Introducing a single silicon nanowire with a known orientation and dimensions to a specific layout location constitutes a major challenge. The challenge becomes even more formidable, if one chooses to realize the task in a monolithic fashion with an extreme topography, a characteristic of microsystems. The need for such a monolithic integration is fueled by the recent surge in the use of silicon nanowires as functional building blocks in various electromechanical and optoelectronic applications. This challenge is addressed in this work by introducing a top-down, silicon-on-insulator technology. The technology provides a pathway for obtaining well-controlled silicon nanowires along with microstructures up to a three-order-of-magnitude scale difference. A two-step etching process is developed, where the first shallow etch defines a nanoscale protrusion on the wafer surface. After applying a conformal protection on the protrusion, a deep etch step is carried out forming the surrounding microscale features. A minimum nanowire cross-section of 35 nm by 168 nm is demonstrated in the presence of an etch depth of 10 m. All cross-sectional features are characterized via transmission electron microscopy and linked to specific process steps. The technology allows control on all dimensional aspects along with the exact location and orientation of the silicon nanowire.
A cross-section sample of the friction film formed on top of a disc during a brake testing procedure against Polymer Matrix Composite pads was made using a Focused Ion Beam (FIB). The FIB-cut sampled the "third body" magnetite layer and the upper part of the cast iron disc containing a graphite flake. Images of the sample examined in a Energy Filtered Transmission Electron Microscope captured an instant view of the important role of the graphite flakes in magnetite formation, where few layer graphene batches interacted with the iron border promoting cracking and oxidation along the graphite–iron interface. The resulting nano-scale interlayer of magnetite and strongly disordered graphite formed a third body which yielded adequate brake performance.
A gray cast iron disc, which had been submitted to a heavy duty automotive brake test, was examined with energy filtered transmission electron microscopy. A graphite flake in a convenient angular position showed the shear interaction of graphite layers with the iron matrix in nano-scale resolution. Atomic layers of graphite were wedged into the ferritic bulk, allowing the entrance of oxygen and the subsequent formation of magnetite. The exfoliated few-layer graphene batches deformed heavily when forced into the matrix. When Raman spectra from the disc surface, which show distinctive carbonaceous bands, were compared with Raman spectra from graphite subjected to deformation in a shaker mill with different milling times, it could be seen that the shear stress on the brake surface was much more effective to induce disorder than the milling, where compressive and impact forces had been additionally exerted on the sample. During shear load the high anisotropy of elastic modulus in the graphite crystalline structure and the low adhesion between graphite basal planes allowed the exfoliation of wrinkled few-layer grapheme batches, causing the formation of more defect related Raman bands than the mechanical stress during high-energy milling.
Tribofilms formed during dry sliding usually exhibit a nanocrystalline structure and complicated composition. In the present study, tribofilms consisting mainly of a solid lubricant, namely graphite nanoparticles, are considered. Systems providing such tribofilms are candidates for anti-friction applications. Since sliding action always leads to mixing of the materials at both sides of the tribological interface, it was of major interest to study the impact of different amounts of a hard constituent, SiC in the considered case, within the soft matrix systematically. Furthermore, the impact of normal pressure was considered. A mechanically mixed layer was observed for the whole range of normal pressures and SiC volume fractions. The calculated coefficient of friction decreased significantly with increasing thickness of this layer but was only marginally affected by SiC volume fraction, which is good news for anti-friction applications.
Multi-layer ohmic contact systems such as Au/Pt/Ti/Pt on III-V double layers such as n-InGaP/p+-GaAs are of considerable technological relevance, e.g. for heterojunction bipolar transistors. The paper shows that such contacts can be effectively reacted through the InGaP layer and exhibit very good contact resistances (0.1 O mm) to the base layer if the thickness of the first Pt layer is properly matched to the thickness of the contacted InGaP layer. Interdiffusion and phase formation associated with the annealing processes are studied by cross-sectional analytical transmission electron microscopy, thin-film x-ray diffraction and Auger electron spectroscopy depth profiling. Thermal ageing experiments up to 400 °C show good electrical stability. Device related reliability tests do not show any degradation effect related to this novel base contact.
