The interaction of nanosecond laser pulses in the ultraviolet wavelength range and femtosecond laser pulses in the near-infrared region with the semiconductor SiC and the composite compound SiCTiCTiB2 was investigated. Surface analytical techniques, such as XPS, depth profile (DP), and micro-Raman spectroscopy (?-RS) were used to identify the chemical changes between untreated and laser-treated areas. Single-pulse irradiation led to material modifications in the condensed state in most instances. Multi-pulse results differed depending on the pulse duration. Crystal structure changes were observed as a consequence of laser-induced melting and resolidification. In air contact all components underwent oxidation reactions according to thermodynamic expectations. Exceptions were observed under exclusion of oxygen, SiC was reduced to elemental Si.
Tribological characterisation of siliconcarbonitride ceramics derived from preceramic polymers
(2006)
Amorphous SiCN ceramics were prepared in a laboratory scale as disk shaped specimens with 10 mm diameter and 0.3 mm thickness. The friction and wear behaviour was characterised in gross slip fretting tests under unlubricated conditions at room temperature against steel (100Cr6) and ceramic (Al2O3). Tests with a ball-on-disk contact were performed in laboratory air with different content of water vapour. The results show clearly that the relative humidity has a significant effect on friction and wear behaviour. All tests in dry air lead to higher friction and higher wear rate than in normal air. Improved friction and wear behaviour was observed with increasing pyrolysis temperature up to 1100 °C of the SiCN specimens. This is attributed to increasingly better mechanical properties and higher stiffness of the amorphous network due to the evaporation of gaseous organic species and the formation of free graphite like carbon.
It has been successfully demonstrated that ceramic materials can be joined in the green
state without a second phase by using low pressure injection molded parts. The investigation of the
joining interface revealed that a high quality interface can be achieved by carefully adjusting the
different manufacturing steps. The use of monomodal particle size distribution in the used powder
CT3000SG is inferior to a broader particle size distribution obtained by replacing 33% of the finer
alumina powder by coarser CT1200SG. In this way the dewaxing process is significantly improved
when the wall thickness of the part exceeds 3 mm. The investigation of the mechanical properties of
the joined and sintered parts revealed, that the bending strength of the joined specimens achieved
about 80 % of the unjoined, monolithic specimens.