Recent progress in the development of A1GaN/GaN heterostructure field effect transistors (HFETs) Shows the great potential towards high temperature / high power electronics. Nevertheless investigations on reliability properties of GaN-based devices are still at the beginning. The frequently used Ti/A1 based ohmic and Pt based Schottky contacts suffer from strong Degradation after aging at elevated temperatures. Therefore new contact systems have to be employed. Concerning the source and drain metallization we used an amorphous WSiN barrier layer as applied for GaAs on top of the Ti/Al-based ohmic contact. This technique significantly reduces the in-diffusion of the Au-containing overlayer, furthermore the barrier layer guaranties smooth contact morphology after RTA and aging, respectively. For the Schottky metallization the Ir/Au system was used. Reliability studies performed on HFET devices containing refractory Ti/A1/Ti/Au/WSiN ohmic and Ir/Au Schottky contacts demonstrate stable conditions during 120h aging at 500°C.
Transmission electron microscopy study of rapid thermally annealed Pd/Ge contacts on In0.53Ga0.47As
(1996)
Phase formation in rapid thermally annealed Pd/Ge contacts on In0.53Ga0.47As has been investigated by means of cross-sectional transmission electron microscopy, convergent-beam electron diffraction, and energy-dispersive x-ray analysis. Solid-phase regrowth is observed to occur similarly as in Pd/Ge contacts on GaAs or InP. The reaction starts at low temperatures with the formation of an amorphous Pd–In–Ga–As layer, which crystallizes at elevated temperatures yielding hexagonal Pd4In0.53Ga0.47As being first described in this work. At temperatures .250 °C, this phase decomposes due to epitaxial solid-phase regrowth of In0.53Ga0.47As and formation of Pd–Ge phases. The stable composition is reached at temperatures .350 °C with excess Ge diffused through top Pd–Ge to the contact interface and growing epitaxially on the semiconductor.