A new type of test sample for the determination of lateral resolution in surface analysis is presented. The certified reference material BAM-L002 Nanoscale strip pattern for length calibration and testing of lateral resolution is an embedded cross-section of epitaxially grown layers of AlxGa1-xAs and InxGa1-xAs on GaAs substrate. The surface of the sample provides a flat pattern with strip widths of 0.4-500 nm. The combination of gratings, isolated narrow strips and sharp edges of wide strips offers improved possibilities for the calibration of a length scale, the determination of lateral resolution and the optimization of instrument settings. The feasibility of the reference material for an analysis of lateral resolution is demonstrated for SIMS.
Low-cycle fatigue experiments under combined axial-torsional loading have been carried out on alloy 800 H tubular specimens at room temperature. In comparison with proportional loading, an extra cyclic hardening effect produced by nonproportional loading was observed. The microstructure study highlights the fact that the dislocation arrangement under proportional loading is significantly different from that under nonproportional loading. Mechanical twinning was found in specimens cycled under axial loading and nonproportional loading. It is suggested that mechanical twinning depends not only on shear stress but also on normal stress on the plane of maximum shearing. The extra hardening can be interpreted in terms of the deformation microstructure. Fatigue cracking was initiated generally at the specimen surfaces along the plane of maximum shearing, but under nonproportional loading cracks were found also in the bulk of the specimens. Transcrystalline crack propagation was observed in the specimens after proportional and nonproportional LCF tests.
The size, surface charge and agglomeration state of nanoparticles under physiological conditions are fundamental parameters to be determined prior to their application in toxicological studies. Although silica-based materials are among the most promising candidates for biomedical applications, more systematic studies concerning the characterisation before performing toxicological studies are necessary. This interest is based on the necessity to elucidate the mechanisms affecting its toxicity. We present here TEM, SAXS and SMPS as a combination of methods allowing an accurate determination of single nanoparticle sizes. For the commercial material, Ludox TM50 single particle sizes around 30 nm were found in solution. DLS measurements of single particles are rather affected by polydispersity and particles concentration but this technique is useful to monitor their agglomeration state. Here, the influence of nanoparticle concentration, ionic strength (IS), pH and bath sonication on the agglomeration behaviour of silica particles in solution has been systematically investigated. Moreover, the colloidal stability of silica particles in the presence of BSA has been investigated showing a correlation between silica and protein concentrations and the formation of agglomerates. Finally, the colloidal stability of silica particles in standard cell culture medium has been tested, concluding the necessity of surface modification in order to preserve silica as primary particles in the presence of serum. The results presented here have major implications on toxicity investigations because silica agglomeration will change the probability and uptake mechanisms and thereby may affect toxicity.
The chemical and microstructural changes occurring during braking simulation tests at the surface of a conventional brake pad material were investigated mainly by scanning and transmission electron microscopy and surface analytical techniques. It can be shown that patches of a third body material develop, comprising a compositional mix of all constituents of the pad and iron oxides from the disk. Milled debris particles still have the crystal structure of barite, the major phase of the pad material, but the grain size is reduced drastically to the nanometer scale. The major wear mechanism is delamination of filler particles from the organic binder, supported by local degradation of the phenolic resin during asperity heating. Quartz crystals are preserved thereby adopting the function of primary contact areas.
A model system was used to simulate the properties of tribofilms which form during automotive braking. The model system was prepared by ball milling of a blend of 70 vol.% iron oxides, 15 vol.% molybdenum disulfide and 15 vol.% graphite. The resulting mixture was characterized by X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and various transmission electron microscopic (TEM) methods, including energy dispersive X-ray spectroscopy (EDXS), high resolution investigations (HRTEM) with corresponding simulation of the HRTEM images, diffraction methods such as scanning nano-beam electron diffraction (SNBED) and selected area electron diffraction (SAED). It could be shown that the ball milling caused a reduction of the grain size of the initial components to the nanometer range. Sometimes even amorphization or partial break-down of the crystal structure was observed for MoS2 and graphite. Moreover, chemical reactions lead to a formation of surface coverings of the nanoparticles by amorphous material, molybdenum oxides, and iron sulfates as derived from XPS.
The formation of a third body layer on a conventional friction material during braking tests was studied in some detail using TEM, SEM, and X-ray photoelectron spectroscopy (XPS) techniques. Plate shaped micro-contact areas representing a compositional mix of all components of the tribocouple and exhibiting a nanocry stalline microstructure were identified after a run-in period.
