The formation of AlN films prepared by N+2 ion implantation into aluminium was investigated using X-ray and Auger photoelectron spectroscopy ( XPS, AES) as well as cross-sectional transmission electron microscopy (XTEM). After 100-keV N+2 implantation of low doses (1×1017 cm−2), the formation of hexagonal AlN nanocrystals (crystal size <5 nm, Ncrystal=1017 cm−3) was observed. Their orientation is strongly correlated with the aluminium matrix. With the dose increasing to 3×1017 cm−2, crystal growth follows, finally forming a homogeneous AlN-layer. Furthermore, the diffraction patterns show an increasing amount of misorientation with increasing dose. From the crystal size distribution, we conclude that continuous nucleation takes place. Samples implanted with an energy of 3 keV exhibit analogous behaviour. Nitride growth was further investigated using microstructured AlN formed by 3-keV implantation through movable TEM-masks (structure size: 15–150 mm).
In the case of high N+2 doses (D&5×1017 cm−2), AlN is detected by AES in the shielded area at a distance of up to 10 mm from the exposed region. The Diffusion coefficient was calculated to be 10−10 cm2 s−1. The formation of AlN proceeds in two steps.
After a continuous nucleation, diffusion-assisted Crystal growth takes place until a homogeneous AlN layer results.
X-ray photoelectron spectroscopy (XPS) and cross-sectional transmission electron microscopy (XTEM) were used to study the formation of AlN films by N+2 ion implantation of aluminium at energies of 3 keV and 100 keV. In both cases, a two-stage mechanism was found, comprising first the oriented precipitation of small particles of the hexagonal AlN-phase, followed by growth and coalescence finally forming a continuous AlN-layer while increasing the implantation dose from 1×1017 cm-2 to 2×1017 cm-2. The results of both methods are in excellent agreement and furthermore provide complementary information concerning chemical composition and binding energies as well as microstructural details.