XTEM and TFXRD investigations of ohmic Ti/Al/Ti/Au/WSiN contacts on AlGaN/GaN HFET layer systems
(2002)
The microstructural features of the high-temperature-stable ohmic contact system Ti/Al/Ti/Au/WSiN on AlGaN/GaN were investigated using analytical transmission electron microscopy and thin film x-ray diffraction. For two typical rapid thermal annealing steps at 750 °C (non-ohmic behaviour) and 850 °C (ohmic behaviour) the intermetallic phases at the metal-semiconductor interface are presented. Increased annealing leads to the transformation of an Al2Au-AlAuTi phase mixture to a mixture of Al2Au-Al3Au8 phases and the formation of Ti-Al-nitride layers at the interfaces. In light of these results the electrical contact properties are discussed.
Recent progress in the development of A1GaN/GaN heterostructure field effect transistors (HFETs) Shows the great potential towards high temperature / high power electronics. Nevertheless investigations on reliability properties of GaN-based devices are still at the beginning. The frequently used Ti/A1 based ohmic and Pt based Schottky contacts suffer from strong Degradation after aging at elevated temperatures. Therefore new contact systems have to be employed. Concerning the source and drain metallization we used an amorphous WSiN barrier layer as applied for GaAs on top of the Ti/Al-based ohmic contact. This technique significantly reduces the in-diffusion of the Au-containing overlayer, furthermore the barrier layer guaranties smooth contact morphology after RTA and aging, respectively. For the Schottky metallization the Ir/Au system was used. Reliability studies performed on HFET devices containing refractory Ti/A1/Ti/Au/WSiN ohmic and Ir/Au Schottky contacts demonstrate stable conditions during 120h aging at 500°C.
XTEM and TFXRD investigations of ohmic Ti/Al/Ti/Au/WSiN contacts on AlGaN/GaN HFET layer systems
(2002)
The microstructural features of the high-temperature-stable ohmic contact system Ti/Al/Ti/Au/WSiN on AlGaN/GaN were investigated using analytical transmission electron microscopy and thin film x-ray diffraction.
For two typical rapid thermal annealing steps at 750 ◦C (non-ohmic behaviour) and 850 ◦C (ohmic behaviour) the intermetallic phases at the metal–semiconductor interface are presented. Increased annealing leads to the transformation of an Al2Au-AlAuTi phase mixture to a mixture of Al2Au-Al3Au8 phases and the formation of Ti-Al-nitride layers at the interfaces. In light of these results the electrical contact properties are discussed.