Results are reported from a pilot study under the Consultative Committee for Amount of Substance (CCQM) to compare measurements of and resolve any relevant measurement issues in, the amount of thermal SiO2 oxide on (100) and (111) orientation Si wafer substrates in the thickness range 1.5 - 8 nm. As a result of the invitation to participate in this activity, 45 sets of measurements have been made in different laboratories using 10 analytical methods: medium-energy ion scattering spectrometry (MEIS), nuclear reaction analysis (NRA), RBS, elastic backscattering spectrometry (EBS), XPS, SIMS, ellipsometry, grazing-incidence x-ray reflectrometry (GIXRR), neutron reflectometry and transmission electron microscopy (TEM). The measurements are made on separate sets of 10 carefully prepared samples, all of which have been characterised by a combination of ellipsometry and XPS using carefully established reference conditions and reference parameters.
The results have been assessed against the National Physical Laboratory (NPL) data and all show excellent linearity. The remaining data sets correlate with the NPL data with average root-mean-square scatters of 0.15 nm, half being better than 0.1 nm and a few at or better than 0.05 nm. Each set of data allows a relative scaling constant and a zero thickness offset to be determined. Each method has an inherent zero thickness offset between 0 nm and 1 nm and it is these offsets, measured here for the first time, that have caused many problems in the past. There are three basic classes of offset: water and carbonadeous contamination equivalent to ~1 nm as seen by ellipsometry; adsorbed oxygen mainly from water at an equivalent thickness of 0.5 nm as seen by MEIS, NRA, RBS and possibly GIXRR; and no offset as seen by XPS using the Si 2p peaks. Each technique has a different uncertainty for the scaling constant and consistent results have been achieved. X-Ray photoelectron spectroscopy has large uncertainties for the scaling constant but a high precision and, critically, if used correctly, has zero offset. Thus, a combination of XPS and the other methods allows the XPS scaling constant to be determined with low uncertainty, traceable via the other methods. XPS laboratories returning results early were invited to test a new reference procedure. All showed very significant improvements. The reference attenuation lengths thus need scaling by 0.986 ± 0.009 (at an expansion factor of 2) deduced from the data for the other methods. Several other methods have small offsets and, to the extent that these can be shown to be constant or measurable, then these methods will also show low uncertainty. Recommendations are provided for parameters for XPS, MEIS, RBS and NRA to improve their accuracy.
Determination of the elastic behavior of silicon nanowires within a scanning electron microscope
(2016)
Three-point bending tests were performed on double-anchored, <110> silicon nanowire samples inside a scanning electron microscope (SEM) via a micromanipulator equipped with a piezo-resistive force sensor. Representing the upper and lower boundaries achievable in a consistent manner, silicon nanowires with widths of 35 nm and 74 nm and a height of 168 nm were fabricated. The nanowires were obtained monolithically along with their 10-m-tall supports through a top-down fabrication approach involving a series of etching processes. Hence, no interface compliance was introduced between supports and nanowires. Exact nanowire dimensions and cross-sectional features were determined by transmission electron microscopy (TEM) following sample preparation through focused ion beam (FIB) machining. Conducting the experiments inside an SEM chamber further raised the opportunity of the direct observation of any deviation from ideal loading conditions such as twisting, which was taken into consideration in simulations. Measured force-displacement behavior was observed to exhibit close resemblance to simulation results obtained by finite element modeling, when the bulk value of 169 GPa was taken as the modulus of elasticity for <110> silicon. Hence, test results show neither any size effect nor evidence of residual stresses for the considered nanoscale objects. The increased effect of the native oxide with reduced nanowire dimensions was captured as well. Thus this very simple in-situ testing method was found to be an alternative to elaborate AFM measurements on geometrically formidable nanostructures. The results demonstrate the applicability of the developed fabrication approach to the incorporation of silicon nanowires in functional micromechanical devices.
Does ultra-mild wear play any role for dry friction applications, such as automotive braking?
