Three principally different mechanisms contribute to the wear-down process of mineral aggregates in sedimentary environments: (1) mechanical abrasion by forces of wind and water and by floating or saltating neighbouring grains, (2) chemical attack and dissolution by fluids, and (3) physical bioerosion and chemical biocorrosion. It is however, difficult to attribute the specific surface changes to specific environments and processes. Quartz sand grains from subaerial and subaquatic environments were analysed by atomic force microscopy (AFM) for traces of natural and experimental aeolian, aquatic and biological wear-down processes. Quantitative topographical parameters of surface alterations were extracted from topography data by non-linear methods derived from digital image analysis. These parameters were examined by multivariate statistic, yielding three well-distinguishable groups. Morphological surface alterations dominated by subaerial, subaquatic and by biological impact could be differentiated. The method may also be used for the detection of aeolian, subaquatic, and biological modification of sedimentary grains and rock surfaces in extraterrestrial environments, and for assessment of environmental damage on monuments and buildings.
Faserverbundbauteile werden durch Tränkung von Fasergewebe mit flüssigem Harz, in der Regel Epoxidharzen, und anschließender Härtung des Harzes gefertigt. Dabei kann man das Gewebe im Vorfeld mit reaktivem Harz tränken und als so genanntes Prepreg verarbeiten oder man injiziert das frisch mit dem Härter gemischte Harz in ein Werkzeug, in dem das Gewebe bereits liegt - z. B. beim RTM-Prozess. Ausgehend von der Aufgabenstellung, eine Prepregherstellung mit hohem Qualitätsstandard zu realisieren und Möglichkeiten der Fertigungskontrolle für den Prepreg-Verarbeiter aufzuzeigen, wurde an einem für die Prepregherstellung vorgesehenen Harzsystem eine weitgehende Charakterisierung des Aushärtungsverlaufs vorgenommen. Wegen der Schwierigkeit, schnell konstante Aushärtungstemperaturen zu erreichen, wurden bei allen Methoden mit einer Heizrate von 1 K/min von RT bis 200 °C aufgeheizt.
EVA is a widely used material for the encapsulation of photovoltaic modules. It melts at elevated temperatures, and seals the module before it is crosslinked at temperatures above 130 °C by a peroxide-initiated crosslinking reaction. EVA has good optical properties necessary for application in solar modules. For process optimization and quality management, a method for the quick and reliable characterization of EVA crosslinking behaviour is of great value. Here, the practicability of ultrasound for online crosslinking monitoring is demonstrated. A sound velocity increase of about 8 m/s during the crosslinking reaction is found. The ultrasound results are compared with rheometer measurements performed with a curemeter typically used for the investigation of rubber crosslinking.
Non-destructive evaluation (NDE) of composites: using ultrasound to monitor the curing of composites
(2013)
Typical composite materials for lightweight construction consist of a fibre (glass or carbon) reinforced thermosetting matrix. The impregnation of the fabric is made with liquid resin – usually epoxy resin or unsaturated polyester resin are used. The main processing methods are resin transfer moulding (RTM) and prepreg technology often used in combination with autoclave curing. After shaping, the resin must be cured. The final properties of the produced parts depend on the curing degree and the final glass transition temperature. Analytical methods and the use of ultrasound for online cure monitoring in the manufacturing process are introduced. Examples for the application of ultrasonic cure monitoring for the production of composite parts for traffic systems are also covered.
The cure behaviour of a specific ethylene vinyl acetate material as used for encapsulation of photovoltaic modules was analysed by rheometer, differential scanning calorimetry and Fourier transform infrared spectroscopy to test for a suitable replacement for the laborious determination of gel content. The results show that all applied methods are capable of describing the effects of the cross-linking process. Some provide results very similar to those yielded by analysis of the insoluble content, but the question remains as to whether indirect methods should be preferred over the direct measurement of physical properties, e.g. as performed by the curemeter. A material stored for one year was also tested to demonstrate the effect of extended storage on cure behaviour and how this is detected by different methods. This complements the other methods, which were clearly able to detect the different cure behaviour of the aged EVA, whereas determination of the gel content could not.