The composition and nanostructure of a beneficial tribofilm formed during sliding of a hybrid nanocomposite against steel were characterized comprehensively. A similar nanostructure was produced by high energy ball milling of the three identified tribofilm constituents: silica, hematite and graphite. By supplying powders to a pin-on-disc test it has been shown that neither silica, nor hematite, nor a mixture of both provide the low coefficient of friction (COF) observed for the hybrid composite. Only if graphite was blended with the oxides, the low COF was obtained. Thus, a film of finely dispersed stable inorganic wear products containing 15 vol% graphite provides low friction and wear in the considered case.
We applied a combination of Raman spectroscopy (RS) and cross-sectional transmission electron microscopy (X-TEM) to identify silicone oil residues and tribofilms at steel disc surfaces after tribological testing. Neither chemical cleaning nor mechanical removal of a 50 µm thick surface layer produced a surface without any silicone residue. Nevertheless, long-term tribological properties are not affected due to silicone degradation which has been proved by Raman spectroscopy. Excellent anti-wear and anti-friction properties of a nanocomposite at severe stressing conditions correlated with the formation of a silica-based tribofilm containing amorphous and graphite-like carbon nanoparticles. Since reliable carbon quantification by analytical TEM is difficult, RS is a useful complementary method for carbon identification at wear scars.
In order to obtain a better understanding of the role of tribofilms during automotive braking, their structures were investigated and the essential features identified.
Next, different ingredient combinations were studied by preparing some model materials with simpler compositions than real tribofilms. A test method was developed for verifying the tribological properties of the model materials and for comparison with results obtained with numerical sliding simulations of such structures. Prerequisites of good brake Performance properties were identified. Although the coefficient of friction could be varied in a wide ränge, smooth sliding conditions could only be achieved with values smaller than 0.4. Tests with artificial third body powders turned out to be useful as screening method for the selection of raw materials for brake pad formulations.
The tribological behaviour of MoS2/ta-C double layer coatings deposited by Laser-Arc technology was investigated in vacuum and air. In vacuum environment, the friction coefficient against steel balls varies between 0.005 and 0.02 depending on the contact pressure. At high contact pressures, the friction coefficient is as low as 0.005 and the life time between 340,000 and 500,000 cycles. Furthermore, it is shown that a ta-C base layer improves the performance of MoS2 coating.
Surface analyses were performed before and after the tribological tests by means of SEM, EDX, XRD, and TEM. They show that in the top layer beneath the sliding surface crystallization of the initially quasi-amorphous MoS2 took place. TEM images also verified an orientation of the basal MoS2-lattice planes parallel to the surface.
Copper, magnetite and graphite particles were mixed in order to observe their impact on the coefficient of friction (CoF) during pin-on-disc tests and on the tribofilm formation after testing. Pure magnetite powder provided a value of CoF of 0.4. Magnetite-copper mixtures tested at 400 °C revealed lower CoF values (~0.4) than those at room temperature (~0.6). Magnetite-graphite and magnetite-graphite-copper mixtures presented lower CoF values (~0.3). All systems formed a magnetite-based tribofilm and patches of metallic copper were found on the tribosurfaces of the mixtures containing copper. Carbon layers and graphite nanoinclusions were observed in the graphite mixtures. The incorporation of zirconia particles, a by-product of ball milling mixing, prevented the selective transfer of graphite and copper to the tribosurfaces of some of the samples.
Besides carbon, metal sulphides are used in every standard brake pad formulation as friction stabilisers. In order to investigate their impact, various powder mixtures were tribologically stressed in a pin-on-disc device in order to produce and test artificial third bodies. containing the three main components of a real friction film, namely magnetite, graphite and a metal sulphide of interest. Since the sliding behaviour is influenced by the relative humidity the powder mixtures are tested at low, medium and high moisture levels. The tests revealed that the presence of graphite dominates the friction behaviour as well as the humidity sensitivity.
The powders were prepared by either manual mixing or high energy ball-milling. Interestingly, all ball-milled blends provided coefficients of friction within the desired range for braking, which was attributed to the effect of zirconia particles from wear debris of the milling balls. The zirconia particles prevent the formation of solid lubricant films on the surfaces and support a homogeneous mixture of all constituents of the powder. Optimum brake performance is gained by an optimum combination of solid lubricants and abrasives.
A modified pin-on-disc test was applied to determine tribological properties of typical brake pad constituents. Ball-milling of these ingredients together with iron oxide and graphite provided model materials displaying the main features of real third bodies. Solid lubricants like graphite affected the friction and wear behaviour of Fe3O4 powders considerably whereas further addition of hard nanoparticles induced only minor effects. This was corroborated by comparison with modelling results. MoS2 played a dual role. Depending on special conditions, this ingredient either reduced or increased friction. The latter could be explained, after nanoscopic characterization, by oxidation and destruction of the wear-protecting tribofilm.