(2012)
Nanostructured third body films and/or storage of wear debris at the surfaces of the first bodies are deemed as prerequisites of sliding under ultra-mild wear conditions. Since such features have been observed experimentally on brake pads and discs, attempts were undertaken to study their sliding behaviour by modelling on the nanoscopic scale with an approach based on Movable Cellular Automata (MCA). The model rendered the possibility to study the influence of different nanostructures systematically and to assess the impact of different brake pad ingredients on the sliding behaviour, velocity accommodation and friction force stabilization at a sliding contact. Besides providing a review on previously published modelling results, some additional new graphs enabling better visualization of dynamic processes are presented. Although ultra-mild wear conditions were considered to be essential for achieving the desired tribological properties, transitions to mesoscopic and macroscopic wear mechanisms were studied as well. The final conclusion is that ultra-mild wear and corresponding smooth sliding behaviour play an important role during automotive braking, even though temporarily and locally events of severe wear may cause friction instabilities, surface damage and release of coarse wear particles.
The composition and nanostructure of a beneficial tribofilm formed during sliding of a hybrid nanocomposite against steel were characterized comprehensively. A similar nanostructure was produced by high energy ball milling of the three identified tribofilm constituents: silica, hematite and graphite. By supplying powders to a pin-on-disc test it has been shown that neither silica, nor hematite, nor a mixture of both provide the low coefficient of friction (COF) observed for the hybrid composite. Only if graphite was blended with the oxides, the low COF was obtained. Thus, a film of finely dispersed stable inorganic wear products containing 15 vol% graphite provides low friction and wear in the considered case.
Exploring the influence of counterpart materials on tribological behaviors of epoxy composites
(2016)
The dependence of the friction and wear of epoxy (EP) composites materials on counterpart materials, such as standard bearing steel, medium carbon steel and chrome-plating (Cr), was investigated. The conventional composite filled with short carbon fiber (SCF) and graphite shows the highest tribological performance when rubbing against Cr, whereas, the hybrid nanocomposite (EP filled with SCF, graphite and silica nanoparticles) exhibits the lowest friction and wear when sliding against the standard bearing steel. The role of nanoparticles in the tribological performance is distinctly different when sliding against with various counterpart materials. It is demonstrated that counterpart materials exert an important influence on material transfer, tribo-oxidation and mechanical mixing of wear products, resulting in the different formation mechanisms of transfer film.
We applied a combination of Raman spectroscopy (RS) and cross-sectional transmission electron microscopy (X-TEM) to identify silicone oil residues and tribofilms at steel disc surfaces after tribological testing. Neither chemical cleaning nor mechanical removal of a 50 µm thick surface layer produced a surface without any silicone residue. Nevertheless, long-term tribological properties are not affected due to silicone degradation which has been proved by Raman spectroscopy. Excellent anti-wear and anti-friction properties of a nanocomposite at severe stressing conditions correlated with the formation of a silica-based tribofilm containing amorphous and graphite-like carbon nanoparticles. Since reliable carbon quantification by analytical TEM is difficult, RS is a useful complementary method for carbon identification at wear scars.
The influence of the surface roughness of pearlitic grey cast iron discs on the formation of tribofilms and the evolution of the friction coefficient during a ring on disc tribotest with the addition of magnetite and magnetite–graphite nanopowders as interfacial media was investigated. The roughness parameters of the cast iron discs were varied by electro discharge machining (EDM) and grinding processes, producing four distinct surface roughness conditions. The evolution of the friction coefficient, however, did not reach the steady state for most of the samples and the role of the surface roughness on the friction coefficient could not be identified. Focused ion beam (FIB) microscopy on the cast iron discs was carried out to investigate the microstructure of the discs near the tribosurface. These results showed that the EDM process not only varied the surface roughness, but also changed the microstructure of the cast iron discs, promoting the incipient fusion of the cast iron surface, with the formation of ridges and casting defects (pores). As a result, a layer of rapidly solidified metal with a dendritic microstructure was formed near to the surface of the EDMed discs.
Formation and function mechanisms of nanostructured tribofilms of epoxy-based hybrid nanocomposites
(2015)
The nanostructures and properties of the tribofilms of epoxy (EP) composites filled with short carbon fibers (SCF) and different volume fractions of monodisperse silica nanoparticles were investigated. When the conventional composite filled only with SCF was considered under a high pv condition, an iron oxide layer is formed on the steel counterface. The addition of even only 0.05 vol% nano-silica leads to a significant change of the tribofilm's structure and the tribological behavior of the composite. With increasing silica content, the oxidation layer on the steel surface is gradually replaced by a silica-based tribofilm. A close relationship between the tribofilms structure and the tribological behavior of the composites was identified. Mixing, possible reactions and tribo-sintering of silica nanoparticles with other wear products are deemed to be main mechanisms inducing the formation and the lubricity of the silica-based tribofilm.
