Weld metal microstructure for alloy 6060 aluminum welds, made using the gas-tungsten arc process and alloy 4043 filler metal, has been characterized using optical metallography, EPMA microprobe analysis, SEM/EBSD and STEM/EDX electron microscopy, and single-sensor differential thermal analysis (SS-DTA). In addition, alloy 6060 castings were solidified at variable cooling rates approaching that of welding, to provide a reference for comparison with weld microstructure. It was found that a major change in cast microstructure occurs at cooling rates higher than 27 K/s resulting in a structure similar to that observed in weld metal. Rapid cooling is believed to favor low temperature solidification reactions that normally would be achieved only at higher silicon content. Accordingly, additions of 4043 filler metal that increase the weld metal silicon content have only limited affect on weld solidification range and microstructure. This has direct implications regarding how 4043 filler additions improve weldability and weld quality.
The resistance of structural steels against corrosion in CO2-H2O and CO2-H2O-O2
atmospheres at temperatures above 550°C was observed with high magnification methods.
The test atmosphere is the basic composition of an oxyfuel coal combustion atmosphere. The
analytical information base was applied to develop reaction schemes for the oxidation of
steels. It was demonstrated that the formation of phases and the kinetics of oxidation reactions
in this atmospheres is affected by the formation of intermediate iron hydroxide and a high
carbon activity. In the temperature regime above 550°C the thermal equilibrium between H2O,
CO2 and Fe reacted and formed CO. CO triggers the formation of FeO and carbides and
increases the reaction kinetics. Porosity at the interface is established by gaseous phases
such as Fe(OH)2 or H2O. H2 formation is not limited to the steel - oxide interface but can occur
in the whole oxide scale. Examples of the experimental results were compared with a
thermodynamic approach. The objective of the work was to derive qualitative rules of the basic
corrosion reactions.