In the past few years, it has been discussed with increasing frequency, whether cube slip does occur in gamma' hardened nickel-base superalloys. Occurrence of cube slip has consequences for the modeling of orientation dependence of the CRSS. Until now, there are only few experimental investigations.
In principle, cube slip should be possible in primitive cubic lattices (e.g. L12 ordered gamma' phase) but not in face centered cubic ones (e.g. Ni solid solution). The most favourable specimen orientations are near [111], where the Schmid factors for this type of glide exceed those for octahedral systems.
There are two basic methods to detect cube slip: macroscopic slip trace analysis and Transmission electron microscopy (TEM) investigation of the dislocation structure. Few observations of cube slip by macroscopic slip traces are reported in the literature. But it is still uncertain under which test conditions cube slip occurs and what the dislocation mechanisms are. Cube slip was observed during tensile or compression tests of several first generation superalloys, but it seems not to occur during shear creep deformation (e.g. CMSX-4 at 980°C), and it is also lacking under conventional tensile or compression loading, if the gmma' particles are small. No observations were ever reported of dislocations gliding on {001} planes in matrix channels.
Different wear-resistant coatings produced by physical vapour deposition (PVD) were characterized with the aid of cross-sectional transmission electron microscopy (XTEM). All coating systems were optimized by the producers and exhibited good properties with respect to their special applications. The microstructure, texture and chemical composition of binary and ternary systems produced by the arc process [TiN, CrN, Cr2N (Ti, Cr)N on steel substrates] and magnetron sputtering process [TiN, CrN on steel substrates, (Ti, Al)N on Si-substrate] were investigated. All coatings had a more or less columnar microstructure, which was interrupted by interlayers in some cases. Whereas arc coatings always did show some kind of substrate modification, the latter was not observed after magnetron sputtering. Electron diffraction normally revealed a mono-phase fcc structure, except at sites very near to the interface. Only for the systems CrN and (Ti, Cr)N were different additional phases observed at low nitrogen partial pressures.
The primary crystallite size of titania powder relates to its properties in a number of applications. Transmission electron microscopy was used in this interlaboratory comparison (ILC) to measure primary crystallite size and shape distributions for a commercial aggregated titania powder. Data of four size descriptors and two shape descriptors were evaluated across nine laboratories. Data repeatability and reproducibility was evaluated by analysis of variance. One-third of the laboratory pairs had similar size descriptor data, but 83% of the pairs had similar aspect ratio data. Scale descriptor distributions were generally unimodal and were well-described by lognormal reference models. Shape descriptor distributions were multi-modal but data visualization plots demonstrated that the Weibull distribution was preferred to the normal distribution. For the equivalent circular diameter size descriptor, measurement uncertainties of the lognormal distribution scale and width parameters were 9.5% and 22%, respectively. For the aspect ratio shape descriptor, the measurement uncertainties of the Weibull distribution scale and width parameters were 7.0% and 26%, respectively. Both measurement uncertainty estimates and data visualizations should be used to analyze size and shape distributions of particles on the nanoscale.
The composition and nanostructure of a beneficial tribofilm formed during sliding of a hybrid nanocomposite against steel were characterized comprehensively. A similar nanostructure was produced by high energy ball milling of the three identified tribofilm constituents: silica, hematite and graphite. By supplying powders to a pin-on-disc test it has been shown that neither silica, nor hematite, nor a mixture of both provide the low coefficient of friction (COF) observed for the hybrid composite. Only if graphite was blended with the oxides, the low COF was obtained. Thus, a film of finely dispersed stable inorganic wear products containing 15 vol% graphite provides low friction and wear in the considered case.
An attempt was undertaken to obtain a better understanding of the tribological properties of two wear-resistant coatings on tool steel by structural and microchemical analysis of wear particles using a transmission electron microscope. Coatings were deposited by physical vapor deposition and plasma-assisted chemical vapor deposition techniques and tribological properties were derived from reciprocating sliding tests of the coatings against alumina balls. Three types of wear particles were identified by electron diffraction and energy dispersive X-ray spectroscopy: nanocrystalline rutile (TiO2), nanocrystalline graphite and microcrystalline graphite. Low coefficients of friction, of the order of 0.2, were attributed to the formation of solid lubricant films of sub-stoichiometric TiO2-x Magnéli phases and/or graphite.