The tribological behaviour of MoS2/ta-C double layer coatings deposited by Laser-Arc technology was investigated in vacuum and air. In vacuum environment, the friction coefficient against steel balls varies between 0.005 and 0.02 depending on the contact pressure. At high contact pressures, the friction coefficient is as low as 0.005 and the life time between 340,000 and 500,000 cycles. Furthermore, it is shown that a ta-C base layer improves the performance of MoS2 coating.
Surface analyses were performed before and after the tribological tests by means of SEM, EDX, XRD, and TEM. They show that in the top layer beneath the sliding surface crystallization of the initially quasi-amorphous MoS2 took place. TEM images also verified an orientation of the basal MoS2-lattice planes parallel to the surface.
A rather new tool, the focused ion beam (FIB) technique, was used to characterise superficial layers at micro-contact areas of a commercial brake pad. The friction material was a polymer matrix composite (PMC) with approximately 50% metal content (semi-metallic) and the counter part was a cast iron rotor. Though the contact areas were not visible as topographic features, they could be identified with the aid of their increased secondary electron emission during FIB-scanning of the surface after tribological activation. Target preparation of micron-sized cross-sections with the FIB enabled the study of superficial layers at predetermined sites at high magnification.
Depending on the constituent of the pad, one, two or three layers were identified. The three layer structure comprised: (i) a 100 nm thick friction film containing nanocrystalline metal oxides and an amorphous phase which was enriched with sulphur, (ii) a nanocrystalline friction layer of compacted wear debris accommodating surface roughness and (iii) a severely deformed layer if the supporting constituent was a metal particle. Though the majority of loose wear particles was iron oxide, the friction film which adhered tightly to the pad surface contained a large amount of copper and sulphur, whereas zinc was transferred to the cast iron rotor.
Automotive braking is based on dry friction between fixed pads and a rotating disc. Besides macroscopic thermo-physical properties, the development of topographic features on the mesoscopic scale and the nanostructure of the third body formed by wear processes, determine brake performance properties. Whereas modelling on the atomistic scale is suitable to understand mechanisms leading to nanocrystalline surface films, the properties of such films can be assessed best with a model based on movable cellular automata (MCA). It turned out that the presence of at least 10% of soft nanoinclusions is most essential in respect to smooth sliding conditions. It made no major difference whether graphite or copper particles were assumed as soft nanoinclusions. The third body material is not only the stuff which spreads over contact areas, but it also contributes to contact size by wear particle compaction and formation of secondary contact areas. The evolution of contact size is the major feature of mesoscopic modelling and thus it is capable to model and explain dynamic changes of the coefficient of friction (COF) during certain brake operations. Although it is still ambiguous in many cases which feature has the major impact on friction behaviour, the following conclusions can be drawn. The reinforcing ingredients of the pad material serve as primary contact sites and thus define the starting condition for mesoscopic simulations. A certain amount of wear is necessary to provide a third body which is capable to form secondary contact sites and friction layers screening the first body materials. The composition and nanostructure of the third body is important as well, because it determines the friction level and is responsible for smooth sliding conditions.
The objective of the present work was to study the impact of Focused Ion Beam (FIB) machining parameters on the thickness of the damaged layer within a thin film PZT. Therefore, different Ga+- ion doses and ion energies were applied to a standard PZT film (80/20 lead zirconium titanate) under two beam incidence angles (90° and 1°). The thicknesses of the corresponding Ga+-implanted layers were then determined by cross-sectional TEM in combination with energy dispersive spectroscopic (EDS) line-scans and correlated with polarisation hysteresis loops. The results show a decrease of Ga+-implanted layer thickness with decreasing inclination angle, whereas ion energy and ion dose could be correlated with gallium concentration in the implanted layers.. Under the most unfavorable conditions the depth of the affected zone was 26 nm, it was only 2 nm for the most favorable conditions.
