Turbine components from conventionally cast nickel-base alloy René 80 show different hot cracking susceptibilities depending on their heat treatment conditions leading to slightly different microstructures. Electron probe micro-analysis, focused ion beam technique and analytical transmission electron microscopy were applied to reveal and identify grain boundary precipitates and the γγ'-microstructure. The distribution of borides along grain boundaries was evaluated statistically by quantitative metallography. The following features could be correlated with an increase of cracking susceptibility: i) Increasing grain size, ii) increasing fraction of grain boundaries with densely spaced borides, iii) lack of secondary γ'-particles in matrix channels between the coarse cuboidal γ'-precipitates. The latter feature seems to be responsible for linking-up of cracked grain boundary precipitates which occurred as an additional cracking mechanism after one heat treatment, whereas decohesion at the boride-matrix-interface in the heat affected zone of laser-drilled holes was observed for both heat treatments.
Tribological screening tests (simple, reciprocating ball-on-flat tests) were performed with the objective to identify an appropriate coating for the articulating surfaces of artificial hip joints whose acetabular cups and femoral stems are made from Ti6Al4V alloy, which is appreciated for its light weight, good biocompatibility and elastic properties similar to those of natural bone. Standard coatings like TiN or CrN performed better than more complicated multi-layer systems, though not as good as different types of amorphous carbon coatings, generally referred to as diamond-like carbon or DLC coatings. Among the latter, hydrogenated amorphous carbon (a-C:H) displayed the best properties, especially if the hydrogen content was increased by reducing the bias voltage during PA-CVD-deposition.
The optimised a-C:H coating revealed the most promising wear behaviour under the applied testing conditions, i.e. the increase of linear wear with the number of cycles was close to zero. Regarding the materials examined in this study, correlation of wear with mechanical properties obtained by nano-indentation revealed that high hardness was not an adequate criterion for selecting appropriate coatings. A high ratio of hardness and elastic modulus (H/E) proved to be more important. Microstructural and micro-analytical investigations revealed transformation of TiN and CrN to TiO2 and Cr2O3, respectively, and amorphous carbon was, at least partly, transformed to graphite. Furthermore, incorporation of Al2O3 from the ball was observed at a very fine scale. The wear debris of favourable coatings always formed agglomerates of nano-scale particles. It was shown that commercial nano-particles of Al2O3, Cr2O3 and carbon black are comparable to particles generated by the tribological tests. However, it is uncertain whether they are comparable to those formed during simulator studies or in vivo. Furthermore, the performance of the favourable coating has to be tested in a hip joint simulator before its potential for application in prostheses can be assessed.
The tribological performance of a hydrogenated amorphous carbon coating on Ti6Al4V against ceramic balls was checked by simple reciprocating sliding tests and by more complicated tests in a hip joint simulator. 3 of 4 joints failed during hip simulator testing already after approximately 100 × 10³ cycles and possibly due to coating failures caused by insufficient polishing of the metallic acetabular cups prior to coating deposition. Since such failures occurred only occasionally, the problem was not revealed by reciprocating sliding tests which are stressing a much smaller surface area compared to the tests in the hip joint simulator. Another type of failure, pits of 12 µm in diameter distributed randomly at the coating surface, was frequently observed by Scanning Electron Microscopy and analyzed comprehensively by Focused Ion Beam technique in combination with Transmission Electron Microscopy in one case. Although not necessarily affecting wear, such small failures might cause long-term problems in vivo, by providing access of body fluid to the substratecoating interface making it susceptible to corrosion.
In the paper, a model typical for contact situations of automotive brakes is established based on the method of movable cellular automata. The processes taking place at local contacts in an automotive brake system are analysed. Based on microscopic and micro-analytical observations, the following contact situations were simulated: (i) a couple of ferritic steel against pearlitic steel, both covered by an oxide layer mixed with graphite nanoparticles and (ii) the same situation but without oxide layers. The results of calculated mean coefficients of friction of the oxide-on-oxide contact correspond well to expected values for a real braking system, whereas steel-on-steel contact are twice as high. This allows one to make some conclusions; for example, oxide formation will take place more quickly than friction layer elimination, and finally this is responsible for the stabilisation of the coefficient of friction.