to model and explain dynamic changes of the coefficient of friction (COF) during certain brake operations. Although it is still ambiguous in many cases which feature has the major impact on friction behaviour, the following conclusions can be drawn. The reinforcing ingredients of the pad material serve as primary contact sites and thus define the starting condition for mesoscopic simulations. A certain amount of wear is necessary to provide a third body which is capable to form secondary contact sites and friction layers screening the first body materials. The composition and nanostructure of the third body is important as well, because it determines the friction level and is responsible for smooth sliding conditions.
A model based on movable cellular automata has been applied to study the sliding behaviour of tribofilms formed during automotive braking. Since it is not possible yet to determine the composition of real tribofilms quantitatively, final verification of modelling results is needed. This was done by preparing artificial third bodies with compositions and nanostructures matching the ones assumed for modelling. Pin-on-disc tests were performed while applying the artificial third bodies to the contact. The results revealed that not only the structure of the third body but also the amount of the applied normal pressure determines the COF obtained by modelling and that much better correlation between experimental and modelling results was obtained while assuming high normal pressures at asperity contacts.