Copper, magnetite and graphite particles were mixed in order to observe their impact on the coefficient of friction (CoF) during pin-on-disc tests and on the tribofilm formation after testing. Pure magnetite powder provided a value of CoF of 0.4. Magnetite-copper mixtures tested at 400 °C revealed lower CoF values (~0.4) than those at room temperature (~0.6). Magnetite-graphite and magnetite-graphite-copper mixtures presented lower CoF values (~0.3). All systems formed a magnetite-based tribofilm and patches of metallic copper were found on the tribosurfaces of the mixtures containing copper. Carbon layers and graphite nanoinclusions were observed in the graphite mixtures. The incorporation of zirconia particles, a by-product of ball milling mixing, prevented the selective transfer of graphite and copper to the tribosurfaces of some of the samples.
The effect of steel counterface topography on the formation mechanisms of nanostructured tribofilms of polyetheretherketone (PEEK) hybrid nanocomposites was studied. Three types of surface finishes with mean roughness Ra ranging from nano- to micro-scale were investigated. Tribo-sintering of nanopartides, oxidation of counterface steel and compaction of wear debris are identified to be competing factors dominating the formation and function of the tribofilms. Counterface topography played an important role on the competing factors, and thereby influenced significantly the final structure, the load-carrying capability and the lubrication performance of the tribofilms. It was disclosed that a thin tribofilm, which mainly consists of silica nanoparticles and which forms on the counterface with a submicron roughness, benefits best the tribological performance of the composites
Different, partly complementary and partly redundant characterization methods were applied to study the transition of magnetite, graphite and MoS2 powders to mechanically alloyed nanostructures. The applied methods were: Transmission electron microscopy (TEM), Mössbauer spectroscopy (MS), Raman spectroscopy (RS), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The main objective was to prepare a model material providing the essential features of a typical tribofilm forming during automotive braking, and to assess the impact of different constituents on sliding behaviour and friction level. Irrespective of the initial grain size, the raw materials were transferred to a nanocrystalline structure and mixed on a nanoscopic scale during high energy ball milling. Whereas magnetite remained almost unchanged, graphite and molybdenum disulphide were transformed to a nanocrystalline and highly disordered structure. The observed increase of the coefficient of friction was attributed to a loss of lubricity of the latter ingredient due to this transformation and subsequent oxidation.
Analytical routines for a comprehensive in-depth morphological, structural, and chemical characterization of functionalized TiO2 films by using different state-of-the-art analytical techniques are presented and discussed with the main objective to identify potential reference TiO2 coating parameters able to be certified at a later stage. TiO2 films fabricated by two different synthetic procedures as representative for two main large-scale applications were selected: (i) pulsed d.c. magnetron sputtering for photocatalytic applications and (ii) screen printing from preformed anatase nanoparticles. The screen-printed films were further loaded with a sensitizing dye for application as a dye-sensitized solar cell. Film properties such as microstructure and crystallographic texture of pulsed d.c. magnetron sputtering synthesized films were systematically studied by means of scanning nanobeam electron diffraction in a transmission electron microscope and the surface and inner morphology by scanning electron microscopy. The dye distribution over the depth of screen-printed TiO2 layers was analyzed before and after dye-loading by means of energy dispersive X-ray spectroscopy at scanning electronmicroscope, Auger electron spectroscopy and time-of-flight secondary ion mass spectrometry. The long-term goal of the present study is the improvement of quality of the TiO2 film parameters as measured by using different types of reference TiO2 coatings having specific parameters certified.
Turbine components from conventionally cast nickel-base alloy René 80 show different hot cracking susceptibilities depending on their heat treatment conditions leading to slightly different microstructures. Electron probe micro-analysis, focused ion beam technique and analytical transmission electron microscopy were applied to reveal and identify grain boundary precipitates and the γγ'-microstructure. The distribution of borides along grain boundaries was evaluated statistically by quantitative metallography. The following features could be correlated with an increase of cracking susceptibility: i) Increasing grain size, ii) increasing fraction of grain boundaries with densely spaced borides, iii) lack of secondary γ'-particles in matrix channels between the coarse cuboidal γ'-precipitates. The latter feature seems to be responsible for linking-up of cracked grain boundary precipitates which occurred as an additional cracking mechanism after one heat treatment, whereas decohesion at the boride-matrix-interface in the heat affected zone of laser-drilled holes was observed for both heat treatments.
