TEM study on the effect of machining on the microstructure of a soft magnetic Ni76Fe17Cu5CrMo2 alloy
(1991)
Low-cycle fatigue experiments under combined axial-torsional loading have been carried out on alloy 800 H tubular specimens at room temperature. In comparison with proportional loading, an extra cyclic hardening effect produced by nonproportional loading was observed. The microstructure study highlights the fact that the dislocation arrangement under proportional loading is significantly different from that under nonproportional loading. Mechanical twinning was found in specimens cycled under axial loading and nonproportional loading. It is suggested that mechanical twinning depends not only on shear stress but also on normal stress on the plane of maximum shearing. The extra hardening can be interpreted in terms of the deformation microstructure. Fatigue cracking was initiated generally at the specimen surfaces along the plane of maximum shearing, but under nonproportional loading cracks were found also in the bulk of the specimens. Transcrystalline crack propagation was observed in the specimens after proportional and nonproportional LCF tests.
The role of grain size and ferrite substructure in respect to mechanical properties of an HSLA steel
(1986)
Several heat treatments were applied to an HSLA steel on type StE460 (German standard) to produce four ferrite substructures of different strength and at least two different grain sizes respectively. Whereas the ferrite substructure has a strong influence on yield strength the effect of grain size was negligible though probably to some extent masked by different pearlite volume fractions. The different strength levels could be explained by regarding the arrangement of dislocations and vanadium carbonitride particles and their mutual interaction. Increasing both grain size and pearlite volume fraction leads to a remarkable shift of transition temperature T sub 27J which was further enhanced by increasing ferrite strength. 16 ref.--AA