This work focuses on surface changes induced by repeated brake applications and tries to provide explanations, how such material modifications might affect friction and wear properties of automotive disc brakes. Surface films were investigated locally by transmission electron microscopy (TEM) after having prepared thin cross-sections with a focused ion beam instrument (FIB). Since the observed friction layers revealed a nanocrystalline structure, modelling with the method of movable cellular automata (MCA) was performed by assuming an array of linked nanometer-sized particles. In spite of complicated material combinations at the pad surface, two very characteristic features were always observed at both the pad and disc surface, namely a steel constituenteither ferritic (pad) or pearlitic (disc), partly covered with patches of nanocrystalline iron oxide, on a zone of severe plastic deformation with fragmented grain structure. When using an automata size of 10 nm, reasonable values for the mean coefficient of friction (COF) were obtained, namely 0.35 and 0.85 for oxide-on-oxide and metal-on-metal contacts, respectively. Immediately after brake application mass-mixing and bond-breaking was observed within a narrow zone at both surfaces.
The surfaces of a brake pad and rotor were investigated after a run-in period during which a stable coefficient of friction had developed. The Focused Ion Beam Technique (FIB) was used to reveal tribologically induced surface films and for cross-sectional preparation of superficial layers. Additional information was obtained by TEM/EDS of thin lamellae prepared with the FIB and by surface analytical methods (GDOS, XPS and RS). Microscopic contact areas of the pad showed bright contrast in Scanning Ion Microscopy (SIM). This was attributed to severe plastic deformation finally leading to a nanocrystalline microstructure. Metallic particles of the pad, the so-called primary contact areas, were mostly covered with a smooth oxide layer of less than 1 µm thickness. Above this layer a thin (100 nm) partly amorphous film was often observed. The film was not only restricted to the metal particles, but also spread over adjacent regions, suggesting that secondary plateaus had formed. Similar layers and films, although with slightly different composition and structure, were also observed at the surface of the rotor.
An attempt was undertaken to obtain a better understanding of the tribological properties of two wear-resistant coatings on tool steel by structural and microchemical analysis of wear particles using a transmission electron microscope. Coatings were deposited by physical vapor deposition and plasma-assisted chemical vapor deposition techniques and tribological properties were derived from reciprocating sliding tests of the coatings against alumina balls. Three types of wear particles were identified by electron diffraction and energy dispersive X-ray spectroscopy: nanocrystalline rutile (TiO2), nanocrystalline graphite and microcrystalline graphite. Low coefficients of friction, of the order of 0.2, were attributed to the formation of solid lubricant films of sub-stoichiometric TiO2-x Magnéli phases and/or graphite.
Automotive brake pads consist of many components but it is still not entirely clear which role each of the elements of this complex composition plays to provide the specified regimes of sliding. This is due to the mutual interaction of multiscale mechanisms, realized during the friction.
In this work we have attempted to partly answer this question using computer simulations. Since the simulation allows us to consider various combinations of the structure of the system being simulated ceteris paribus, it becomes possible to understand the role of each constituent sequentially. The main attention is paid to the structure and composition of the thin film that forms on the surface of both bodies as a result of compaction of the wear product, its chemical composition and oxidation. This layer, also named a third body or friction film, differs in composition and microstructure from the two first bodies. We considered a single contact for the steady state sliding when the structure and composition of friction films already are formed. As a modelling tool we used the method of movable cellular automata, which has well proven itself in solving of such tasks. We investigated the influence of modification of the structure and composition of the third body on the features of system behaviour at friction. To assess the adequacy of the numerical model, experimental studies with an artificial third body were also carried out. The Simulation results are in good agreement with experimental data.
A model based on movable cellular automata has been applied to study the sliding behaviour of tribofilms formed during automotive braking. Since it is not possible yet to determine the composition of real tribofilms quantitatively, final verification of modelling results is needed. This was done by preparing artificial third bodies with compositions and nanostructures matching the ones assumed for modelling. Pin-on-disc tests were performed while applying the artificial third bodies to the contact. The results revealed that not only the structure of the third body but also the amount of the applied normal pressure determines the COF obtained by modelling and that much better correlation between experimental and modelling results was obtained while assuming high normal pressures at asperity contacts.
A modified pin-on-disc test was applied to determine tribological properties of typical brake pad constituents. Ball-milling of these ingredients together with iron oxide and graphite provided model materials displaying the main features of real third bodies. Solid lubricants like graphite affected the friction and wear behaviour of Fe3O4 powders considerably whereas further addition of hard nanoparticles induced only minor effects. This was corroborated by comparison with modelling results. MoS2 played a dual role. Depending on special conditions, this ingredient either reduced or increased friction. The latter could be explained, after nanoscopic characterization, by oxidation and destruction of the wear-protecting tribofilm.
Does ultra-mild wear play any role for dry friction applications, such as automotive braking?
(2012)
Nanostructured third body films and/or storage of wear debris at the surfaces of the first bodies are deemed as prerequisites of sliding under ultra-mild wear conditions. Since such features have been observed experimentally on brake pads and discs, attempts were undertaken to study their sliding behaviour by modelling on the nanoscopic scale with an approach based on Movable Cellular Automata (MCA). The model rendered the possibility to study the influence of different nanostructures systematically and to assess the impact of different brake pad ingredients on the sliding behaviour, velocity accommodation and friction force stabilization at a sliding contact. Besides providing a review on previously published modelling results, some additional new graphs enabling better visualization of dynamic processes are presented. Although ultra-mild wear conditions were considered to be essential for achieving the desired tribological properties, transitions to mesoscopic and macroscopic wear mechanisms were studied as well. The final conclusion is that ultra-mild wear and corresponding smooth sliding behaviour play an important role during automotive braking, even though temporarily and locally events of severe wear may cause friction instabilities, surface damage and release of coarse wear particles.
The tribological properties of nanostructured surface films formed during dry sliding, for example during
automotive braking, were determined by modelling using the method of movable cellular automata.
Starting from a basic model structure, consisting of magnetite with 13% graphite inclusions, the impact of
additional soft and hard particles of different size and volume fraction was studied systematically. It was
revealed that agglomerates of soft particles decomposed and finally mixed with the oxide in the same
way as single nanoparticles. On the other hand, agglomerates of hard particles mixed with the other
components without decomposing. Whereas increasing the amount of soft components in the third body
lowered the coefficient of friction, the opposite occurred with the hard particles. The boundary conditions
for obtaining smooth sliding conditions with minor fluctuations between friction forces at successive time
steps could be defined. In addition to features of the nanostructure, the applied normal pressure
impacted modelling results. Within the parameter range of smooth sliding behaviour, increasing pressure
induced thicker granular interface layers, which lead to a slight decrease of the coefficient of friction.
Changing the amount of soft or hard particles did not change this pressure dependency but only the
friction level.