Residual stress depth profiles of a cast nickel-base superalloy were measured by regarding the deflections occurring in plate-shaped specimens while successively removing layers from the machined or treated surface by electropolishing. The results are in good agreement with previous findings showing (i) the influence of grinding parameters on the width of so-called white layers, which correspond to steep gradients of residual tensile stress, and (ii) a broad zone of compressive residual stress in the case of shot peening.
The unique nanostructure formed during severe as well as moderate braking on the surface of brake discs was investigated by conventional and analytical Transmission Electron Microscopy. In both cases nanocrystalline magnetite mixed with carbon nanoinclusions and minor amounts of other pad constituents were identified. On the basis of these observations the friction performance of a single micro-contact was simulated with the method of Movable Cellular Automata. Inspite of a simplified nanostructure which was examined in two dimensions only, the calculated mean coefficient of friction fitted well to the value usually demanded for automotive braking. Furthermore, the model predicts that oxide films without soft nanoinclusions are not capable of providing smooth velocity accommodation at the pad–disc interface and thus lead to unstable friction behaviour.
Patches of white etching layers on rail surfaces were investigated using sophisticated techniques like cross-sectional transmission electron microscopy (XTEM) and synchroton X-ray diffraction. Optical microscopy failed to resolve the microstructure, but in the TEM submicron grains with high dislocation densities and occasional twins, which are characteristic features of high carbon martensite, were observed. The martensitic structure was confirmed by evaluation of synchroton X-ray diffraction line profiles. The latter technique also allowed to determine dislocation densities of the order of 1012 cm-2 and residual compressive stresses of about 200 MPa.
The certified reference material BAM-L200, a nanoscale stripe pattern for length calibration and specification of lateral resolution, is described. BAM-L200 is prepared from a cross-sectioned epitaxially grown layer stack of AlxGa1–xAs and InxGa1–xAs on a GaAs substrate. The surface of BAM-L200 provides a flat pattern with stripe widths ranging down to 1 nm. Calibration distances, grating periods and stripe widths have been certified by TEM with traceability to the length unit. The combination of gratings, isolated narrow stripes and sharp edges of wide stripes offers plenty of options for the determination of lateral resolution, sharpness and calibration of length scale at selected settings of imaging surface-analytical instruments. The feasibility of the reference material for an analysis of the lateral resolution is demonstrated in detail by evaluation of ToF-SIMS, AES and EDX images. Other applications developed in the community are summarized, too. BAM-L200 fully supports the implementation of the revised International Standard ISO 18516 (in preparation) which is based on knowledge outlined in the Technical Report ISO/TR 19319:2013.
The sintering temperature of BaTiO3 powder was reduced to 900 °C due to the ZnO-B2O3-Li2O-Nb2O5-Co2O3 addition. Excellent densification was achieved after sintering at 900 °C for 2 h. The low sintering temperature of newly developed capacitor materials allows a co-firing with pure silver electrodes. The dielectric constant and the temperature stability of the dielectric constant are strongly correlated with the composition of the ZnO-B2O3-Li2O additives. A high dielectric constant up to 3000 and a dielectric loss less than 0.024 were measured on multilayer capacitors sintered at 900 °C with silver inner electrodes.
Mechanical and thermal response of a nickel-base superalloy upon grinding with high removal rates
(1997)
A model based on movable cellular automata (MCA) is described and applied for simulating the stress–strain and sliding behavior of a nanocomposite consisting of an epoxy matrix and 6 vol.% of homogeneously distributed silica nanoparticles. Tensile tests were used for verification of the model. It was realized that a slight modification of epoxy properties due to the addition of silica nanoparticles had to be taken into account in order to obtain good correlation between experimental and modeling results. On the other hand, sliding simulations revealed no susceptibility of results to slight modifications of matrix properties, but a significant impact of nanoparticles on the interface structure and smoothness of sliding mechanism. Furthermore, assuming both possibilities, bond breaking and rebinding of automata pairs, can explain different friction levels of polymer materials.
