Residual stress depth profiles of a cast nickel-base superalloy were measured by regarding the deflections occurring in plate-shaped specimens while successively removing layers from the machined or treated surface by electropolishing. The results are in good agreement with previous findings showing (i) the influence of grinding parameters on the width of so-called white layers, which correspond to steep gradients of residual tensile stress, and (ii) a broad zone of compressive residual stress in the case of shot peening.
Different wear-resistant coatings produced by physical vapour deposition (PVD) were characterized with the aid of cross-sectional transmission electron microscopy (XTEM). All coating systems were optimized by the producers and exhibited good properties with respect to their special applications. The microstructure, texture and chemical composition of binary and ternary systems produced by the arc process [TiN, CrN, Cr2N (Ti, Cr)N on steel substrates] and magnetron sputtering process [TiN, CrN on steel substrates, (Ti, Al)N on Si-substrate] were investigated. All coatings had a more or less columnar microstructure, which was interrupted by interlayers in some cases. Whereas arc coatings always did show some kind of substrate modification, the latter was not observed after magnetron sputtering. Electron diffraction normally revealed a mono-phase fcc structure, except at sites very near to the interface. Only for the systems CrN and (Ti, Cr)N were different additional phases observed at low nitrogen partial pressures.
In the past few years, it has been discussed with increasing frequency, whether cube slip does occur in gamma' hardened nickel-base superalloys. Occurrence of cube slip has consequences for the modeling of orientation dependence of the CRSS. Until now, there are only few experimental investigations.
In principle, cube slip should be possible in primitive cubic lattices (e.g. L12 ordered gamma' phase) but not in face centered cubic ones (e.g. Ni solid solution). The most favourable specimen orientations are near [111], where the Schmid factors for this type of glide exceed those for octahedral systems.
There are two basic methods to detect cube slip: macroscopic slip trace analysis and Transmission electron microscopy (TEM) investigation of the dislocation structure. Few observations of cube slip by macroscopic slip traces are reported in the literature. But it is still uncertain under which test conditions cube slip occurs and what the dislocation mechanisms are. Cube slip was observed during tensile or compression tests of several first generation superalloys, but it seems not to occur during shear creep deformation (e.g. CMSX-4 at 980°C), and it is also lacking under conventional tensile or compression loading, if the gmma' particles are small. No observations were ever reported of dislocations gliding on {001} planes in matrix channels.