This review article comprises of three parts. Firstly, reports of brake manufacturers on the beneficial impact of solid lubricants for pad formulations are surveyed. Secondly, since tribofilms were identified to play a crucial role in friction stabilization and wear reduction, the knowledge about tribofilm structures formed during automotive braking was reviewed comprehensively. Finally, a model for simulating the sliding behavior of tribofilms is suggested and a review on modelling efforts with different model structures related to real tribofilms will be presented. Although the variety of friction composites involved in commercial brake systems is very broad, striking similarities were observed in respect to tribofilm nanostructures. Thus a generalization of the tribofilm nanostructure is suggested and prerequisites for smooth sliding performance and minimal wear rates have been identified. A minimum of 13 vol.% of soft inclusions embedded in an iron oxide based tribofilm is crucial for obtaining the desired properties. As long as the solid lubricants or their reaction products are softer than magnetite, the main constituent of the tribofilm, the model predicts smooth sliding and a minimum of wear.
Copper is one of the most important components in brake pads and its amount can reach up to 14%. In spite of a number of positive features copper usage in brake pad formulations has recently become the subject of considerable discussions, primarily due to concerns about potential risks related to environmental impacts of copper particles. So, for developing new pad formulations with possible replacements of copper content, it is very important to understand the functionality of copper additions to brake friction materials. In the paper theoretical investigation of the role of copper as a pad ingredient was carried out on the basis of modelling by the method of movable cellular automata (MCA). Our previous studies show that copper as a constituent of the tribofilm formed during braking provides smooth sliding by forming a granular layer of mechanically mixed materials from the friction layers. In the present study the concentration of copper particles in a Fe3O4-matrix was varied systematically in the range 5.5-28 vol. % and compared to mixtures with the same amount of graphite nanoparticles. The sliding simulations were performed while assuming material properties at 500°C in order to assess the beneficial role of copper during severe braking conditions corresponding to fading cycles during dynamometer testing.
Reference nanomaterials
(2016)
This chapter reviews relevant aspects of the still less explored field of RNMs. In the first part, definition of RMs according to different metrological levels was presented as well as the general strategy on their development. In the second part, the importance of RNMs in material science and nanotoxicology is explained and considerations on the use of silica nano-objects as potential future reference material was discussed. Overall, several points should be highlighted from this chapter: Definition of a reference material depends on the level of standardization. Certified reference material represents the highest level of traceability. Different types of reference materials, standard materials and certified reference materials are available, as shown in Table 3.1. The preparation of nano-objects with well-defined mechanical properties is still an unsolved issue and thus needs further R&D activities. Nevertheless, amorphous silica seems to be a promising candidate for reaching this objective. Traceable properties of nanomaterials are still limited to few cases such as primary particle size and thickness measurements of very thin films. In general, developed RMs are monoparametric thus, only one characteristic of the nano-objects is reported. In nanotoxicology, the challenge is in the development of suitable RNM that bears similarities to the measurements made on the sample analysed.
Besides carbon, metal sulphides are used in every standard brake pad formulation as friction stabilisers. In order to investigate their impact, various powder mixtures were tribologically stressed in a pin-on-disc device in order to produce and test artificial third bodies. containing the three main components of a real friction film, namely magnetite, graphite and a metal sulphide of interest. Since the sliding behaviour is influenced by the relative humidity the powder mixtures are tested at low, medium and high moisture levels. The tests revealed that the presence of graphite dominates the friction behaviour as well as the humidity sensitivity.
The powders were prepared by either manual mixing or high energy ball-milling. Interestingly, all ball-milled blends provided coefficients of friction within the desired range for braking, which was attributed to the effect of zirconia particles from wear debris of the milling balls. The zirconia particles prevent the formation of solid lubricant films on the surfaces and support a homogeneous mixture of all constituents of the powder. Optimum brake performance is gained by an optimum combination of solid lubricants and abrasives.
The sliding behaviors of two simplified tribofilms with amorphous structure consisting either of SiO₂ molecules or C atoms were simulated by molecular dynamics modeling. The objective was to identify mechanisms explaining the experimentally observed lubricating properties of the two amorphous films. The impacts of layer thickness, normal pressure, temperature and different substrate materials were studied systematically, while the sliding velocity was kept constant at 30 m/s. While the layer thickness was not critical, all the other parameters showed special effects under certain conditions. Normal pressure impeded void formation and could even eliminate voids if applied at high temperature. Stick-slip sliding was changed to smooth sliding at high temperature due to void healing. Considering the carbon film, high friction forces and shearing of the entire film was observed with diamond substrates, whereas interface sliding at low friction forces and an amorphous layer of iron mixed with carbon was observed if the supporting substrates consisted of α-Fe. Both films show a decrease of friction forces and smooth sliding behavior at elevated temperature, corresponding well to the tribological behavior of and advanced nanocomposite sliding against a steel disc under severe stressing conditions when high flash temperatures can be expected.