Different wear-resistant coatings produced by physical vapour deposition (PVD) were characterized with the aid of cross-sectional transmission electron microscopy (XTEM). All coating systems were optimized by the producers and exhibited good properties with respect to their special applications. The microstructure, texture and chemical composition of binary and ternary systems produced by the arc process [TiN, CrN, Cr2N (Ti, Cr)N on steel substrates] and magnetron sputtering process [TiN, CrN on steel substrates, (Ti, Al)N on Si-substrate] were investigated. All coatings had a more or less columnar microstructure, which was interrupted by interlayers in some cases. Whereas arc coatings always did show some kind of substrate modification, the latter was not observed after magnetron sputtering. Electron diffraction normally revealed a mono-phase fcc structure, except at sites very near to the interface. Only for the systems CrN and (Ti, Cr)N were different additional phases observed at low nitrogen partial pressures.
An attempt was undertaken to obtain a better understanding of the tribological properties of two wear-resistant coatings on tool steel by structural and microchemical analysis of wear particles using a transmission electron microscope. Coatings were deposited by physical vapor deposition and plasma-assisted chemical vapor deposition techniques and tribological properties were derived from reciprocating sliding tests of the coatings against alumina balls. Three types of wear particles were identified by electron diffraction and energy dispersive X-ray spectroscopy: nanocrystalline rutile (TiO2), nanocrystalline graphite and microcrystalline graphite. Low coefficients of friction, of the order of 0.2, were attributed to the formation of solid lubricant films of sub-stoichiometric TiO2-x Magnéli phases and/or graphite.
The microstructures of two samples of a Zr(C,N) coating on steel, which unexpectedly differed in their tribological properties, were investigated by analytical transmission electron microscopy. The samples were produced by a cathodic arc evaporation process in two commercial coating devices under similar coating conditions with the exception of the number of Zr targets.
The source of the differing tribological properties of the samples was detected by analytical transmission electron microscopy (TEM) methods energy-dispersive X-ray spectroscopy (EDX), energy filtering TEM (EFTEM), electron diffraction, high resolution electron microscopy, and high angel annular dark field. The TEM preparation and the results of the TEM investigations are shown in detail. The origin of the unexpected behavior was determined to be a nano-scale multilayer structure that existed only in the tribologically superior specimen. EDX and EFTEM investigations indicated enrichment in oxygen at the interface between coating and steel substrate in the tribologically inferior sample. Findings of the microstructural configuration were obtained by taking a closer look at the structure and comparing the results of the several analytical TEM techniques. This allows the allocation of the concentration fluctuations in N, C, and Zr to the two thickness fractions of the nano multilayers and a local correlation of the identified minority phase Zr3(C,N)4 to the higher N content in the narrower type of the multilayer fraction of the sample with the excellent tribological properties. The minority phase Zr3(C,N)4 is randomly distributed in the sample with the defective tribological properties.
Coating conditions are not topic of this work, but after discussion of the TEM results, the fact that one of the coating devices worked with one Zr target and the other one with two, could be identified as cause for the formation of the nano multilayer structure in the sample with the superior tribological properties.
The frictional behavior at local contacts in an automotive brake system was analysed on the basis of computer simulation by movable cellular automata method. The boundary conditions of the model were adjusted to experimental observations obtained by TEM. The model proved to be adequate for simulating mechanical mixing and velocity accommodation at the pad-disc interface. Dynamics of particle interaction were visualized by showing rotation angles and velocity vectors. The model provided information on the development of plastic deformation for metal-on-metal contacts and on crack formation at graphite lamellae of cast iron disc. Results are in agreement with conventional friction theories.
The method of movable cellular automata (MCA) was applied to simulate the stress-strain behavior of a nano composite consisting of an epoxy matrix and 6 vol. % silica nano particles. The size of the elements used for modelling was fixed at 10 nm, corresponding approximately to the diameter of the filler particles. Since not only the stress-strain response of the two constituents but also debonding of neighboring particles and granular flow was taken into account, plastic deformation as well as crack initiation and propagation could be simulated with the model. Modelling results were compared with tensile test results of both, pure epoxy as well as the epoxy-6 vol. % SiO2 composite. Since assuming bulk properties of the two constituents did not yield satisfactory results, slight modifications of the nanoparticle response functions and nanostructures were tested numerically. Finally, it was observed that only the assumption of slightly increased strength properties of the epoxy yielded good correlation between experimental and modelling results. This was attributed to an increased cross linking of the epoxy caused by the presence of silica nano particles.