This review article comprises of three parts. Firstly, reports of brake manufacturers on the beneficial impact of solid lubricants for pad formulations are surveyed. Secondly, since tribofilms were identified to play a crucial role in friction stabilization and wear reduction, the knowledge about tribofilm structures formed during automotive braking was reviewed comprehensively. Finally, a model for simulating the sliding behavior of tribofilms is suggested and a review on modelling efforts with different model structures related to real tribofilms will be presented. Although the variety of friction composites involved in commercial brake systems is very broad, striking similarities were observed in respect to tribofilm nanostructures. Thus a generalization of the tribofilm nanostructure is suggested and prerequisites for smooth sliding performance and minimal wear rates have been identified. A minimum of 13 vol.% of soft inclusions embedded in an iron oxide based tribofilm is crucial for obtaining the desired properties. As long as the solid lubricants or their reaction products are softer than magnetite, the main constituent of the tribofilm, the model predicts smooth sliding and a minimum of wear.
Third bodies, also termed friction layers, tribofilms or secondary contact patches, are layers of more or less compacted wear debris between pads and rotor of a disc brake. Our approach of assessing the sliding behavior and friction properties induced by third bodies has been: i) structural characterization after AK-master test procedure, ii) sliding simulation of model structures similar to the observed ones but with simpler and well defined compositions, and iii) verification of simulation results by pin-on-disc tests with artificial third bodies showing the same microstructures and compositions as the model structures. The idea was to simulate structure formation during real braking conditions by high energy ball milling of appropriate powder blends. The final outcome of numerous parameter studies was that a third body containing 15 vol% soft ingredients and 0-20 vol % hard ingredients, both distributed homogeneously in a nanocrystalline iron oxide matrix, should be most desirable for braking. This general description of the optimum third body structure and several parameter studies performed by modelling enabled us to interpret a number of features of the AK-master test procedure, such as i) friction evolution during bedding, ii) the role of solid lubricants in respect to the initiation of smooth sliding behavior, and iii) friction evolution during a single braking event (in-stop behavior).